Metakaolin-based paint coating and preparation method thereof

A technology for metakaolin and paint, applied in the field of metakaolin-based paint and coating and its preparation, can solve the problems of no fire and fire resistance, high cost, weak acid and alkali resistance, etc., and achieve good waterproof, low material cost, Simple preparation process

Inactive Publication Date: 2016-06-08
茂名高岭科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

General paint adhesion is not strong, acid resistance and alkali resistance are not strong, water resistance is not high, there are defects to a certain extent, and cannot meet people's needs
There are deficiencies in the existing paints in the market, whether they have fire-resistant and fire-resistant effects, and it is difficult to make up for losses in the event of fire, etc., and the cost of raw materials for paint production is relatively high, which cannot meet the economic benefits of users.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) Add 28 parts of paint powder, 15 parts of metakaolin, 40 parts of water solvent, and 20 parts of ethanol into the mixing equipment, and then stir for 15 minutes at a temperature of 75°C;

[0029] 2) Add 20 parts of ethyl acetate, 15 parts of ethyl butyl ester, 20 parts of butyl stearate, 4 parts of polyvinyl butyral, and 12 parts of methyl ethyl ketone, and then stir for 20 minutes at a temperature of 55°C;

[0030] 3) Then add 3 parts of water-soluble resin, 12 parts of acrylonitrile, 3 parts of methyl methacrylate, 3 parts of acetic acid, 3 parts of gelatin, 5 parts of ethyl cellosolve, and 3 parts of silicone oil, and then add the Under stirring for 15 minutes, metakaolin-based paint coating 1 was obtained.

Embodiment 2

[0032] 1) Add 25 parts of paint powder, 25 parts of metakaolin, 30 parts of water solvent, and 30 parts of ethanol into the mixing equipment, and then stir for 25 minutes at a temperature of 60°C;

[0033] 2) Add 15 parts of ethyl acetate, 20 parts of ethyl butyl ester, 15 parts of butyl stearate, 7 parts of polyvinyl butyral, and 8 parts of methyl ethyl ketone, and then stir for 25 minutes at a temperature of 45°C;

[0034] 3) Then add 6 parts of water-soluble resin, 10 parts of acrylonitrile, 6 parts of methyl methacrylate, 1 part of acetic acid, 6 parts of gelatin, 2 parts of ethyl cellosolve, and 5 parts of silicone oil, and then add the Under stirring for 20 minutes, metakaolin-based paint coating 2 was obtained.

Embodiment 3

[0036] 1) Add 26 parts of paint powder, 20 parts of metakaolin, 35 parts of water solvent, and 25 parts of ethanol into the mixing equipment, and then stir for 20 minutes at a temperature of 70°C;

[0037] 2) Add 18 parts of ethyl acetate, 18 parts of ethyl butyl ester, 18 parts of butyl stearate, 5 parts of polyvinyl butyral, and 10 parts of methyl ethyl ketone, and then stir for 22 minutes at a temperature of 50°C;

[0038] 3) Then add 4 parts of water-soluble resin, 11 parts of acrylonitrile, 5 parts of methyl methacrylate, 2 parts of acetic acid, 4 parts of gelatin, 3 parts of ethyl cellosolve, and 4 parts of silicone oil, and then add the Under stirring for 18 minutes, metakaolin-based paint coating 3 was obtained.

[0039] Effect example

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wear resistanceaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of chemical materials and particularly relates to a metakaolin-based paint coating and a preparation method thereof. The metakaolin-based paint coating is prepared from, by weight, 25-28 parts of paint powder, 15-25 parts of metakaolin, 30-40 parts of hydrosolvent, 20-30 parts of ethyl alcohol, 15-20 parts of ethyl acetate, 15-20 parts of ethyl butyl ester, 15-20 parts of butyl stearate, 4-7 parts of polyvinyl butyral, 8-12 parts of methyl ethyl ketone, 3-6 parts of water-soluble resin, 10-12 parts of acrylonitrile, 3-6 parts of methyl methacrylate, 1-3 parts of acetic acid, 3-6 parts of solidification glue, 2-5 parts of ethyl cellosolve and 3-5 parts of silicon oil. The metakaolin-based paint coating has excellent waterproof, fireproof, antibacterial and anti-corrosion functions and is low in material cost, simple in preparation process and suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of chemical materials, and in particular relates to a metakaolin-based paint coating and a preparation method thereof. Background technique [0002] Lacquer is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. Paint is a coating made of raw materials such as iron oxide or resin to decorate and protect objects. It is a viscous oily pigment, flammable when wet, insoluble in water, slightly soluble in fat, soluble in alcohol, aldehyde, ether, benzene, alkanes, easily soluble in gasoline, kerosene, diesel. [0003] In recent years, with the development of the national economy, various glass paint products have appeared in people's lives. Glass paint is used everywhere in housing decoration, store decoration, sliding doors, furniture products, bathroom products, glass handicraft processing, etc., making the waterproof paint ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/18C09D5/14C09D5/08C09D7/12
CPCC09D201/00C08K2201/014C08L2201/02C08L2205/035C09D5/08C09D5/14C09D5/18C09D7/61C09D7/63
Inventor 梅明军
Owner 茂名高岭科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products