Radiation curable pressure sensitive adhesive sheet

A pressure-sensitive adhesive and radiation curing technology, applied in the direction of film/sheet adhesives, adhesives, non-polymer organic compound adhesives, etc., can solve problems such as poor stress relief and non-satisfaction, Achieve the effect of good hardness and good fluidity

Active Publication Date: 2016-08-31
3M INNOVATIVE PROPERTIES CO
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If a pressure-sensitive adhesive with poor stress relief is used, even a material thickness ten or more times the height of the three-dimensional surface feature may not be applied with the required quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Radiation curable pressure sensitive adhesive sheet
  • Radiation curable pressure sensitive adhesive sheet
  • Radiation curable pressure sensitive adhesive sheet

Examples

Experimental program
Comparison scheme
Effect test

example

[0108] Hereinafter, the present invention is described in further detail using examples, but the present invention is not limited by these examples.

[0109] Monomer and Initiator Abbreviations

[0110] 2-EHA: 2-ethylhexyl acrylate

[0111] ISTA: Isostearyl acrylate (available from Osaka Organic Chemical Industry Ltd.)

[0112] AA: Acrylic

[0113] AEBP: 4-Acryloyloxyethoxybenzophenone

[0114] DCP-A: Tricyclodecane dimethanol diacrylate

[0115] DCP-M: Tricyclodecane dimethanol dimethacrylate

[0116]SR-399: dipentylerythritol pentaacrylate (available from Sartomer)

[0117] V-65: thermal initiator (2,2'-oxazolbis(2,4-dimethylvaleronitrile)) (available from Wako Pure Chemical Industries, Ltd.)

[0118] MOI: 2-isocyanatoethyl methacrylate (available from Showa Denko)

[0119] TPO: 2,4,6-trimethylbenzoyldiphenylphosphine oxide

[0120] EtOAc: ethyl acetate

[0121] MEK: methyl ethyl ketone

[0122] Preparation process

preparation example 1

[0124] A pressure-sensitive adhesive sheet (PSA sheet 1) was prepared as follows. Acrylic copolymers were synthesized comprising monomers of acrylates with UV crosslinkable sites as radiation reactive sites. 4-Acryloyloxyethoxybenzophenone was used as acrylate with UV crosslinkable sites.

[0125] A mixture of 2-EHA / ISTA / AA / AEBP with a ratio of 37.5:50.0:12.5:0.95 (by mass) was prepared and then mixed with ethyl acetate / methyl ethyl ketone (EtOAc:MEK=20% by mass:80% by mass) %) mixed solvent to obtain a monomer concentration of 45% by mass. Next, V-65 was added as an initiator in an amount of 0.2% by mass relative to the mass of the monomer component, and the system was purged with nitrogen for 10 minutes. The reaction was allowed to proceed for 24 hours at 50 °C in a constant temperature bath to obtain a clear viscous solution. The weight average molecular weight of the obtained acrylic copolymer (polymer 1) was 210,000 (polystyrene equivalent, measured by gel permeation c...

preparation example 2

[0129] A transfer adhesive strip (PSA sheet 2) was prepared in the same manner as PSA sheet 1, except that the ratio of solid polymer component to DCP-A was adjusted to 90:10 by mass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a radiation curable pressure sensitive adhesive sheet capable of yielding both a pressure sensitive adhesive sheet with good initial adhesion to an adherend before irradiation and a pressure sensitive adhesive sheet with good rigidity after irradiation. A radiation curable pressure sensitive adhesive sheet includes a (meth)acrylic copolymer having a radiation reactive site and a plasticizer capable of bonding with the (meth)acrylic copolymer upon being irradiated.

Description

[0001] This application is a divisional application of a Chinese invention patent application with an application date of August 9, 2012, an application number of 201280039223.8, and an invention title of "radiation-curable pressure-sensitive adhesive sheet". technical field [0002] The present invention relates to a radiation curable pressure sensitive adhesive sheet, a laminate and a method for its preparation. Background technique [0003] Image display modules of electronic devices such as portable phone terminals, computer monitors, etc., and optical members such as touch panels generally have glass or plastic films laminated thereon as surface protection layers. Such a surface protection layer is fixed to the image display module or the touch panel by applying a frame-shaped tape or an adhesive to the outer blank area of ​​the image display portion or outside the effective operating area of ​​the touch panel. Therefore, a gap is formed between the image display portio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J4/02C09J4/06B32B7/12
CPCB32B7/12C09J4/06C09J2301/302C08F220/1808C08F220/1818C09J133/14C08L2312/06C09J7/385Y10T428/2891Y10T428/31938C08F220/06C08F220/281C09J7/29C09J133/06C08F220/18C09J133/08
Inventor 诹访敏宏木下康宏
Owner 3M INNOVATIVE PROPERTIES CO