A trolley case and carbon fiber technology, applied in the field of carbon fiber reinforced nylon composite trolley case casters, can solve the problems of low surface finish, high cost, poor processability, etc. Effect

Inactive Publication Date: 2016-08-03
XIANGXING FUJIAN BAG ANDLUGGAGE GRP CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Relevant research and tests have also been carried out in China. A large number of test results show that: carbon fiber reinforced nylon can increase the tensile strength, flexural strength, flexural modulus, surface hardness, wear resistance, and heat resistance of nylon composite materials. Sassafras coefficient is small, light weight and other advantages, but carbon fiber reinforced materials also have their disadvantages, such as: high cost, poor processability, poor surface finish, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber reinforced nylon composite draw-bar box castor
  • Carbon fiber reinforced nylon composite draw-bar box castor
  • Carbon fiber reinforced nylon composite draw-bar box castor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A carbon fiber reinforced nylon composite trolley case caster, comprising the following components by weight:

[0042]

[0043] The EPDM-g-MAH has a high grafting rate of 1.6% and a grafting efficiency of 80%.

[0044] Calcium stearate, tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, stearic acid and dried nylon 66, EPDM-g-MAH, surface activation The hollow glass microspheres are mixed in a high-speed mixer to obtain a mixture; the mixture and short active carbon fibers are granulated and then injection molded to obtain trolley case casters.

Embodiment 2

[0046] A carbon fiber reinforced nylon composite trolley case caster, comprising the following components by weight:

[0047]

[0048] The EPDM-g-MAH has a high grafting rate of 1.6% and a grafting efficiency of 80%.

[0049] Magnesium stearate, tris(2,4-di-tert-butylphenyl) phosphite, polyethylene wax, dried nylon 6, EPDM-g-MAH, and surface-activated hollow glass microspheres were mixed in a high-speed mixer Mix in medium to obtain a mixture; pelletize the mixture and active short carbon fibers and then injection mold to obtain trolley case casters.

Embodiment 3

[0051] A carbon fiber reinforced nylon composite trolley case caster, comprising the following components by weight:

[0052]

[0053]The EPDM-g-MAH has a high grafting rate of 1.6% and a grafting efficiency of 80%.

[0054] Magnesium stearate, tris(2,4-di-tert-butylphenyl) phosphite, polyethylene wax, dried nylon 6, EPDM-g-MAH, and surface-activated hollow glass microspheres were mixed in a high-speed mixer and mixing in a medium to obtain a mixture; the mixture and activated carbon fibers are granulated and then injection molded to obtain trolley case casters.

[0055] The performance comparison table of the trolley case caster material of each embodiment of table 1

[0056]

[0057]

[0058] Abrasion: Test according to GB3960-1983 standard, apply 20 kg force, 45 # Steel pair grinding ring, time 2 hours.

[0059] As can be seen from Table 1, the performance of each inspection item of the trolley case caster material of each embodiment of the present invention is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
grafting efficiencyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a carbon fiber reinforced nylon composite draw-bar box castor .The castor is prepared from nylon, active carbon fibers, EPDM-g-MAH, surface-activated hollow glass micro-beads, a heat stabilizer, an antioxidant and a lubricating agent; the heat stabilizer, the antioxidant, the lubricating agent and the dried nylon, EPDM-g-MAH and surface-activated hollow glass micro-beads are mixed in a high-speed mixer, and a mixture is obtained; the mixture and the active carbon fibers are subjected to injection molding, and the draw-bar box castor is obtained .The carbon fiber reinforced nylon composite draw-bar box castor has the advantages of being high in performance, moderate in cost, easy to form and machine and the like and has a wide industrial application prospect.

Description

technical field [0001] The invention relates to a nylon composite trolley case caster, in particular to a carbon fiber reinforced nylon composite trolley case caster. Background technique [0002] Trolley box caster system materials (including brackets and casters) are produced with reinforced nylon at home and abroad. Nylon is mainly modified by fiber, which can significantly improve the acid and alkali resistance and physical and mechanical properties of nylon, making it applicable to a wider range, so fiber modified nylon is of great significance. Reinforced nylon includes glass fiber reinforced / carbon fiber reinforced / basalt fiber reinforced and aramid fiber reinforced. Among them, glass fiber and carbon fiber are the main types. Glass fiber reinforced nylon is a composite material made of polymer as a matrix and glass fiber as a reinforcing material. It combines the properties of polymer and glass fiber and has high strength and corrosion resistance. , heat insulation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L77/02C08L51/04C08K13/06C08K9/06C08K9/02C08K7/28C08K7/06C08K5/098
CPCC08L77/06C08L77/02C08L2205/03C08L51/04C08K13/06C08K9/06C08K9/02C08K7/28C08K7/06C08K5/098C08L51/003
Inventor 薛行远彭超谢孝波陈琼涂思敏
Owner XIANGXING FUJIAN BAG ANDLUGGAGE GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap