Catalyst for preparation of furfuryl alcohol by furfural liquid phase hydrogenation and preparation method
A catalyst and furfural liquid technology, which is applied in the field of catalysts for furfural liquid-phase hydrogenation to furfuryl alcohol, can solve the problems of short life, non-recyclable catalyst, easy deactivation, etc., and achieve less addition, low price, high activity and selectivity sexual effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0038] Example 1:
[0039] Weigh copper nitrate (Cu(NO 3 ) 2 ·3H 2 O) 132.9g, chromic anhydride (CrO 3 )50.0g, lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O) 4.7g and 36g of 25wt% acid silica gel are miscible in 500mL of deionized water; first put 100mL of deionized water into the reactor, and under constant stirring, the copper-chromium-lanthanum-silicon mixture is mixed with 3wt% alkane Ammonia water (18wt%) of base phenol polyoxyethylene ether was added in parallel to control the pH value of the reaction at 6, while raising the temperature of the reaction solution to 40°C. After the addition, the temperature was kept and stirred for 0.5 hours, filtered, and dried at 120°C for 12 hours. Then it was calcined in a muffle furnace at 300°C for 4 hours, and finally ground into a catalyst sample smaller than 120 mesh. The specific surface area of the sample was 128m. 2 / g, the dispersion degree of metallic Cu is 0.68, CuO / Cr in the catalyst 2 O 3 The molar ratio is 2.2, CuO / La 2 O 3 The mo...
Example Embodiment
[0040] Example 2:
[0041] Weigh copper nitrate (Cu(NO 3 ) 2 ·3H 2 O) 145.0g, chromic anhydride (CrO 3 )50.0g, lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O) 3.35g and 25g of 25wt% acid silica gel are miscible in 500mL of deionized water; first put 100mL of deionized water into the reactor, and under constant stirring, the copper-chromium-lanthanum-silicon mixture is mixed with 5wt% Ammonia water (18wt%) of polyvinylpyrrolidone was added in parallel to control the pH of the reaction at 6, and at the same time the temperature of the reaction solution was raised to 40°C. After the addition, the temperature was kept and stirred for 0.5 hours, filtered, and dried at 120°C for 12 hours. Calcined in a furnace at 300°C for 4 hours, and finally milled into a catalyst sample smaller than 120 mesh, the specific surface area of the sample is 130m 2 / g, the dispersion degree of metallic Cu is 0.65, CuO / Cr in the catalyst 2 O 3 The molar ratio is 2.4, CuO / La 2 O 3 The molar ratio is 155.1, CuO / SiO ...
Example Embodiment
[0042] Example 3:
[0043] Weigh copper nitrate (Cu(NO 3 ) 2 ·3H 2 O) 108.7g, chromic anhydride (CrO 3 )50.0g and lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O) 6.5g and 54g of 25wt% acid silica gel are miscible in 500mL deionized water; first, 100mL of deionized water is put into the reactor, and under constant stirring, the copper-chromium-lanthanum-silicon mixture is mixed with 4wt% poly Ethylene glycol ammonia water (18wt%) was added in parallel to control the pH of the reaction at 6, and at the same time the temperature of the reaction solution was increased to 40°C. After the addition, the temperature was kept and stirred for 0.5 hours, filtered, and dried at 120°C for 12 hours. Calcined in a Furnace at 300°C for 4 hours, and finally milled into a catalyst sample smaller than 120 mesh, with a specific surface area of 125m 2 / g, the dispersion of metal Cu is 0.61, CuO / Cr in the catalyst 2 O 3 The molar ratio is 1.8, CuO / La 2 O 3 The molar ratio is 66.6, CuO / SiO 2 The molar ratio i...
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Specific surface area | aaaaa | aaaaa |
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap