Remote controller shell material with antibacterial function and preparation method of remote controller shell material

A shell material and remote control technology, which is applied in the field of polymer resin materials, can solve the problems of poor weather resistance and poor antibacterial sustainability of remote control shell materials, so as to reduce the risk of bacteria harming the human body, prolong the antibacterial life cycle, and improve the effect Effect

Active Publication Date: 2016-04-20
HISENSE VISUAL TECH CO LTD
View PDF15 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problems of poor weather resistance and poor antibacterial sustainability of the remote control shell material when the inorganic silver antibacterial agent or organic antibacterial agent is used alone in the remote control shell material. Composite antibacterial agent, organic antibacterial agent and inorganic antibacterial agent are attached in the composite antibacterial agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Remote controller shell material with antibacterial function and preparation method of remote controller shell material
  • Remote controller shell material with antibacterial function and preparation method of remote controller shell material
  • Remote controller shell material with antibacterial function and preparation method of remote controller shell material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of the remote control shell material of the present invention, 1) soaking the composite antibacterial agent in the coupling agent, then drying the ABS matrix resin and the soaked composite antibacterial agent at 70-80°C for 4-5h respectively; 2 ) According to the formula, other additives except the composite antibacterial agent are uniformly mixed with the ABS matrix resin, and then extruded and granulated with the composite antibacterial agent through a screw extruder to obtain an ABS antibacterial composite material.

[0016] Because the glass fiber will cause damage to the ordinary screw, the screw extruder is reinforced, and the screw length-to-diameter ratio is 37-45. The temperature in zone one: 175-185°C, the temperature in zone two: 185-195°C, the temperature in zone three: 205-215°C, the temperature in zone four: 215-225°C, the temperature in zone five: 205-215°C, the temperature in zone six: 195-205°C, the rotational speed of the screw i...

Embodiment 1

[0023] Composite antibacterial agent is prepared in the following way, and the steps are as follows:

[0024] 1) Use HF, HCL, HNO 3 Mix the acid solution to corrode the glass fiber, add the corrosion inhibitor LAN-826 with a mass fraction of 0.05% of the total acid solution, corrode for 30s, and corrode micropores on the surface of the glass fiber; the diameter of the micropores is 1.2-1.5μm, after the corrosion , wash off the acid solution and corrosion inhibitor on the surface of the glass fiber with deionized water, and then dry. HF, HCL, HNO in mixed acid solution 3 The mass ratio is 10:1:1, wherein the volume concentration of the main acid liquid HF is 2%, and the volume concentration of the auxiliary acid is 0.5%. The glass fiber is cylindrical, with a length of 3-5 mm and a diameter of 30-40 μm.

[0025] 1) Add the dried glass fiber with micropores to the silver ammonia solution, the concentration of the silver ammonia solution is 0.5mol / L, raise the temperature to 5...

Embodiment 2

[0028] Composite antibacterial agent is prepared in the following way, and the steps are as follows:

[0029] 1) Use HF, HCL, HNO 3 Mix the acid solution to corrode the glass fiber, add the corrosion inhibitor LAN-826 with a mass fraction of 0.2% of the total acid solution, corrode for 35s, and corrode micropores on the surface of the glass fiber; the pore size of the micropores is 1.0-1.2 μm, after the corrosion , wash off the acid solution and corrosion inhibitor on the surface of the glass fiber with deionized water, and then dry. HF, HCL, HNO in mixed acid solution 3 The mass ratio is 20:1:1, wherein the volume concentration of the main acid liquid HF is 4%, and the volume concentration of the auxiliary acid is 2%. Among them, the glass fiber is cylindrical, with a length of 5-8 mm and a diameter of 40-50 μm.

[0030] 2) Add the dried glass fiber with micropores into the silver-ammonia solution, the concentration of the silver-ammonia solution is 1.5mol / L, raise the tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
microporeaaaaaaaaaa
Login to view more

Abstract

The invention provides a remote controller shell material with an antibacterial function and a preparation method of the remote controller shell material. The remote controller shell material is prepared from the following components in parts by weight: 81 to 89 parts of ABS matrix resin, 4 to 12 parts of a composite antibacterial agent, 0.1 to 0.14 part of a coupling agent, 2 to 4 parts of a compatilizer, 0.2 to 0.3 part of an antioxidant, and 0.2 to 0.4 part of a lubricant. The preparation method comprises the following steps: (1) wetting the composite antibacterial agent in the coupling agent, and then respectively drying the ABS matrix resin and the wetted composite antibacterial agent under the condition of 70 to 80 DEG C for 4 to 5 hours; (2) uniformly mixing other auxiliaries except for the composite antibacterial agent in the formula with the ABS matrix resin to obtain a mixture, and extruding and granulating the mixture and the composite antibacterial agent through a screw extruding machine to obtain an ABS antibacterial composite material. The remote controller shell material disclosed by the invention adopts the novel composite antibacterial agent, so that the antibacterial slow-release property is improved, the weather fastness is high, and the intensity is high.

Description

technical field [0001] The invention belongs to the technical field of polymer resin materials with antibacterial function, and in particular relates to a remote control shell material with antibacterial function and a preparation method. Background technique [0002] ABS (Acrylonitrile Butadiene Styrenecopolymers, referred to as ABS, the Chinese name is acrylonitrile-butadiene-styrene copolymer) plastic, because of its good comprehensive physical properties, good chemical resistance, easy molding and processing, and low price, it can be realized The high-gloss effect is therefore widely used in the casing of electronic equipment. However, if it is used as a remote control casing, due to prolonged contact with human hands, it will cause bacteria to grow on the surface and increase the potential harm to the human body. Therefore, if a material with antibacterial function is used, the growth of bacteria on the surface of the remote control can be inhibited, and the risk of bac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L35/06C08L5/08C08L91/00C08K13/06C08K9/02C08K9/06C08K7/14C08K3/08C08K5/47
CPCC08L55/02C08L2205/03C08L35/06C08K13/06C08K9/06C08K9/02C08K7/14C08K2003/0806C08K5/47C08L5/08C08L91/00
Inventor 李洋洋何洋
Owner HISENSE VISUAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap