Composite material toughened ceramisite concrete and preparation method thereof

A technology of ceramsite concrete and composite materials, which is applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of seismic and impact resistance to be improved, and achieves improved micro stress-strain performance, easy processing , a wide range of effects

Active Publication Date: 2016-05-04
福建省东霖建设工程有限公司
View PDF3 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the seismic and impact resistance performance tests of the recycled aggregate concrete upper load-bearing structure still need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The preparation method of activated wood powder fiber is: take 45kg of wood powder fiber at room temperature, filter after stirring in 136L20wt% sodium hydroxide aqueous solution for 36h, wood powder fiber is washed to neutrality; Stir in the hydrogen oxide aqueous solution for 30 hours, filter and wash with water; then add the wood powder fiber into the pH 8, 25wt% Tween 20 aqueous solution for 3 hours, stir for 18 hours, filter, wash with water, and vacuum dry at 61 °C Standby after 24h;

[0036] The preparation method of modified silica nanotubes is as follows:

[0037] (1) Put 30 stainless steel balls with a diameter of 10mm and 45 stainless steel balls with a diameter of 5mm in two identical 5L nylon tanks, then add 0.9kg of silica nanotubes, and then add 90ml of Water and ethanol, and sealed with a nylon cover; put two ball mill jars symmetrically into the ball mill, and ball mill for 48 hours at a speed of 400rpm and automatically change the direction of rotatio...

Embodiment 2

[0052] The preparation method of activated wood powder fiber is: take 45kg of wood powder fiber at room temperature, filter after stirring in 136L20wt% sodium hydroxide aqueous solution for 36h, wood powder fiber is washed to neutrality; Stir in the hydrogen oxide aqueous solution for 30 hours, filter and wash with water; then add the wood powder fiber into the pH 8, 25wt% Tween 20 aqueous solution for 3 hours, stir for 18 hours, filter, wash with water, and vacuum dry at 60°C Standby after 24h;

[0053] The preparation method of modified silicon dioxide nanotubes comprises the following steps:

[0054] (1) Put 30 stainless steel balls with a diameter of 10mm and 45 stainless steel balls with a diameter of 5mm in two identical 5L nylon tanks, then add 0.9kg of silica nanotubes, and then add 90ml of Water and ethanol, and sealed with a nylon cover; put two ball mill jars symmetrically into the ball mill, and ball mill for 48 hours at a speed of 400rpm and automatically change ...

Embodiment 3

[0068] The preparation method of activated wood powder fiber is: take wood powder fiber 45kg at room temperature, filter after stirring in 136L20wt% sodium hydroxide aqueous solution for 36h, wood powder fiber is washed to neutrality; Stir in the hydrogen oxide aqueous solution for 30 hours, filter and wash with water; then add the wood powder fiber to the pH 8, 25wt% Tween 20 aqueous solution for 3 hours, stir for 18 hours, filter, wash with water, and vacuum dry at 62°C Standby after 24h;

[0069] The preparation method of modified silicon dioxide nanotubes comprises the following steps:

[0070] (1) Put 30 stainless steel balls with a diameter of 10mm and 45 stainless steel balls with a diameter of 5mm in two identical 5L nylon tanks, then add 0.9kg of silica nanotubes, and then add 90ml of Water and ethanol, and sealed with a nylon cover; put two ball mill jars symmetrically into the ball mill, and ball mill for 48 hours at a speed of 400rpm and automatically change the dir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of preparation of concrete, and in particular relates to composite material toughened ceramisite concrete and a preparation method thereof. The composite material toughened ceramisite concrete comprises the following components in parts by weight: 320-360 parts of cement, 40-80 parts of lithium slagpowder, 20-40 parts of silica fume, 700-900 parts of recycled coarse aggregates, 500-800 parts of ceramisites, 3-4 parts of a water reducing agent, 100-200 parts of water, 10-20 parts of polyacrylate, 20-30 parts of a toughening composite material, 0.05-0.1 part of sodium gluconate, and 10-15 parts of triethanolamine, wherein the toughening composite material is prepared from the following raw materials in parts by weight: 1.2-1.8 parts of modified silicon dioxide nanotubes, 22-28 parts of a styrene-butadiene-styrene block copolymer, 46-50 parts of activated wood powder fibers, 3.5-5 parts of a silane coupling agent, 3.0-3.5 parts of a solubilizing agent, 4-6 parts of a filler and 180-220 parts of water. The concrete has good toughness, isotropy, fatigue resistance, compactness, crack resistance, shock resistance and permeability resistance, and is a high-performance concrete toughening material, and the 28-day compression strength of the prepared concrete can reach 30-60MPa, so that the concrete is suitable for building bearing structures.

Description

technical field [0001] The invention belongs to the field of concrete preparation, and in particular relates to a composite material toughened ceramsite concrete and a preparation method thereof. Background technique [0002] The General Office of the State Council's "Notice on Several Opinions on Promoting the Modernization of the Housing Industry and Improving Housing Quality" stipulates that coastal cities and other cities with scarce land resources have banned the use of solid clay bricks since June 2000 to protect my country's limited land resources. The development of shale ceramsite, fly ash ceramsite, etc. that use no soil or less soil is conducive to the protection of land resources and the promotion of ecological civilization. In foreign countries, ceramsite concrete has been widely used in building blocks and large wall panels, even in load-bearing structures, and the economic benefits are very obvious. Compared with the aerated block which replaces the clay bric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B14/06C04B18/02C04B18/14C04B18/16C04B18/26C04B24/10C04B24/12C04B24/26C04B24/42
CPCC04B20/023C04B20/026C04B28/02C04B18/146C04B18/14C04B18/16C04B18/023C04B24/2641C04B24/10C04B24/122C04B14/062C04B24/26C04B18/26C04B24/42Y02W30/91
Inventor 蒋国平肖三霞
Owner 福建省东霖建设工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com