Ultra-weather resistant building outer wall paint film wall cloth and manufacturing process thereof

An ultra-weather-resistant technology for building exterior walls, applied in construction, building structure, covering/lining, etc., can solve problems such as reducing the life of paint film, inconsistent effect, discounting decorative effect, etc., to enhance anti-oxidation performance and facilitate maintenance. Updated, decorative effect

Active Publication Date: 2016-06-29
刘新宇
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rock flake paint (also known as imitation granite paint) is a pure water-based sand wall-like architectural coating. The effect of spraying is full of granite style. Excellent product, but there are still many defects in the process of use, and it cannot fully meet the high quality requirements of consumers
[0003] First of all, whether it is real stone paint or rock flake paint, a large number of tiny air bubbles are produced in the paint film during spraying. After drying, the paint film is loose and not dense enough. The water absorption rate of the paint film is relatively high, and the bonding strength is correspondingly reduced. , rainwater will penetrate into the paint film, causing the paint film to turn white when it meets water and have poor water resistance; moreover, the paint film with weak compactness and loose appearance is prone to decompose and decompose colored substances when it is irradiated by ultraviolet rays from the sun, eventually causing yellowing Discoloration etc.
In order to achieve a realistic effect comparable to natural granite, rock flake paint is sprayed with PVC color flakes. PVC color flakes are easy to fade, oxidize, and have poor weather resistance. When spraying, sand will fall off and splash around, polluting the environment. In severe cases, it can waste three If the thickness is uneven during the construction process, or the paint film is too thin, it will cause blooming phenomenon, which will bring difficulty to the construction and greatly reduce the life of the paint film.
Moreover, with artificial spraying, due to the difference in the technical level of the spraying construction personnel, the spraying effect is inconsistent, there are color differences, poor texture, inconsistent flatness, and inconsistent thickness, which greatly reduces the decorative effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] According to 30 parts by weight of natural mineral pigments, the ratio of 100 parts by weight of acrylate copolymer emulsion is prepared into color paste A, and the color paste A is evenly coated on both sides of the glass fiber non-woven fabric with a grammage of 30g / m2, and the color paste A and After the glass fiber is integrated, it enters the vacuum machine to discharge the air in the paint film. The vacuum degree of the vacuum machine is 0.66kPa. The paint film is taken out and dried naturally to form an elastic paint film. The elastic paint film is crushed and processed into an average particle size of 2 ~6mm elastic film color film.

[0029] The acrylate copolymer emulsion and lithopone are evenly blended into a thick build emulsion according to the ratio of 1:1.5 in parts by weight, and the thick build emulsion is evenly painted on a glass fiber polyester with a grammage of 80g / m2 On the mixed surface felt, after the thick-build emulsion and the fibers of the g...

Embodiment 2

[0032] According to the ratio of 6 parts by weight of natural mineral pigments and 100 parts by weight of transparent fluorocarbon paint, color paste B is prepared, and color paste B is evenly coated on both sides of the glass fiber non-woven fabric with a grammage of 30g / m2. After the fibers are integrated, enter the vacuum machine to discharge the air in the paint film, take it out and dry it naturally to form a hard paint film, and crush the hard paint film into hard paint film color chips with an average particle size of 2~6mm.

[0033] The acrylate copolymer emulsion and lithopone are evenly blended into a thick build emulsion according to the ratio of 1:1.8 in parts by weight, and the thick build emulsion is evenly painted on a glass fiber polyester with a grammage of 100g / m2 On the mixed surface mat, after the thick-build emulsion and the fibers of the glass fiber polyester surface felt are completely integrated, enter the vacuum machine to discharge the air in the subst...

Embodiment 3

[0036] According to the ratio of 30 parts by weight of natural mineral pigments and 100 parts by weight of acrylate copolymer emulsion, color paste A is prepared, and the color paste A is evenly coated on both sides of the glass fiber non-woven fabric with a grammage of 30g / m2. After the fibers are integrated, they enter the vacuum machine to discharge the air in the paint film. The vacuum degree of the vacuum machine is 0.66kPa. The paint film is taken out and dried naturally to form an elastic paint film. The elastic paint film is crushed and processed into an average particle size of 2~ 6mm elastic paint film color film.

[0037] According to the ratio of 20 parts by weight of natural mineral pigments and 100 parts by weight of transparent fluorocarbon paint, color paste B is prepared, and the color paste B is evenly coated on both sides of the glass fiber non-woven fabric with a grammage of 30g / m2. After the fibers are integrated, enter the vacuum machine to discharge the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultra-weather resistant building outer wall paint film wall cloth and a manufacturing process thereof. The paint film wall cloth provided by the invention comprises a paint film colored sheet layer and a base material layer which are integrally formed, wherein the paint film colored sheet layer is formed by coating the two surfaces of a glass fiber cloth with color paste, drying the glass fiber cloth, and grinding the glass fiber cloth; the color paste is prepared by mixing a natural mineral pigment, and an elastic emulsion type glue solution or fluorocarbon coating according to certain parts by weight; the base material layer is formed by coating the two surfaces of a fiberglass-polyester mixed surface felt with thick plasma type emulsion, and drying the fiberglass-polyester mixed surface felt. According to the ultra-weather resistant building outer wall paint film wall cloth provided by the invention, the defects that difficulty in paint coating, uneven thickness after coating, easiness in loosening, sand falling and the like of the traditional granite paint are overcome; a paint film colored sheet and a base material are integrally formed through hot pressing, the thickness of the paint film colored sheet layer on the base material layer is strictly controlled in a manufacturing process, a vacuum step is strictly controlled, and an UV (ultraviolet) machine is used for glazing to seal and cure, so that the decorating wall cloth provided by the invention is high in uniformity, flatness, anti-water ability, antioxidant ability and ultraviolet resistance. The blank of outer wall decorating wall cloth in the market is filled.

Description

technical field [0001] The invention belongs to the field of decorative materials, and in particular relates to a super-weather-resistant building exterior wall paint film wall covering and a manufacturing process thereof. Background technique [0002] Over the years, the building exterior wall decoration industry has developed rapidly, with a wide variety of products ranging from natural stone, ceramics, synthetic panels, and coatings. Coatings occupy a considerable share in building exterior wall decoration materials. Coatings have the advantages of cheap price, easy construction, and short construction period; at the same time, coatings in building exterior wall decoration materials have gradually shown poor weather resistance and poor decorative effects. Good and other obvious defects. In order to overcome this defect, a new generation of products represented by real stone paint has emerged in recent years. Rock flake paint (also known as imitation granite paint) is a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F13/00
CPCE04F13/002
Inventor 刘新宇
Owner 刘新宇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products