Express highway toll collection recognition device based on electrochromic device and manufacturing method thereof

A technology of electrochromic devices and identification devices, which is applied in the field of transportation and can solve the problems of reduced identification accuracy, low efficiency, and missed fees

Inactive Publication Date: 2016-03-02
林业城
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the surface of the existing toll recognition device is greatly affected by sunlight, etc., which easily reduces the recognition accuracy, resulting in low efficiency and leakage of fees.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Express highway toll collection recognition device based on electrochromic device and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Assemble the toll identification device 10 , the electrochromic device 20 and the control device 30 .

[0068] Making the electrochromic device 20 includes:

[0069] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0070] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 320nm;

[0071] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 220nm; W film is used as WO 3 a growth source for the nanowires;

[0072] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtaine...

Embodiment 2

[0087] Assemble the toll identification device 10 , the electrochromic device 20 and the control device 30 .

[0088] Making the electrochromic device 20 includes:

[0089] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0090] a. Magnetron sputtering fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 360nm;

[0091] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 200nm; W film is used as WO3 a growth source for the nanowires;

[0092] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained pr...

Embodiment 3

[0107] Assemble the toll identification device 10 , the electrochromic device 20 and the control device 30 .

[0108] Making the electrochromic device 20 includes:

[0109] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0110] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film on the surface of tempered glass 1 with a specific size, with a thickness of about 340nm;

[0111] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 210nm; W film is used as WO 3 a growth source for the nanowires;

[0112] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an express highway toll collection recognition device based on an electrochromic device and a manufacturing method thereof, and the structure of the electrochromic device and manufacturing process are improved, so that the device has a characteristic of self-energizing. Thus, a novel express highway toll collection recognition device in short response time, prolonged life and good antifreezing property is manufactured. The method is simple and easy to operate, and the method is easy for industrialization.

Description

technical field [0001] The invention belongs to the field of transportation, and more specifically relates to a highway toll recognition device based on an electrochromic device and a manufacturing method thereof. Background technique [0002] The role of license plate recognition in expressway toll collection is to reduce travel time, improve the technical content of the toll management system and assist personnel management to prevent card loss and toll leakage. [0003] However, the surface of the existing toll recognition device is greatly affected by sunlight, etc., which easily reduces the recognition accuracy, thereby causing low efficiency and leakage of fees. Contents of the invention [0004] Aiming at the problems existing in the background technology, the present invention provides a highway toll recognition device based on an electrochromic device and a manufacturing method thereof, which improves the structure and manufacturing process of the self-powered ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02F1/15G02F1/153G02F1/163
CPCG02F1/15G02F1/153G02F1/163
Inventor 刘桂花
Owner 林业城
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products