Coating for cement fence and preparation method thereof
A fence and coating technology, applied in the coating and other directions, can solve the problems of poor anti-ultraviolet ability and easy aging, and achieve the effects of improved anti-aging performance and anti-ultraviolet performance, low cost, and strong water and high temperature resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] See attached figure 1 , a preparation method of cement fence coating, comprising the following steps:
[0030] 1) Take acrylic emulsion, film-forming aid and thickening agent, stir and mix to form base material, for subsequent use;
[0031] 2) After mixing, grinding and sieving the pigments and fillers, the pigments and fillers are formed for use;
[0032]3) take deionized water, dispersant and wetting agent, stir and mix to form an aqueous solution, and add the pigments and fillers obtained in step 2) into the aqueous solution to form a color paste;
[0033] 4) Mix the base material obtained in step 1) with the color paste obtained in step 3), add anti-aging auxiliary agent and leveling agent therein, and filter to obtain the product.
[0034] Further, in the aqueous solution of step 3), 0.1-0.5 parts by weight of defoaming agent and 0.1-0.5 part by weight of anti-mildew bactericide are also added.
Example Embodiment
[0035] Example 1
[0036] 1) get 35 parts by weight of acrylic emulsion, 5 parts by weight of film-forming aids and 2 parts by weight of thickener, stir and mix, form base material, standby; Wherein, thickener is alkaline swelling type thickener, and acrylic emulsion consists of Acrylic acid 40wt%, butyl acrylate 45wt%, deionized water 6wt%, emulsifier 5wt%, acrylamide 2wt% and silicone monomer 2wt% are polymerized.
[0037] 2) Take pigments and fillers, wherein the weight ratio of pigments and fillers is 1:2, after mixing, grinding, and sieving, the particles below 50 μm form pigments and fillers, for subsequent use; wherein, the pigment is an inorganic iron oxide pigment, and the filler is kaolin clay .
[0038] 3) Take 20 parts by weight of deionized water, 2 parts by weight of dispersant and wetting agent, 0.5 part by weight of defoaming agent, stir and mix to form an aqueous solution, and add 20 parts by weight of pigments and fillers obtained in step 2) into the aqueous...
Example Embodiment
[0041] Embodiment 2
[0042] 1) Get 50 parts by weight of acrylic emulsion, 3 parts by weight of film-forming assistant and 1 part by weight of thickener, stir and mix, form base material, standby; Water 10wt%, emulsifier 3.5wt%, acrylamide 3wt%, organosilicon monomer 3wt% and ammonium persulfate 0.5wt% are polymerized.
[0043] 2) Take pigments and fillers, mix, grind and sieve to form pigments and fillers for use.
[0044] 3) Take 10 parts by weight of deionized water, 1 part by weight of dispersant and wetting agent, 0.3 part by weight of defoamer, and 0.1 part by weight of antiseptic and bactericide, stir and mix to form an aqueous solution, and add 30 parts by weight of pigments and fillers obtained in step 2). added to the aqueous solution to form a color paste.
[0045] 4) mixing the base material obtained in step 1) with the color paste obtained in step 3), and adding 3 parts by weight of anti-aging auxiliary agent and 2 parts by weight of leveling agent in it, the l...
PUM
Property | Measurement | Unit |
---|---|---|
Gloss | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap