Thermochromic release film

A thermochromic, release film technology, applied in the direction of heat-sensitive coatings, coatings, etc., can solve the problems of accelerated aging, affecting the service life of products, etc., to achieve the effect of prolonging the service life and avoiding accelerated aging

Inactive Publication Date: 2016-08-31
JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Since the surface of the release film needs to be covered with an adhesive, the main material of the adhesive is a high molecular polymer, which is very sensitive to the space environment. The adhesive is in the external environment such as ultraviolet rays, temperature, oxygen, water and pollutants Under the influence, it will accelerate aging, thus affecting the service life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermochromic release film
  • Thermochromic release film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A thermochromic release film, comprising a base film layer, the base film layer is provided with a release layer, the release layer is coated with a release agent, and the release agent contains the following parts by mass Each component of the number: thermochromic compound: 10 parts; vinyl silicone resin: 20 parts; methacrylate: 2 parts; titanium dioxide: 4 parts; antioxidant: 0.8 parts; coupling agent: 2 parts; Foaming agent: 0.5 parts; adhesion promoter: 0.1 parts; solvent: 20 parts.

[0020] Wherein, the material of the base film layer is PE, the thermochromic compound is an organic thermochromic compound triarylmethane compound, the antioxidant is di-tert-butylphenol; the coupling agent is a silane coupling agent; The defoamer is ethylene glycol distearate; the adhesion promoter is a chlorinated resin.

Embodiment 2

[0022] A thermochromic release film, comprising a base film layer, the base film layer is provided with a release layer, the release layer is coated with a release agent, and the release agent contains the following parts by mass Each component of the number: thermochromic compound: 14 parts; vinyl silicone resin: 18 parts; methacrylate: 1 part; titanium dioxide: 3 parts; antioxidant: 1.8 parts; coupling agent: 5.5 parts; Foaming agent: 0.2 parts; adhesion promoter: 0.6 parts; solvent: 25 parts.

[0023] Wherein, the material of the base film layer is PET, the thermochromic compound is an organic thermochromic compound spiropyran compound, the antioxidant is butyl hydroxyanisole; the coupling agent is a silane coupling agent ; The defoamer is polyoxypropylene polyoxyethylene glyceryl ether; the adhesion promoter is chlorinated resin.

Embodiment 3

[0025] A thermochromic release film, comprising a base film layer, the base film layer is provided with a release layer, the release layer is coated with a release agent, and the release agent contains the following weight percent The content of each component: thermochromic compound: 20 parts; vinyl silicone resin: 25 parts; methacrylate: 3.5 parts; titanium dioxide: 5.5 parts; antioxidant: 1.7 parts; coupling agent: 4.2 parts; Defoamer: 0.9 parts; adhesion promoter: 1.1 parts; solvent: 29 parts.

[0026] Wherein, the material of the base film layer is PMMA, the thermochromic compound is an organic thermochromic compound triarylmethane compound, the antioxidant is butyl hydroxyanisole; the coupling agent is a silane coupling agent; The defoamer is polyoxypropylene polyoxyethylene glyceryl ether; the adhesion promoter is organosilane compound.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a thermochromic release film. The thermochromic release film is characterized by comprising a base film layer; a release layer is arranged on the base film layer and is formed by coating a release agent; the release agent is prepared from the following components in parts by mass: 10-25 parts of a thermochromic compound, 18-30 parts of vinyl organic silicon resin, 1-7 parts of methacrylate, 3-9 parts of titanium dioxide, 0.1-2.5 parts of an antioxidant, 2-7.5 parts of a coupling agent, 0.2-1.8 parts of a defoaming agent, 0.1-1.5 parts of an adhesion promoter and 20-40 parts of a solvent; the thermochromic release film does not produce adhesion when being separated from an adhesion belt or adhesive tape which is in contact with the release film; furthermore, the thermochromic release film contains the thermochromic compound, so that the color of the release film can visually display when the release film is positioned in an environment with overhigh temperature; therefore, the thermochromic release film has a warning function, the accelerated aging of an adhesive is avoided in the external environment such as high temperature, and the service life of a product is prolonged.

Description

technical field [0001] The invention relates to a release film, in particular to a thermochromic release film. Background technique [0002] Release film, also known as anti-adhesive film, is based on polyethylene terephthalate plastic (PET for short), biaxially oriented polypropylene film plastic (BOPP for short), polyethylene plastic (PE for short), and carbonate plastic (PET for short). PC), polystyrene plastic (referred to as PS), polypropylene plastic (abbreviated as CPP) is a material with low surface energy on the surface. When the adjacent adhesive is peeled from the release surface, the release material can be easily peeled off or removed without damaging the physical properties of the adhesive. The release film is characterized by smooth surface, high cleanliness, stable size in subsequent processing, adjustable transparency and color, and a wide range of options for film thickness and substrate types. Utilizing these characteristics of the release film can devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/07C09D5/26C09D7/12
CPCC09D183/04C08L2205/03C09D5/26C09D7/61C09D7/63C09D7/65C08L101/04C08K13/02C08K2003/2241C08L71/02C08L67/00
Inventor 於险峰
Owner JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap