Preparation method of environment-friendly green composite building adhesive

An environmentally friendly, adhesive technology, applied in the preparation of animal glue or gelatin, adhesives, protein adhesives, etc., can solve the problems of bone glue not being resistant to water, losing bonding strength, harming the body, etc., and achieve corrosion resistance Strong, strong adhesive force, good waterproof effect

Inactive Publication Date: 2016-03-02
仇颖超
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main technical problem to be solved by the present invention is to solve the problem that the currently commonly used construction adhesives contain aldehyde organic solvents, which are harmful to the body and pollute the environment, and the bone glue is not water-resistant, loses bonding strength due to water swelling, and is not corrosion-resistant. The problem is to provide a method of using bone glue to prepare green composite building adhesives. The invention pretreats sheep bones to make them fully expanded, and then separates the bone glue by soaking in water and adjusting the pH value. The bone glue and polyethylene Diol and sodium isocyanate are mixed and reacted to finally obtain a composite construction adhesive. The present invention modifies the biological bone glue, and the prepared adhesive is not only environmentally friendly, but will not cause poisonous harm to production and users, and its adhesive Strong joint force, good water resistance, strong corrosion resistance, improve the life of the adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0019] First, take 1 kg of sheep bone and put it into a high-temperature and high-pressure furnace, set the temperature at 200°C and the pressure at 2 MPa, keep it for 50 minutes, then cool it to room temperature, take it out, remove the impurities on the surface of the sheep bone, and put it into the container , add ethanol solution with a mass fraction of 35% to soak the sheep bones, let stand for 30min, then take out the sheep bones, put them in an oven for drying; put the dried sheep bones into a pulverizer for crushing, Sieve 80 meshes to obtain sheep bone powder, then put the gained sheep bone powder into a container, add 15% sodium carbonate solution to submerge the sheep bone powder for 3 cm in mass fraction, and then use 5% barium hydroxide Adjust the pH of the solution to 9.5, then heat the container to 40°C, and keep the temperature for 2 hours to completely expand the sheep bone powder; after the complete heat preservation is completed, filter while it is hot, colle...

example 2

[0022]First, take 2kg of sheep bone and put it into a high-temperature and high-pressure furnace, set the temperature at 250°C, set the pressure at 3MPa, keep it for 60 minutes, then cool it to room temperature, take it out, remove the impurities on the surface of the sheep bone, and put it into the container , add ethanol solution with a mass fraction of 35% to soak the sheep bone, let it stand for 40min, then take out the sheep bone and put it in an oven for drying; put the dried sheep bone into a pulverizer for pulverization, Sieve 90 meshes to obtain sheep bone powder, then put the gained sheep bone powder into a container, add 15% sodium carbonate solution to submerge sheep bone powder 4cm in mass fraction, then use 5% barium hydroxide Adjust the pH of the solution to 9.8, then heat the container to 43°C, and keep the temperature for 3 hours to completely expand the sheep bone powder; after the complete heat preservation is completed, filter while it is hot, collect the ex...

example 3

[0025] First, take 3kg of sheep bone and put it into a high-temperature and high-pressure furnace, set the temperature at 300°C, and set the pressure at 4MPa, keep it for 70 minutes, then cool it to room temperature, take it out, remove the impurities on the surface of the sheep bone, and put it into the container , add ethanol solution with a mass fraction of 35% to soak the sheep bones, let stand for 50min, then take out the sheep bones, put them in an oven for drying; put the dried sheep bones into a pulverizer for crushing, Sieve 100 meshes to obtain sheep bone powder, then put the gained sheep bone powder into a container, add 15% sodium carbonate solution to submerge the sheep bone powder for 5 cm, then use 5% barium hydroxide The pH of the solution is adjusted to 10.0, then the container is heated to 45°C, and the temperature is kept for 4 hours to completely expand the sheep bone powder; after the complete heat preservation is completed, filter while it is hot, collect ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of environment-friendly green composite building adhesive and belongs to the field of adhesives. Sheep bones are pretreated to be completely puffed, water is added for immersion, the pH value is adjusted, and then bone glue is formed after separation; the bone glue, polyethylene glycol and sodium cyanate are mixed and react, and finally the composite building adhesive is obtained. The biological bone glue is modified, the prepared adhesive is environmentally friendly, free of harm to production and users, high in adhesive force, good in waterproofness and high in corrosion resistance, and the service life of the adhesive is prolonged.

Description

technical field [0001] The invention discloses a preparation method of an environment-friendly green composite building adhesive, which belongs to the field of adhesives. Background technique [0002] Construction adhesives are used in every process and even every material in the construction industry. It is roughly divided into the following aspects: application in various building constructions; application in indoor and outdoor decoration and decoration; sealing of various buildings , including doors and windows, large slab walls, expansion joints, joints and special buildings, etc.; applications in building maintenance, renovation, reinforcement and reinforcement; reinforcement and maintenance of various transportation facilities and water conservancy projects; widely used in composite building materials The production of light weight, high strength, and multiple functions is the development direction of composite building materials; mixed with water to make various high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J189/00C09J175/08C09J11/04
CPCC09J11/04C09J189/00C09J2301/408C08L75/08C08K2003/2241
Inventor 仇颖超宋国王志慧
Owner 仇颖超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap