Water-borne acrylic resin anticorrosive coating and preparation method thereof

A technology of water-based acrylic and anti-corrosion coatings, applied in the field of coatings, can solve problems such as the decline of paint film performance, and achieve the effect of good coating film performance and long storage time

Inactive Publication Date: 2016-08-24
宋介珍
View PDF6 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, after long-term storage of the above-mentioned water-based acrylic pain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Prepare the following raw materials: 30 parts of modified acrylic emulsion, 16 parts of water-based epoxy resin, 10 parts of silica sol, 4 parts of aluminum tripolyphosphate, 5 parts of anti-corrosion pigment zinc phosphate, 20 parts of pigment iron oxide red, 0.5 parts of additives and 10 parts of water. The auxiliary agent is a wetting agent, a dispersant, a film-forming auxiliary agent, a pH regulator, a defoamer, and a rheological auxiliary agent mixed in equal proportions.

[0026] Wherein, the preparation method of the modified acrylic acid emulsion is:

[0027] S1, in parts by weight, mix 50 parts of hydroxyl silicone oil, 10 parts of silane coupling agent KH-570, 3 parts of KOH, and 6 parts of ethyl acetate, and heat it up to 90°C under a nitrogen atmosphere and keep the reaction for 3 hours to obtain Modified polysiloxane prepolymer; the hydroxyl content in the hydroxy silicone oil is 8wt%;

[0028] S2, in parts by weight, take 12 parts of butyl acrylate, 5 p...

Embodiment 2

[0031] Prepare the following raw materials:

[0032] 55 parts of modified acrylic emulsion, 25 parts of water-based epoxy resin, 16 parts of silica sol, 6 parts of aluminum tripolyphosphate, 15 parts of anti-corrosion pigment zinc phosphate, 40 parts of pigment and filler iron oxide red, 5 parts of additives and 15 parts of water. The auxiliary agent is a wetting agent, a dispersant, a film-forming auxiliary agent, a pH regulator, a defoamer, and a rheological auxiliary agent mixed in equal proportions.

[0033] Wherein, the preparation method of the modified acrylic acid emulsion is:

[0034] S1, in parts by weight, mix 60 parts of hydroxyl silicone oil, 15 parts of silane coupling agent KH-570, 5 parts of KOH, and 10 parts of ethyl acetate, and heat it up to 90°C under a nitrogen atmosphere for 3 hours to obtain Modified polysiloxane prepolymer; the hydroxyl content in the hydroxy silicone oil is 8wt%;

[0035] S2, in parts by weight, take 15 parts of butyl acrylate, 10 p...

Embodiment 3

[0038] Prepare the following raw materials:

[0039] 40 parts of modified acrylic emulsion, 20 parts of water-based epoxy resin, 12 parts of silica sol, 5 parts of aluminum tripolyphosphate, 12 parts of anti-corrosion pigment zinc phosphate, 30 parts of pigment and filler iron oxide red, 3 parts of additives and 12 parts of water. The auxiliary agent is a wetting agent, a dispersant, a film-forming auxiliary agent, a pH regulator, a defoamer, and a rheological auxiliary agent mixed in equal proportions.

[0040] Wherein, the preparation method of the modified acrylic acid emulsion is:

[0041] S1, in parts by weight, mix 55 parts of hydroxyl silicone oil, 12 parts of silane coupling agent KH-570, 4 parts of KOH, and 8 parts of ethyl acetate, and heat it up to 90°C under a nitrogen atmosphere and keep the reaction for 3 hours to obtain Modified polysiloxane prepolymer; the hydroxyl content in the hydroxy silicone oil is 8wt%;

[0042] S2, in parts by weight, take 13 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water-borne acrylic resin anticorrosive coating and a preparation method thereof, and belongs to the technical field of coatings. The water-borne acrylic resin anticorrosive coating is prepared from, by weigh , 30-55 parts of modified acrylic emulsion, 16-25 parts of water-borne epoxy resin, 10-16 parts of silica sol, 4-6 parts of aluminum triphosphate, 5-15 parts of anticorrosive pigment, 20-40 parts of pigment filler, 0.5-5 parts of additive and 10-15 parts of water. The water-borne acrylic coating has the advantage of being long in storage time, and still has the good coating property after being stored for 12 months or longer.

Description

technical field [0001] The invention relates to a water-based acrylic resin anticorrosion coating and a preparation method thereof, belonging to the technical field of coatings. Background technique [0002] The research on acrylic monomers and resins began in 1805, but due to limited conditions, it was not produced industrially by Rohm & Haas until 1927, and the real application in coatings was after 1953. Acrylic paints are developed today. It is already a type of synthetic resin coating with the most types, the most comprehensive performance, and the strongest versatility. Compared with other polymer resins, acrylic resin coatings have many outstanding advantages, such as its excellent light resistance, weather resistance, and outdoor exposure durability. Strong, not easy to decompose and turn yellow under ultraviolet light, can maintain the original luster and color for a long time, good heat resistance; corrosion resistance, good resistance to acid, alkali, salt, gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D187/00C09D163/00C09D5/08C09D7/12C08G81/02
CPCC09D187/005C08G81/024C09D5/084C09D7/61C08L63/00C08K13/02C08K3/36C08K2003/327C08K2003/328C08K2003/2272
Inventor 宋介珍
Owner 宋介珍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap