Self-adhesive vacuum-plating electronic protective film

A technology of vacuum plating and protective film, applied in the directions of adhesives, conductive adhesives, polymer adhesive additives, etc., can solve the problems of large stretching degree, poor adhesion, and warping of protective films, and achieve easy solutions. The effect of warping, good adhesion, and improved conductivity

Active Publication Date: 2016-05-11
广东顺德君盈包装科技股份有限公司
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the low price of polyethylene material, the viscosity can be adjusted in a wide range according to different application requirements, so the current vacuum coating protective film base material is mainly made of polyethylene, which is prepared by extrusion molding, injection molding, blow molding and other methods. However, since pol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: A kind of self-adhesive vacuum plating electronic protection film, comprises the component of following weight portion: 20 parts of thermoplastic polyester elastomers; 3 parts of polyolefin elastomers; 2 parts of PE waxes; 5 parts of high-density polyethylenes; 3 parts of vinyl alcohol; 1 part of nano silicon carbide; 1 part of tackifying resin; 0.1 part of antioxidant; 1 part of functional monomer; 1 part of antistatic agent.

[0027] Among them, the thermoplastic polyester elastomer is a hard segment formed by polyester composed of aromatic dicarboxylic acid and alicyclic diol, and aliphatic polycarbonate or polyoxyalkylene glycol with 3 carbon atoms A thermoplastic polyester elastomer formed by combining soft segments composed of polyester; the antistatic agent is a 1:1 mixture of glycerol monostearate and erucamide.

Embodiment 2

[0028] Embodiment 2: A kind of self-adhesive vacuum plating electronic protection film, comprises the component of following weight portion: 30 parts of thermoplastic polyester elastomers; 5 parts of polyolefin elastomers; 7 parts of PE waxes; 15 parts of high-density polyethylenes; 5 parts of vinyl alcohol; 4 parts of nano silicon carbide; 2 parts of tackifying resin; 0.5 parts of antioxidant; 4 parts of functional monomer; 4 parts of antistatic agent.

[0029] Among them, the thermoplastic polyester elastomer is composed of a hard segment of polyester composed of aromatic dicarboxylic acid and alicyclic diol, and aliphatic polycarbonate or polyoxyalkylene glycol with 6 carbon atoms A thermoplastic polyester elastomer formed by combining soft segments composed of polyester; the antistatic agent is a 1:1 mixture of glycerol monostearate and erucamide.

Embodiment 3

[0030] Embodiment 3: a kind of self-adhesive vacuum plating electronic protection film, comprises the component of following parts by weight: 40 parts of thermoplastic polyester elastomers; 8 parts of polyolefin elastomers; 10 parts of PE waxes; 25 parts of high-density polyethylenes; 8 parts of vinyl alcohol; 6 parts of nano silicon carbide; 3 parts of tackifying resin; 1 part of antioxidant; 5 parts of functional monomer; 5 parts of antistatic agent.

[0031] Among them, the thermoplastic polyester elastomer is composed of a hard segment of polyester composed of aromatic dicarboxylic acid and alicyclic diol, and aliphatic polycarbonate or polyoxyalkylene glycol with 10 carbon atoms A thermoplastic polyester elastomer formed by combining soft segments composed of polyester; the antistatic agent is a 1:1 mixture of glycerol monostearate and erucamide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a self-adhesive vacuum-plating electronic protective film which comprises a thermoplastic polyester elastomer, a polyolefin elastomer, PE (polyethylene) wax, high-density polyethylene, polyvinyl alcohol, nano silicon carbide, a tackifying resin, an antioxidant, a functional monomer and an antistatic agent. When in use, the self-adhesive vacuum-plating electronic protective film disclosed by the invention has the advantages of no surface wrinkling or deformation, stable adhesive force, favorable adhesiveness, favorable repeeling property, no residual adhesive phenomenon, favorable barrier property, favorable mechanical properties and lower dielectric constant, is an excellent vacuum-plating protective film material, and is nontoxic, environment-friendly, safe and practical.

Description

technical field [0001] The present invention relates to a membrane material. More specifically, the present invention relates to a self-adhesive vacuum-plated electronic protection film. Background technique [0002] The vacuum coating protective film is generally a modified polymer matrix protective film material, which has the characteristics of self-adhesive and thermal shrinkage, and is mainly composed of a polymer substrate and a pressure-sensitive functional material. Compared with surface protection coatings, it has the advantages of convenient use, low price, and reliable effect, and has attracted much attention in the field of material surface protection. Due to the low price of polyethylene materials, the viscosity can be adjusted in a wide range according to different application requirements, so the current vacuum coating protective film substrate mainly uses polyethylene as raw material, and is prepared by extrusion molding, injection molding, blow molding and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J7/00C09J4/02C09J4/06C09J9/02C09J11/08C09J11/04
CPCC09J4/06C09J7/00C09J9/02C09J11/04C09J11/08C09J2301/314C09J2301/408
Inventor 孙政良
Owner 广东顺德君盈包装科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap