Epoxidized natural rubber coated modified white carbon black and preparation method thereof and rubber material
A technology of natural rubber and rubber materials, applied in the field of surface modification of silica, can solve the problems of low tensile stress, low reactivity, large permanent deformation, etc., and achieves improved tensile strength, simple preparation method, and permanent deformation rate reduced effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] The invention provides a preparation method of epoxidized natural rubber coated modified silica, which comprises the following steps:
[0023] (1) Provide a dispersion of white carbon black, and mix the dispersion with epoxidized natural rubber to obtain a mixture;
[0024] (2) Perform shearing treatment on the mixed material obtained in the step (1) to obtain a mixed slurry;
[0025] (3) Perform solid-liquid separation of the mixed slurry in step (2) to obtain a silica precursor coated with epoxidized natural rubber;
[0026] (4) The white carbon black precursor obtained in step (3) is heat-treated to obtain an epoxidized natural rubber coated modified white carbon black.
[0027] The present invention first provides a dispersion of white carbon black. The present invention does not have special restrictions on the operation of preparing the dispersion liquid, and the technical solution for preparing dispersion liquid well known to those skilled in the art may be adopted. In t...
Example Embodiment
[0041] Example 1:
[0042] Disperse 100g of white carbon black powder in 400g of water. After ultrasonically crushing and dispersing uniformly, add 50g of epoxidized natural rubber emulsion with a dry rubber content of 20wt% and an epoxidation degree of 40%. Mix in a machine and process for 0.5h at 10000rpm; the obtained mixed slurry is separated by sedimentation in a centrifuge with a speed of 8000rpm, dried at 70℃ for 12h, crushed by a crusher, and treated at 180℃ under vacuum for 2h, Obtain epoxidized natural rubber coated modified silica; perform moisture absorption treatment at an air humidity of 80%, so that the moisture content of the silica reaches 6%; mix with natural rubber and vulcanize according to the formula listed in Table 1 rubber.
[0043] The epoxidized natural rubber coated modified silica obtained in this example was subjected to X-ray photoelectron spectroscopy characterization test, and the result is shown in FIG. 2. It can be seen from Figure 2 that after t...
Example Embodiment
[0044] Example 2:
[0045] Directly take 500g of white carbon black slurry with a dry matter content of 20wt%, and after high-speed shearing, add 5g of N-(β-aminoethyl-γ-aminopropyl)methyldimethoxysilane under mechanical stirring to react After 1h, add 60g of epoxidized natural rubber emulsion with dry rubber content of 25wt% and epoxidation degree of 25%, and treat it for 2 times under 200Mpa working pressure in a high-pressure homogeneous dispersing machine; spray the obtained mixed slurry Drying, the inlet temperature of the spray drying device is 200°C, and the outlet temperature is 100°C; the obtained silica precursor is treated at 150°C for 5 hours under the protection of nitrogen to obtain epoxidized natural rubber coated modified silica; Hygroscopic treatment is carried out at an air humidity of 80% to make the water content of the white carbon black reach 6%; according to the formula listed in Table 1, it is mixed with natural rubber and vulcanized to obtain rubber.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap