All-component material separation and collection device and method for waste lithium batteries

A waste lithium battery and collection device technology, which is applied in the field of storage batteries, can solve the problems of complex recycling process, the introduction of a large amount of chemical reagents, and the impossibility of large-scale industrial operation, so as to achieve the effect of high recycling efficiency and easy industrialization

Active Publication Date: 2016-08-03
STATE GRID HENAN ELECTRIC POWER ELECTRIC POWER SCI RES INST +2
View PDF9 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, some invention patents disclose the recycling and treatment methods of lithium batteries, but there are the following deficiencies: (1) focus on the recycling of precious metal components such as cobalt and nickel, or only recycle electrode materials, and the recovery and utilization of other components of waste lithium batteries There are few reports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • All-component material separation and collection device and method for waste lithium batteries
  • All-component material separation and collection device and method for waste lithium batteries

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Such as figure 1 As shown, a material separation and collection device for all components of waste lithium batteries, which includes a roller crusher 2 and a knife crusher 3 connected by an electric conveyor belt 1, and a plastic crusher connected to the knife crusher 3 in sequence through a pipeline A material separation and collection device, a hammer mill 6 and a battery material separation device; an electrolyte adsorption and collection device 11 is provided above the roller crusher 2 and the knife crusher 3;

[0041] The plastic material separation and collection device includes a dense first vibrating screen 4, the first vibrating screen 4 is a sealed structure, the top of the first vibrating screen 4 is connected with a plastic material storage bin 41 through a pipeline, and the plastic material storage bin 41 is connected with a A dust collection device 5 is provided above the vacuum pump 14 and the plastic material storage bin 41;

[0042] The battery materia...

Embodiment 2

[0055] A method and device for recycling waste lithium batteries, comprising the following steps:

[0056] Take 300kg of waste energy storage lithium batteries, the battery type is lithium iron phosphate battery, the specification is 180Ah square steel shell battery, and the external dimensions are 178mm×278mm×70mm. Carry out recycling according to the following method steps.

[0057]Other contents and operations are the same as in Example 1, except that in step (1), the rolling force is between 3000 Newton and 5000 Newton, and the primary debris material with a particle size of 30-40 mm is obtained after rolling and crushing. In step (2), the knife crusher 3 rotates at a speed of 2000 rpm, and the primary debris material contacts the cutter head of the high-speed rotating knife crusher 3 at an angle of 70 degrees, and the particle size of the obtained secondary debris material is The diameter size is 2-5mm. During the crushing, cutting and crushing process, the electrolyte ...

Embodiment 3

[0059] A method and device for recycling waste lithium batteries, comprising the following steps:

[0060] Take 200kg of waste laptop lithium batteries, the battery type is lithium cobalt oxide battery, the specification is 3000mAh square cylindrical battery, the external dimensions are 18mm in diameter and 65mm in height. Carry out recycling according to the following method steps.

[0061] Other contents and operations are the same as in Example 1, except that in step (1), the rolling force is between 3000 Newton and 4000 Newton, and the primary debris material with a particle size of 25-40 mm is obtained after rolling and crushing. In step (2), the knife crusher 3 rotates at a speed of 1800 rpm, and the primary debris material contacts the cutter head of the high-speed rotating knife crusher 3 at an angle of 45 degrees, and the particle size of the obtained secondary debris material is The diameter size is 15-20mm. During the crushing, cutting and crushing process, the el...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an all-component material separation and collection device and method for waste lithium batteries. The simple dry methods of mechanical smashing, vacuum separation, vibratory screening, specific gravity separation, airflow separation and the like are mainly utilized, and separation and collection of electrode materials, current collector metal, plastic membranes and battery shells in waste lithium batteries are achieved; no chemical reagent is introduced in the separation and collection process, the whole process is automatic, electrolytes, dust and the like are collected and treated at the same time, and the all-component material separation and collection device and method for waste lithium batteries have the advantages that recovery efficiency is high, the environment-friendly and low-carbon effect is achieved, environment protection and energy saving are achieved, and industrialization is easy.

Description

technical field [0001] The invention belongs to the technical field of storage batteries, and in particular relates to a method and a separation and collection device for separating and collecting materials of all components of waste lithium batteries. Background technique [0002] Lithium-ion batteries have been rapidly developed and widely used in the fields of grid energy storage, electric vehicles, computers, communications, and consumer electronics products, and the scale and quantity have continued to expand. According to the service life of batteries, by 2024, the cumulative amount of waste lithium batteries scrapped will be It will reach more than 1 million tons and will show an explosive cumulative growth trend. The cumulative effect of its health, environment, and safety hazards will be multiplied and cannot be ignored. If it cannot be recycled effectively, it will also cause a waste of resources. Carrying out the recycling and utilization of waste batteries can r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M10/54
CPCY02W30/84H01M10/54
Inventor 赵光金唐国鹏吴文龙
Owner STATE GRID HENAN ELECTRIC POWER ELECTRIC POWER SCI RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap