Alga-calcium-mineral air purification medium and preparation method and application thereof

An air purification and mineral technology, applied in the field of air purification, can solve the problems of secondary pollution of desorption, harsh process, low order of magnitude of adsorption-desorption channel, etc., and achieves low desorption, simple production process, and obvious difference in adsorption and decomposition potential energy. Effect

Active Publication Date: 2016-03-23
湖北格林森绿色环保材料股份有限公司
View PDF16 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The carriers of the existing photocatalytic air purification media are mostly activated carbon and natural adsorption clay conventional adsorption materials, and the order of magnitude o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alga-calcium-mineral air purification medium and preparation method and application thereof
  • Alga-calcium-mineral air purification medium and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The raw material formulation of algal calcium mineral air purification medium consists of (substance measurement units are parts by weight):

[0034] (1) Algae mineral powder, 45 parts of raw soil refined by diatoms, particle size 800 mesh;

[0035] (2) Calcium powder, adopting 5 parts of calcium sulfate hemihydrate, fineness is 250 orders;

[0036] (3) Catalytic powder, adopts 1.0 parts of perovskite powder;

[0037] (4) mineral modifier, adopt each 1.4 parts of tourmaline powder and sepiolite powder;

[0038] (5) 44.6 parts of liquid medium, obtained by compounding clear water: sodium lauryl sulfate: sodium bicarbonate=97:1.5:1.5;

[0039] (6) 1.6 parts of photocatalyst.

[0040] Such as figure 1 Shown, adopt above-mentioned raw material to produce and prepare the technology of algae calcium mineral air purification medium as follows:

[0041] (1) Pre-mixing of raw materials: Accurately measure various algae minerals, calcium powder, catalytic powder, and mineral...

Embodiment 2

[0049] The raw material formulation of algal calcium mineral air purification medium consists of (substance measurement units are parts by weight):

[0050] (1) Algae mineral powder adopts 42 parts of diatomaceous earth, and the particle size is 180 mesh;

[0051] (2) Calcium powder, adopting 4.2 parts of calcium sulfate hemihydrate, fineness is 120 orders;

[0052] (3) Catalytic powder, adopts 0.8 part of perovskite powder;

[0053] (4) Mineral modifier, adopt 1 part of tourmaline powder+1.4 parts of zeolite powder;

[0054] (5) 48 parts of liquid medium, all of which are clear water;

[0055] (6) 1.5 parts of photocatalyst, using doped nano-TiO 2 powder, the composition is TiO 2 / SiO 2 .

[0056] Such as figure 1 Shown, adopt above-mentioned raw material to produce and prepare the technology of algae calcium mineral air purification medium as follows:

[0057] (1) Pre-mixing of raw materials: Accurately measure various algae minerals, calcium powder, catalytic powder...

Embodiment 3

[0065] The raw material formulation of algal calcium mineral air purification medium consists of (substance measurement units are parts by weight):

[0066] (1) Algae mineral powder, using 48.44 parts of seaweed, particle size 400 mesh;

[0067] (2) Calcium powder, using 9.8 parts of calcium silicate, the fineness is 300 mesh;

[0068] (3) Catalyst powder, using LaNiO 3 1.2 parts of nano powder;

[0069] (4) Mineral modifier, adopt attapulgite, zeolite powder, vermiculite powder each 1 part;

[0070] (5) 36 parts of liquid medium, obtained by compounding clear water: sodium lauryl sulfate: sodium bicarbonate=98:1:1;

[0071] (6) 1.8 parts of photocatalyst, using doped nano-TiO 2 powder, the composition is TiO 2 / Fe 3+ .

[0072] Such as figure 1 Shown, adopt above-mentioned raw material to produce and prepare the technology of algae calcium mineral air purification medium as follows:

[0073] (1) Pre-mixing of raw materials: Accurately measure various algae minerals, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention provides an alga-calcium-mineral air purification medium. The air purification medium is mainly prepared from, by weight, 42-48.44 parts of alga mineral powder, 4.2-9.8 parts of calcium powder, 0.8-1.2 parts of catalysis powder, 2.4-3.0 parts of mineral modifiers, 36-48 parts of liquid-phase media and 1.5-1.8 parts of photocatalyst. The raw materials are subjected to pre-stirring, hole forming and granulating, polishing and oxidation, primary drying, photocatalyst surface treatment and secondary drying to form particle medium carriers. The air purification medium has the advantages that the absorption-catalysis-purification performance is outstanding, the preparation process is mild and free of rigorous requirements, product application is flexible, and an air purification device with de-odoring, deodorization, taste removal or bacteria resistance and mildew-proof functions by applying appropriate matched application components.

Description

technical field [0001] The invention relates to the technical field of air purification, in particular to an algal calcium mineral air purification medium and a preparation method and application thereof. Background technique [0002] On August 13, 2015, a research report published by American scientist Robert Rhodes showed that air pollution in China would cause an average of 4,000 deaths per day, accounting for 17% of the total death toll in China. In 2014, the China Building Decoration Association released the "Report on Home Environment and Interior Decoration", which showed that the average rate of formaldehyde exceeding the standard was 70% to 80%, and the highest detection value exceeded the national standard by 4.2 times. There are more than 300 pollutants that can be detected indoors, including more than 20 carcinogens. Due to the slow release of various indoor building decoration materials and household continuous potential harmful pollution sources, the indoor air...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/14B01J20/30B01D53/86
CPCB01D53/86B01D2253/106B01D2257/91B01J20/14
Inventor 韦华童军温发华
Owner 湖北格林森绿色环保材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap