Anti-seepage acid-resisting concrete and preparation method thereof

A technology of acid-resistant concrete and sodium fluorosilicate, applied in the field of building materials, can solve the problems of affecting production cost and production efficiency, poor impermeability, short service life, etc., to speed up curing speed, improve compactness, improve resistance The effect of permeability

Inactive Publication Date: 2016-05-04
邢台建工商品混凝土有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In some special industries, such as the chemical industry, acid-proof tanks and electroplating tanks often have performance requirements for concrete such as impermeability and acid resistance, but ordinary impermeability and acid-resistant concrete has poor impermeability and short service life, which seriously affects Production Cost and Production Efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of anti-seepage and acid-resistant concrete, comprising the following components:

[0023] 420kg of cement, 630kg of quartz sand, 800kg of basalt, 178kg of water, 30kg of coal gangue powder, 70kg of fly ash, 60kg of silica fume, 300kg of water glass, 220kg of porcelain powder, 45kg of sodium fluorosilicate, 6kg of hollow glass fiber and high-efficiency polycarboxylic acid Water reducing agent 12.2kg.

[0024] Each component has the following technical indicators: the water glass is a soluble sodium silicate liquid, the modulus is 2.7-3.0, and the specific gravity is 1.4-1.44; the sodium fluorosilicate: the purity is 92%, and it passes through a square hole of 0.10-0.15mm The remaining 8% is sieved; the fineness of the porcelain powder is 4900 holes / cm2 and the remaining 15% is sieved; the quartz sand: the bulk density is 1.6t / m 3 , specification: 1.5mm, its acid resistance is 93%; the basalt: bulk density 3.3t / m 3 , specification 23mm; said cement: ordinary por...

Embodiment 2

[0034] A kind of anti-seepage and acid-resistant concrete, comprising the following components:

[0035] 380kg of cement, 530kg of quartz sand, 900kg of basalt, 190kg of water, 40kg of coal gangue powder, 75kg of fly ash, 65kg of silica fume, 330kg of water glass, 250kg of porcelain powder, 35kg of sodium fluorosilicate, 5kg of hollow glass fiber and high-efficiency polycarboxylic acid Water reducer 10kg.

[0036] Each component has the following technical indicators: the water glass is a soluble sodium silicate liquid, the modulus is 2.7-3.0, and the specific gravity is 1.4-1.44; the sodium fluorosilicate: the purity is 92%, and it passes through a square hole of 0.10-0.15mm The remaining 8% is sieved; the fineness of the porcelain powder is 4900 holes / cm2 and the remaining 15% is sieved; the quartz sand: the bulk density is 1.6t / m 3 , specification: 1.5mm, its acid resistance is 93%; the basalt: bulk density 3.3t / m 3 , specification 23mm; the cement: ordinary Portland ceme...

Embodiment 3

[0046] A kind of anti-seepage and acid-resistant concrete, comprising the following components:

[0047] 470kg of cement, 580kg of quartz sand, 860kg of basalt, 175kg of water, 37kg of coal gangue powder, 80kg of fly ash, 70kg of silica fume, 280kg of water glass, 200kg of porcelain powder, 40kg of sodium fluorosilicate, 9kg of hollow glass fiber and high-efficiency polycarboxylic acid Water reducer 8.1kg.

[0048] Each component has the following technical indicators: the water glass is a soluble sodium silicate liquid, the modulus is 2.7-3.0, and the specific gravity is 1.4-1.44; the sodium fluorosilicate: the purity is 92%, and it passes through a square hole of 0.10-0.15mm The remaining 8% is sieved; the fineness of the porcelain powder is 4900 holes / cm2 and the remaining 15% is sieved; the quartz sand: the bulk density is 1.6t / m 3 , specification: 1.5mm, its acid resistance is 93%; the basalt: bulk density 3.3t / m 3 , specification 23mm; the cement: ordinary Portland cem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
power levelaaaaaaaaaa
Login to View More

Abstract

The invention provides anti-seepage acid-resisting concrete and a preparation method thereof. The anti-seepage acid-resisting concrete is prepared from the following components in parts by weight: 380 to 470 parts of cement, 530 to 630 parts of quartz sand, 800 to 900 parts of basalt, 175 to 190 parts of water, 30 to 40 parts of coal gangue micro powder, 70 to 80 parts of coal ash, 60 to 70 parts of silica fume, 280 to 330 parts of water glass, 200 to 250 parts of synthetic cement, 35 to 45 parts of sodium fluosilicate, 5 to 9 parts of hollow glass fiber and 8.1 to 12.2 parts of additive; the preparation method of the anti-seepage acid-resisting concrete adopts a manner of adding materials in batches, and the stirring time is reasonably adjusted; the anti-seepage acid-resisting concrete provided by the invention is reasonable in component matching structure, the preparation method is simple and effective, and the problems of seepage resistance and acid resistance of concrete are effectively solved.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an anti-seepage and acid-resistant concrete and a preparation method thereof. Background technique [0002] Concrete is one of the most commonly used building materials. It is an engineering composite material that binds aggregates into a whole by cementitious materials. Generally, cement is used as cementitious material, sand and stone are used as aggregate, mixed with water (may contain admixtures and admixtures) in a certain proportion, and obtained by stirring. It is widely used in civil engineering. In some special industries, such as the chemical industry, acid-proof tanks and electroplating tanks often have performance requirements for concrete such as impermeability and acid resistance, but ordinary impermeability and acid-resistant concrete has poor impermeability and short service life, which seriously affects Production cost and production efficiency. Contents of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B111/23C04B111/27
CPCC04B28/26C04B2111/23C04B2111/27C04B7/02C04B14/06C04B14/04C04B18/12C04B18/08C04B18/146C04B18/023C04B22/126C04B14/42C04B2103/302
Inventor 南春明
Owner 邢台建工商品混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com