Impact-resistance-modified polyvinyl chloride composite material

A technology of impact-resistant modification and polyvinyl chloride, which is applied in the field of impact-resistant modified polyvinyl chloride composite materials, can solve the problems of difficulty in achieving a balance between impact resistance and processing performance, difficult processing of polyvinyl chloride, and poor impact performance. , to achieve the effect of promoting the carbonization reaction, good dispersibility, and improving flame retardant and smoke suppression.

Inactive Publication Date: 2016-06-15
ANHUI LANTONG TECH CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the impact performance of polyvinyl chloride is poor, which limits the application of polyvinyl chloride to a large extent.
Although the addition of toughening agent modified polyvinyl chloride can improve the impact performance of polyvinyl chloride material, but the addition of too much toughening agent will increase the melt viscosity of polyvinyl chloride, thus making the processing of polyvinyl chloride difficult and causing consumption Can improve and product deterioration
In the current modification method, it is difficult to achieve a balance between impact resistance and processability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of impact-resistant modified polyvinyl chloride composite material proposed by the present invention, its raw material comprises the following components by weight: 100 parts of polyvinyl chloride, 0.5 parts of polyurethane, 8 parts of methyl methacrylate-butyl acrylate copolymer, 0.5 parts of polystyrene, 2 parts of polytetrafluoroethylene, 0.1 parts of nanographite microflakes, 2 parts of magnesium hydroxide, 2 parts of zinc stannate, 10 parts of zinc borate, 1 part of chlorinated paraffin, 12 parts of organically modified montmorillonite 1 part, 1 part of poly-4-methyl-1-pentene, 5 parts of sulfonated polyethersulfone, 0.5 part of methyl tin mercaptide, 5 parts of epoxy soybean oil, 0.5 part of pentaerythritol, tris(2,4 phosphite - 2.5 parts of di-tert-butylphenyl) ester, 1 part of hexamethylphosphoric triamide, 6 parts of triethyl phosphate;

[0019] Wherein, the nano graphite flakes are modified nano graphite flakes; the modified nano graphite flakes are pre...

Embodiment 2

[0021] A kind of impact-resistant modified polyvinyl chloride composite material proposed by the present invention, its raw material comprises the following components by weight: 100 parts of polyvinyl chloride, 2 parts of polyurethane, 2 parts of methyl methacrylate-butyl acrylate copolymer, 2 parts of polystyrene, 0.5 parts of polytetrafluoroethylene, 1 part of nanographite microflakes, 0.5 parts of magnesium hydroxide, 5 parts of zinc stannate, 4 parts of zinc borate, 5 parts of chlorinated paraffin, 3 parts of organically modified montmorillonite Parts, 5 parts of poly-4-methyl-1-pentene, 2 parts of sulfonated polyethersulfone, 2 parts of methyl tin mercaptide, 2 parts of epoxy soybean oil, 3 parts of pentaerythritol, tris(2,4 - 1 part of di-tert-butylphenyl) ester, 2.5 parts of hexamethylphosphoric triamide, 1 part of triethyl phosphate;

[0022] Wherein, the nano graphite flakes are modified nano graphite flakes; the modified nano graphite flakes are prepared according t...

Embodiment 3

[0024] A kind of anti-impact modified polyvinyl chloride composite material proposed by the present invention, its raw material comprises the following components by weight: 100 parts of polyvinyl chloride, 1.3 parts of polyurethane, 6 parts of methyl methacrylate-butyl acrylate copolymer, 1.4 parts of polystyrene, 1.6 parts of polytetrafluoroethylene, 0.7 parts of nanographite microflakes, 1.4 parts of magnesium hydroxide, 3.2 parts of zinc stannate, 8.2 parts of zinc borate, 3 parts of chlorinated paraffin, 10 parts of organically modified montmorillonite 3.2 parts of poly-4-methyl-1-pentene, 3.6 parts of sulfonated polyethersulfone, 1.2 parts of methyl tin mercaptide, 3.6 parts of epoxy soybean oil, 1.5 parts of pentaerythritol, tris(2,4 - 1.7 parts of di-tert-butylphenyl) ester, 2 parts of hexamethylphosphoric triamide, 3.2 parts of triethyl phosphate;

[0025] Wherein, the degree of polymerization of the polyvinyl chloride is 1200, and the intrinsic viscosity is 100mL / g; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses an impact-resistance-modified polyvinyl chloride composite material which is prepared from polyvinyl chloride, polyurethane, methyl methacrylate-butyl acrylate copolymer, polystyrene, polytetrafluoroethylene, nano graphite microsheets, magnesium hydroxide, zinc stannate, zinc borate, chlorinated paraffin, organic modified montmorillonite, poly-4-methyl-1-amylene, sulfonated polyethersulfone, methyl tin mercaptide, epoxy soybean oil, pentaerythritol, tri(2,4- di-tert-phenyl) phosphite, hexamethyl phosphoric triamide and triethyl phosphate. The impact-resistance-modified polyvinyl chloride composite material disclosed by the invention has the advantages of favorable toughness, excellent impact resistance, excellent processability, high flame retardancy and favorable antistatic property.

Description

technical field [0001] The invention relates to the technical field of polyvinyl chloride materials, in particular to an impact-resistant modified polyvinyl chloride composite material. Background technique [0002] Polyvinyl chloride (PVC) is a thermoplastic high polymer produced by polymerization of vinyl chloride monomer. Because of its excellent flame retardancy, abrasion resistance, chemical corrosion resistance, comprehensive mechanical and physical properties, product transparency, It has the advantages of electrical insulation, low price, and convenient processing and installation. It has become one of the five general-purpose synthetic resins in the world. It has been widely used in the production of products with different characteristics, such as pipes, doors and windows, etc. But the impact performance of polyvinyl chloride is poor, which limits the application of polyvinyl chloride to a large extent. Although the addition of toughening agent modified polyvinyl ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L75/04C08L33/12C08L25/06C08L27/18C08L81/06C08L91/06C08K13/06C08K9/06C08K7/00C08K3/04C08K3/22C08K3/38C08K3/24C08K5/526C08K5/521C08K5/5399C08K3/34
CPCC08L27/06C08K2201/011C08L2201/02C08L2201/04C08L2201/08C08L2205/035C08L75/04C08L33/12C08L25/06C08L27/18C08L81/06C08L91/06C08K13/06C08K9/06C08K7/00C08K3/04C08K2003/2224C08K2003/387C08K3/24C08K5/526C08K5/521C08K5/5399C08K3/346
Inventor 谭中全
Owner ANHUI LANTONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com