A kind of ultra-smooth self-cleaning coating and preparation method thereof

An ultra-smooth, coating technology, applied in the direction of coating, can solve the problems of poor practicability, unsuitable for on-site construction, rising cost, etc., to achieve the effects of convenient operation, enhanced stability and good practicability

Active Publication Date: 2018-02-02
ZHEJIANG UNIV
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The super-hydrophilic self-cleaning coating requires high-temperature calcination in the later stage, which is not suitable for on-site construction, nor is it suitable for the surface of organic materials, and organic alkoxides are mostly used as raw materials, which increases the cost and poor practicability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-smooth self-cleaning coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Under the protection of nitrogen, mix tetraethyl orthosilicate component A, silica sol component B, silane coupling agent component C, and solvent D uniformly at 20°C, add catalyst E drop by drop, and hydrolysis and condensation reaction 2 Hours, a sol-like organic-inorganic hybrid coating is obtained, wherein the mass ratio of components A, B, C, D, and E is 1:0.3:1.9:2.0:0.9.

[0033] The sol-like coating prepared above was sprayed onto the surface of a glass slide, and heat-treated at 100° C. for 1 hour to obtain an organic-inorganic hybrid coating. Then dip the coating into silicone oil F, remove excess silicone oil to get an ultra-smooth self-cleaning coating.

[0034] In this example, the silica sol component B is a silica ethanol sol with a pH=2, a solid content of 50%, and a particle size of 10 nm, and the silane coupling agent component C is methyltriethoxy Silane, dimethyldimethoxysilane, phenyltriethoxysilane composition; solvent D is ethanol; catalyst E is ...

Embodiment 2

[0038] Under the protection of nitrogen, mix tetraethyl orthosilicate component A, silica sol component B, silane coupling agent component C, and solvent D uniformly at 10°C, add catalyst E drop by drop, and hydrolysis and condensation reaction 1 Hours, a sol-like organic-inorganic hybrid coating was obtained, wherein the mass ratio of components A, B, C, D, and E was 1:0:6.8:4.0:2.8.

[0039] The sol-like coating prepared above was sprayed on the surface of the silicon chip, and heat-treated at 80° C. for 5 hours to obtain an organic-inorganic hybrid coating. Then soak the coating in silicone oil F to get an ultra-smooth self-cleaning coating soaked in silicone oil.

[0040] Silane coupling agent component C is methyltriethoxysilane, dimethyldimethoxysilane, phenyltriethoxysilane composition in the present embodiment; Solvent D is propanol; Catalyst E is concentration 10 %wt of acetic acid; Silicone oil F is methyl silicone oil with a viscosity of 50mPa·s. The test data of ...

Embodiment 3

[0043]Under nitrogen protection, tetraethyl orthosilicate component A, silica sol component B, silane coupling agent component C, and solvent D were mixed uniformly at 40°C, catalyst E was added, and the hydrolysis and condensation reaction was carried out for 3 hours. An organic-inorganic hybrid coating material is obtained, wherein the mass ratio of components A, B, C, D, and E is 1:0:2.1:5.0:0.9.

[0044] Spray the above-prepared sol-like coating onto the surface of a glass slide, and heat-treat it at 120°C for 2 hours to obtain an organic-inorganic hybrid coating, and then soak the coating in silicone oil to obtain an ultra-smooth coating soaked in silicone oil .

[0045] Silane coupling agent component C is methyltriethoxysilane, dimethyldimethoxysilane, phenyltriethoxysilane composition in this example; Solvent D is methyl alcohol; Catalyst E is concentration 4%wt Sulfuric acid; lubricating oil F is 500mPa·s end epoxy silicone oil. The detection data of the ultra-smoot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-smooth self-cleaning coating and a preparation method thereof. The preparation steps of the coating are as follows: under the protection of nitrogen, tetraethyl orthosilicate, silica sol, silane coupling agent and solvent are uniformly mixed, Adding a catalyst, hydrolyzing and condensing at 10-50°C for 1-5 hours to obtain a sol-like coating material, spraying the coating on the surface of the substrate, and then heat-treating to obtain an organic-inorganic hybrid coating; the coating After soaking the layer in silicone oil, take out and remove excess silicone oil to obtain the ultra-smooth self-cleaning coating of the present invention, the hysteresis angle of water droplets on it is less than 5°, has anti-fouling self-cleaning performance, and can be used for anti-fouling of marine and medical equipment and self-cleaning materials. The invention has the advantages of transparent coating, good stability, long service life, simple process, easy operation and convenient application.

Description

technical field [0001] The invention relates to a method for preparing an ultra-smooth coating on the surface of a substrate, and belongs to the technical field of antifouling and self-cleaning coatings. Background technique [0002] There are many ways to prepare antifouling and self-cleaning coatings, and there are two different ways according to different principles: one is super-hydrophobic self-cleaning coating; the other is super-hydrophilic self-cleaning coating. Super-hydrophobic self-cleaning coating means that when water droplets fall on the surface of the material, the contact angle is greater than 150°. When the water droplets are easy to roll, they will take away the dust and sludge together to achieve the purpose of self-cleaning. Super-hydrophilic self-cleaning coating means that water droplets fall on the surface of the material, the contact angle of water droplets is less than 10°, and water forms a water film on the surface of the material. The surface of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D183/06C09D183/08C09D1/00C03C17/42
Inventor 张庆华韦存茜詹晓力陈丰秋
Owner ZHEJIANG UNIV