Nanometer organic carbon fertilizer and preparation method thereof

A nano-organic and carbon fertilizer technology, applied in fertilization devices, fertilizer mixtures, applications, etc., can solve problems such as unsuitable for popularization and application, cumbersome preparation process, high difficulty, etc., achieve good repair and improvement, save labor, and meet carbon requirements. balanced effect

Inactive Publication Date: 2016-03-02
SHENZHEN BATIAN ECOTYPIC ENG
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The Chinese invention patent application with the publication number CN103755481A discloses a nano-carbon organic fertilizer, which is mainly obtained through the fermentation of biological strains. The nano-carbon is directly added to the system as a raw material, not a reaction product. The preparation of this method The process is very complicated, difficult, and takes a long time, so it is not suitable for industrial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A nanometer organic carbon fertilizer, which comprises the following components by mass percentage:

[0033] Equal quality urea, ammonium nitrate, ammonium nitrate phosphorus, and ammonium sulfate are used as nitrogen raw materials for a total of 30kg,

[0034] Equal quality monoammonium phosphate and diammonium phosphate are used as phosphorus element raw materials, a total of 30kg,

[0035] Equal quality potassium sulfate, potassium magnesium sulfate, and potassium chloride are used as potassium element raw materials 20kg,

[0036] Equal quality nano silicon dioxide, nano diatomite, nano bentonite, nano calcium carbonate as nano synergist 14kg,

[0037] Nano organic carbon 5kg,

[0038] The rest is stone powder 1kg.

[0039] Preparation:

[0040] Using molasses as raw material, adding acid to carry out digestion reaction, the digestion reaction is carried out in a closed reaction kettle irradiated by microwaves, after digestion, a nano-organic carbon solution is o...

Embodiment 2

[0042] A nanometer organic carbon fertilizer, which comprises the following components by mass percentage:

[0043] Equal quality urea, ammonium nitrate, and ammonium nitrate phosphorus are used as nitrogen element raw materials, a total of 20kg,

[0044] Monoammonium phosphate is 20kg in total as the phosphorus element raw material,

[0045] Potassium sulfate of equal quality, potassium magnesium sulfate is used as potassium element raw material 15kg,

[0046] Equal quality nano silicon dioxide, nano diatomite, nano bentonite as nano synergist 20kg,

[0047] Nano organic carbon 3kg,

[0048] The rest is stone powder 2kg.

[0049] Preparation:

[0050]Using molasses as raw material, adding acid to carry out digestion reaction, the digestion reaction is carried out in a closed reaction kettle irradiated by microwaves, after digestion, a nano-organic carbon solution is obtained, which is filtered with a filter paper with a pore size of 0.8um, and finally nitrogen and phospho...

Embodiment 3

[0053] A kind of nanometer organic carbon fertilizer, raw material comprises following components:

[0054] Equal quality urea, ammonium nitrate, and ammonium nitrate phosphorus are used as nitrogen element raw materials for a total of 10kg,

[0055] Monoammonium phosphate is 30kg in total as the phosphorus element raw material,

[0056] Potassium sulfate of equal quality, potassium magnesium sulfate is used as potassium element raw material 25kg,

[0057] Equal quality nano silicon dioxide, nano diatomite, nano bentonite as nano synergist 10kg,

[0058] Nano organic carbon 3kg,

[0059] The rest is stone powder 2kg.

[0060] Preparation:

[0061] Using molasses as raw material, acid is added to carry out digestion reaction. The digestion reaction is carried out in a closed reaction kettle irradiated by microwaves. The masses of molasses and acid solution are 10kg and 1kg respectively, and the mass concentration of acid solution is 0.2%.

[0062] After digestion, a nano o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nanometer organic carbon fertilizer. The nanometer organic carbon fertilizer comprises, by mass, 10-30% of a nitrogen raw material, 8-30% of a phosphor raw material, 5-25% of a potassium raw material, 0.1-15% of a nanometer synergist, 1-15% of nanometer organic carbon and the balance accessory material. The accessory material is stone flour. The preparation method of the nanometer organic carbon fertilizer utilizes microwave digestion advantages to realize high efficiency treatment on organic waste water under the case of less acid use amount and production of the nanometer organic carbon as a fertilizer carbon source. The nanometer organic carbon can be easily absorbed by crops, and through combination with nitrogen, phosphor and potassium and the nanometer synergist, nitrogen, phosphor and potassium absorption and utilization are promoted and carbon, nitrogen, phosphor and potassium demands of plants are satisfied.

Description

technical field [0001] The invention relates to the technical field of fertilizers, in particular to a nano-organic carbon fertilizer and a preparation method thereof. Background technique [0002] The theory of plant nutrition points out that carbon is a large element in plant nutrition, and the average content of carbon in plants is about 45%, which is several times higher than the sum of large, medium and trace elements. The application of chemical fertilizers needs to consider the balance between various nutrient elements, which is also the goal of soil testing and formula fertilization. However, in the case of a substantial increase in the amount of nitrogen, phosphorus and potassium fertilization, the supplement of carbon is not considered, which makes the "carbon short board" more acute, and the actual effect of balanced fertilization is greatly reduced. If "carbon starvation" can be eliminated by adjusting and optimizing the balance of plant nutrition through fertil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00
Inventor 裴福云
Owner SHENZHEN BATIAN ECOTYPIC ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com