Magnesium-based inorganic adhesive modified with silicon-acrylic emulsion for straw and preparation method thereof

A technology of inorganic adhesives and silicon-acrylic emulsions, applied in the direction of inorganic adhesives, adhesives, adhesive additives, etc., can solve problems such as poor water resistance, warping and deformation of straw boards, and reduced strength, so as to improve water resistance and avoid Effect of warping deformation and improvement of deformation ability

Active Publication Date: 2018-08-07
CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the condensation speed of the magnesium-based inorganic adhesive is fast, so that the reaction heat of the magnesium-based inorganic adhesive is too concentrated during the hardening process, and the strength phase cannot be formed well, resulting in warping and deformation of the straw board, lower strength, and higher brittleness. Large; and poor water resistance, it is easy to absorb moisture in the air and cause brine flooding, which seriously affects the decorative quality and use effect of cemented products, reduces the strength of cemented products, and shortens the service life of cemented products. Especially in high humidity areas
Although the use of silica fume, phosphoric acid, sulfate, urea-formaldehyde resin, etc. can improve one or several defects of magnesium-based inorganic adhesives, the effect is not satisfactory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium-based inorganic adhesive modified with silicon-acrylic emulsion for straw and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An embodiment of the magnesium-based inorganic adhesive modified with silicon-acrylic emulsion for straw of the present invention and its preparation method, the preparation method of the adhesive comprises the following steps:

[0034] (1) 167 parts by weight of water are placed in the reaction kettle, heated up to 60° C., adding 100 parts by weight of magnesium chloride hexahydrate (wherein the mass fraction of magnesium chloride is 46%) and stirring at a constant speed for 10 minutes to form a transparent magnesium chloride solution, Stirring speed is 250r / min;

[0035] (2) in above-mentioned magnesium chloride solution, slowly add the magnesium sulfate heptahydrate of 61 parts by weight and stir at a constant speed for 20 minutes;

[0036] (3) Then add 218 parts by weight of light-burned magnesia (wherein the mass fraction of magnesia is 85%) in the reactor, and stir at a constant speed for 15 minutes;

[0037] (4) Slowly add 10 parts by weight of silicon acrylic e...

Embodiment 2

[0040] An embodiment of the magnesium-based inorganic adhesive modified with silicon-acrylic emulsion for straw of the present invention and its preparation method, the preparation method of the adhesive comprises the following steps:

[0041] (1) 184 parts by weight of water are placed in the reactor, the temperature is raised to 55°C, and 100 parts by weight of magnesium chloride hexahydrate (wherein the mass fraction of magnesium chloride is 46%) is added and stirred at a constant speed for 8 minutes to form transparent magnesium chloride Solution, stirring speed is 300r / min;

[0042] (2) in above-mentioned magnesium chloride solution, slowly add the magnesium sulfate heptahydrate of 51 parts by weight and stir at a constant speed for 15 minutes;

[0043] (3) Then add 223 parts by weight of light-burned magnesia (wherein the mass fraction of magnesia is 85%) in the reactor, and stir at a constant speed for 15 minutes;

[0044] (4) slowly join the silicon acrylic emulsion (...

Embodiment 3

[0047] An embodiment of the magnesium-based inorganic adhesive modified with silicon-acrylic emulsion for straw of the present invention and its preparation method, the preparation method of the adhesive comprises the following steps:

[0048] (1) 202 parts by weight of water are placed in the reactor, the temperature is raised to 65°C, and 100 parts by weight of magnesium chloride hexahydrate (wherein the mass fraction of magnesium chloride is 46%) is added and stirred at a constant speed for 5 minutes to form transparent magnesium chloride Solution, stirring speed is 350r / min;

[0049] (2) in above-mentioned magnesium chloride solution, slowly add the magnesium sulfate heptahydrate of 44 parts by weight and stir at a constant speed for 10 minutes;

[0050] (3) Then add 298 parts by weight of light-burned magnesia (wherein the mass fraction of magnesia is 85%) in the reactor, and stir at a constant speed for 15 minutes;

[0051] (4) by dropping funnel, the silicon-acrylic em...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a silicon acrylic emulsion modified magnesium-containing inorganic adhesive for straws. The adhesive is prepared from, by weight, 100 parts of magnesium chloride hexahydrate, 44-61 parts of magnesium sulfate heptahydrate, 218-298 parts of light calcined magnesia, 167-202 parts of water, 10-43 parts of silicone acrylic emulsion and 4-9 parts of dispersant. Adhered products prepared with the adhesive are high in water resistance, strength and toughness and appropriate in coagulation rate. The invention further discloses a preparation method of the silicone acrylic emulsion modified magnesium-containing inorganic adhesive. The method includes steps: feeding water into a reaction kettle, heating, adding the magnesium chloride hexahydrate, and stirring at a constant speed to obtain a magnesium chloride solution; slowly adding the magnesium sulfate heptahydrate into the magnesium chloride solution, and stirring at a constant speed; adding the light calcined magnesia into the reaction kettle, and stirring at a constant speed; slowing dripping the silicone acrylic emulsion into the reaction kettle, adding the dispersant after dripping is finished, stirring and cooling to obtain the adhesive.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to a silicon-acrylic emulsion-modified magnesium-based inorganic adhesive used for producing environmentally friendly, moisture-resistant, flame-retardant, and high-strength crop straw wood-based panels and a preparation method thereof. Background technique [0002] Magnesium-based inorganic adhesive is a new type of adhesive in the wood adhesive industry. It is environmentally friendly, low in price, high and low temperature resistance, high wear resistance, good air stability and weather resistance, and can also be well combined with Straw scraps are bonded to produce fireproof straw boards with good processing properties, which have been widely used in the fields of construction, decoration, packaging and other materials. However, the condensation speed of the magnesium-based inorganic adhesive is fast, so that the reaction heat of the magnesium-based inorganic adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J1/00C09J11/08
CPCC09J1/00C09J11/08
Inventor 肖俊华左迎峰吴义强刘文杰赵星
Owner CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com