High-durability high-efficiency nano antimicrobial water-based wood paint and preparation method thereof

A wood coating, high-efficiency technology, applied in antifouling/underwater coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve the problems of low production cost, low VOC value of coatings, poor compatibility of matrix resin emulsions, etc. Achieve good stability, long-lasting antibacterial performance and good compatibility

Inactive Publication Date: 2016-06-08
HUZHOU NEW AOKE CHEM CO LTD
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating prepared by the invention has low VOC value, anti-blocking, scratch resistance, pollution resistance, yellowing resistance and good sealing performance, but it adds more inorganic nanoparticles, low production cost, and poor compatibility with matrix resin emulsion. poor stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A long-lasting and high-efficiency nano antibacterial water-based wood coating, calculated in parts by weight, comprising the following steps:

[0055] 15 parts of water-based polyurethane resin emulsion,

[0056] 15 parts of water-based acrylic modified polyurethane resin emulsion,

[0057] 20 parts of water-based alkyd resin emulsion,

[0058] Polycarboxybetaine methyl methacrylate 5 parts,

[0059] 6 parts of hydroxyethyl cellulose, 8 parts of sodium hexametaphosphate,

[0060] 5 parts of nitrocellulose ester, 2 parts of fumaropimaric acid,

[0061] 1.5 parts of nano-titanium oxide, 1 part of nano-porous silica,

[0062] 0.8 part of nano-zinc oxide, 1 part of nano-hydroxyapatite,

[0063] 1 part of pH adjuster, 4 parts of defoamer, 1 part of dispersant,

[0064] 1 part of leveling agent and 10 parts of deionized water.

[0065] The preparation method includes the following steps:

[0066] (1) Mix the water-based polyurethane resin emulsion, the water-based acrylic modified polyuretha...

Embodiment 2

[0070] A long-lasting and high-efficiency nano antibacterial water-based wood coating, calculated in parts by weight, comprising the following steps:

[0071] 20 parts of water-based polyurethane resin emulsion,

[0072] 20 parts of water-based acrylic modified polyurethane resin emulsion,

[0073] 30 parts of water-based alkyd resin emulsion,

[0074] 10 parts of polycarboxybetaine methyl methacrylate,

[0075] 9 parts of hydroxyethyl cellulose, 12 parts of sodium hexametaphosphate,

[0076] 10 parts of nitrocellulose ester, 4 parts of fumaric acid,

[0077] 3 parts of nano-titanium oxide, 3 parts of nano-porous silica,

[0078] 1.3 parts of nano zinc oxide, 1.8 parts of nano hydroxyapatite,

[0079] 2 parts of pH adjuster, 6 parts of defoamer, 3 parts of dispersant,

[0080] 2 parts of leveling agent and 20 parts of deionized water.

[0081] The preparation method includes the following steps:

[0082] (1) Mix the water-based polyurethane resin emulsion, the water-based acrylic modified poly...

Embodiment 3

[0086] A long-lasting and high-efficiency nano antibacterial water-based wood coating, calculated in parts by weight, comprising the following steps:

[0087] 15 parts of water-based polyurethane resin emulsion,

[0088] 17 parts of water-based acrylic modified polyurethane resin emulsion,

[0089] 22 parts of water-based alkyd resin emulsion,

[0090] 8 parts of polycarboxybetaine methyl methacrylate,

[0091] 7 parts of hydroxyethyl cellulose, 10 parts of sodium hexametaphosphate,

[0092] 9 parts of nitrocellulose ester, 2.5 parts of fumaropimaric acid,

[0093] 2 parts of nano-titanium oxide, 1.5 parts of nano-porous silica,

[0094] 1 part of nano-zinc oxide, 1.4 parts of nano-hydroxyapatite,

[0095] 1.5 parts of pH adjuster, 4 parts of defoamer, 2 parts of dispersant,

[0096] 2 parts of leveling agent and 18 parts of deionized water.

[0097] The preparation method includes the following steps:

[0098] (1) Mix the water-based polyurethane resin emulsion, the water-based acrylic modifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-durability high-efficiency nano antimicrobial water-based wood paint which comprises the following components in parts by weight: 15-20 parts of water-based polyurethane resin emulsion, 15-20 parts of water-based acrylic modified polyurethane resin emulsion, 20-30 parts of water-based alkyd resin emulsion, 5-10 parts of polycarboxylic acid betaine methyl methacrylate, 6-9 parts of hydroxyethyl cellulose, 8-12 parts of sodium hexametaphosphate, 5-10 parts of nitrocellulose ester, 2-4 parts of fumaropimaric acid, 1.5-3 parts of nano titanium oxide, 1-3 parts of nano porous silicon oxide, 0.8-1.3 parts of nano zinc oxide, 1-1.8 parts of nano hydroxyapatite, 1-2 parts of pH regulator, 4-6 parts of defoaming agent, 1-3 parts of dispersing agent, 1-2 parts of leveling agent and 10-20 parts of deionized water. The wood paint has the advantages of broad spectrum, high efficiency, durable antimicrobial property, high stability, favorable adhesion resistance, favorable scratch resistance, favorable closeness and low VOC (volatile organic compound) content.

Description

Technical field: [0001] The invention belongs to the technical field of coatings, and particularly relates to a durable and efficient nanometer antibacterial waterborne wood coating. Background technique: [0002] With the rapid development of industry and the deteriorating environment, coatings are developing in the direction of functionalization and ecologicalization. The development of functional coatings that meet environmental protection requirements has become the consensus of the industry. Wood coatings account for more than 10% of the world's total coating consumption. In the field of wood coatings, furniture plays an important role in people's working and living environments, but it may also become a medium for the spread of germs. In recent years, the harm of various bacteria and viruses has obviously increased. According to the microbiological test of daily office desks by Fudan University School of Medicine, the harmful bacteria Hanlang is 4 times that of ordinary bat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D175/04C09D175/14C09D7/12C09D5/14
CPCC09D167/08C08K2201/011C08L2205/02C08L2205/025C08L2205/035C09D5/14C09D7/61C09D7/63C09D7/65C08L75/04C08L75/14C08L1/284C08L1/18C08K13/04C08K7/26C08K2003/2296C08K2003/2241C08K2003/324
Inventor 严连庆
Owner HUZHOU NEW AOKE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap