Multilayer packaging glue film for solar cell and preparing technology thereof
A technology for solar cells and encapsulation films, applied in lamination devices, laminations, circuits, etc., to achieve the effect of improving anti-PID performance, improving ion barrier properties, and improving anti-PID performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example one:
[0026] A multi-layer encapsulating film for solar cells, composed of three layers of film: EVA-EAA layer, POE layer and EVA-sodium polyacrylate resin mixed layer. The composition of each film is as follows:
[0027] EVA-EAA layer: 40 parts of EVA (where the content of VA is 25%, melt index is 40g / 10min), 60 parts of EAA (wherein, the content of AA is 19%, melt index is 10g / 10min), 0.1 part of tert-butyl Peroxy-2-ethylhexyl ester, 0.1 part triallyl cyanurate, 0.01 part 2-hydroxy-4-n-octyloxybenzophenone, 0.01 part sebacic acid bis-2,2,6 ,6-Tetramethylpiperidinol ester, 0.01 part of β-(3,5-di-tert-butyl-4-hydroxyphenyl) n-octadecyl propionate, 0.01 part of γ-aminopropyl triethoxy Base silane
[0028] POE layer: 100 parts POE (melt index 20g / 10min), 1.5 parts tert-butylperoxy-2-ethylhexyl carbonate, 1.5 parts triallyl isocyanurate, 0.3 parts 2-ethylhexyl- 4-methoxycinnamate, 0.3 part of succinic acid and (4-hydroxy-2,2,6,6-tetramethyl-1-piperidinol) polymer, 0.1...
Example Embodiment
[0036] Embodiment two:
[0037] A multi-layer encapsulating film for solar cells, composed of three layers of film: EVA-EAA layer, POE layer and EVA-sodium polyacrylate resin mixed layer. The composition of each layer of film includes: 100 parts of main resin , 1.5 parts of tert-butylperoxy-2-ethylhexyl carbonate, 1.5 parts of triallyl isocyanurate, 0.3 parts of 2-hydroxy-4-n-octoxy benzophenone, 0.3 parts of double ( 1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl) sebacate, 0.1β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid Stearyl alcohol ester, 0.1 part of γ-methacryloxypropyl trimethoxysilane, the main resin of each layer of adhesive film is as follows:
[0038] EVA-EAA layer: 20 parts of EVA (wherein, the content of VA is 40%, the melt index is 20g / 10min), 80 parts of EAA (where the content of AA is 30%, the melt index is 40g / 10min);
[0039] POE layer: 00 parts of POE (melt index 40g / 10min);
[0040] EVA-sodium polyacrylate resin mixed layer: 60 parts of EVA (wherein, the co...
Example Embodiment
[0047] Embodiment three:
[0048] A multi-layer encapsulating film for solar cells, composed of three layers of film: EVA-EAA layer, POE layer and EVA-sodium polyacrylate resin mixed layer. The composition of each film is as follows:
[0049] EVA-EAA layer: 30 parts of EVA (including 30% VA content and 35g / 10min melt index), 70 parts EAA (including 25% AA content and 30g / 10min melt index), 2 parts 2,5 -Dimethyl-2,5-bis(tert-butylperoxy)hexane, 2 parts triallyl cyanurate, 0.15 parts 2-ethylhexyl-4-methoxycinnamate, 0.15 Part of the polymer of dimethyl succinate and 4-hydroxy-2,2,6,6-tetramethyl-1-piperidine ethanol, 0.05 part of pentaerythritol bisphosphite di(stearyl alcohol) ester, 1 part 3-aminopropyltrimethoxysilane;
[0050] POE layer: 100 parts POE (melt index 40g / 10min), 3 parts tert-butylperoxy-2-ethylhexyl carbonate, 3 parts triallyl isocyanurate, 0.5 parts 2-hydroxybenzotriazole , 0.5 parts of bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl) sebacate, 0.3 parts of 2,6-di...
PUM
Property | Measurement | Unit |
---|---|---|
Melt finger | aaaaa | aaaaa |
Melt finger | aaaaa | aaaaa |
Melt finger | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap