Paper cup cover and manufacturing technology thereof

A manufacturing process and technology for paper cups, which are applied in the field of paper cup lids and their production processes, can solve the problems of poor bonding ability and low strength performance of paper cup lids, and achieve the effect of excellent strength performance.

Active Publication Date: 2016-07-20
香河合益包装机械有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the strength performance of the paper cup lid produced by the production process described in the reference document is not high, and needs to be strengthened
This is because the paper cup lid is made of bagasse pulp, reed pulp, and wheat straw pulp bonded by coagulant polysaccharide agent, and the binding ability between bagasse pulp, reed pulp, and wheat straw pulp is not strong.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper cup cover and manufacturing technology thereof
  • Paper cup cover and manufacturing technology thereof
  • Paper cup cover and manufacturing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Dissolve 1Kg of sodium alginate in 3Kg of water to obtain an aqueous solution of sodium alginate; process 90Kg of bagasse pulp through beating and refining; add the obtained aqueous solution of sodium alginate to the obtained slurry under stirring conditions, Mix evenly; add 0.5Kg titanium dioxide, 5Kg diatomaceous earth, and 0.5Kg tea polyphenols in turn under the condition of stirring, and mix evenly; inject it into the mold of the cup cover, under the mold pressing state, at a temperature of 185-200°C Under the condition of heating and drying for 2 to 3 minutes; after that, use a trimmer to trim the edge to obtain the sample 1a.

[0034] Dissolve 1Kg of sodium alginate in 3Kg of water to obtain an aqueous solution of sodium alginate; process 90Kg of bagasse pulp through beating and refining; add the obtained aqueous solution of sodium alginate to the obtained slurry under stirring conditions, Mix evenly; add 0.5Kg titanium dioxide, 5Kg diatomaceous earth, and 0.5Kg t...

Embodiment 2

[0035] Embodiment 2: Carry out according to the method of embodiment 1, obtain sample 2a and sample 2b respectively. The difference is the feeding of each component: bagasse slurry 95Kg, tea polyphenol 0.5Kg, sodium alginate 0.5Kg, titanium dioxide 0.5Kg, diatomite 3Kg, water 0.5Kg.

Embodiment 3

[0036] Embodiment 3: Carry out according to the method of embodiment 1, obtain sample 3a and sample 3b respectively. The difference is the feeding of each component: bagasse pulp 92Kg, tea polyphenol 1Kg, sodium alginate 0.7Kg, titanium dioxide 0.8Kg, diatomite 3Kg, water 2.5Kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a paper cup cover and a manufacturing technology thereof. The paper cup cover comprises, by mass, 90-95 parts of bagasse pulp, 0.5-1 part of tea polyphenol, 0.5-1 part of sodium alginate, 0.5-1 part of titanium dioxide, 3-8 parts of diatomite and 0-1 part of water. A manufacturing technology of the paper cup cover includes the steps of (1), dissolving the sodium alginate into water so as to obtain a sodium alginate water solution; (2), pulping and defibrinating the bagasse pulp; (3), under the condition of stirring, adding the sodium alginate water solution obtained in the step (1) into slurry obtained in the step (2) with uniformly mixing; (4), under the condition of stirring, sequentially adding the titanium dioxide, the diatomite and the tea polyphenol with uniformly mixing; (5), injecting a mixture into a mould of the cup cover and heating to dry for 2-3 minutes at 185-200 DEG C in the pressing and closing state of the mould; (6), trimming edges by an edge trimmer. The paper cup cover is energy saving, environment friendly and excellent in strength performance.

Description

technical field [0001] The invention relates to the technical field of manufacturing technology of plant fiber molded products, more specifically, it relates to a paper cup lid made of plant fiber and its production process. Background technique [0002] my country's sugarcane production is second only to Brazil and India, and is the third largest sugarcane plantation in the world. Sugarcane occupies an important position in my country's agricultural economy, and its output and output value are second only to grain, oilseeds and cotton, ranking fourth. Due to the strong adaptability of sugarcane, the planting area of ​​sugarcane in my country has increased year by year in recent years. [0003] Sugar cane is mainly used to make sugar, and my country is one of the main sugar producing countries in the world. As the main by-product of the sugar industry, bagasse is used in papermaking, animal feed, etc., and the added value of the product is low. The patent document (refere...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H11/12D21H17/68D21H17/67D21H17/06D21H17/14D21J3/00
CPCD21H11/12D21H17/06D21H17/14D21H17/675D21H17/68D21H17/74D21J3/00
Inventor 鲍新春
Owner 香河合益包装机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap