Production method of ecotypic sintering ceramic colored permeable brick

A technology of sintered ceramics and production methods, which is applied in the production, application, and household appliances of ceramic materials, and can solve problems such as single color, restricted industrialization promotion, and complex production processes, so as to protect the ecological environment and reduce the consumption of original ecological resources. , high-strength effect

Inactive Publication Date: 2016-09-21
宜兴友邦陶瓷有限公司
View PDF8 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no coloring agent introduced into the surface layer blank, and the color of the product is relatively simple; the raw materials used in the cascade high-temperature adhesive are all dried and crushed separately, and the product is fired in a silicon carbide rod electric furnace or a gas shuttle kiln. , it seems that the production process is relatively complicated, and the degree of industrialization is also restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] An ecological sintered ceramic color permeable brick, the inner layer skeleton material and the surface layer skeleton material respectively use coarser and finer grained waste ceramic particles as the main raw materials, and add lithium porcelain stone, potassium feldspar, kaolin, Colorless and colored transparent glaze composed of raw materials such as calcite powder, dolomite, talc, glass powder and ceramic coloring material for billets. Both the inner layer skeleton material and the surface layer skeleton material need to be added with organic binder CMC and water, as follows Formula ingredients (percentage by weight on a dry basis):

[0053] Inner skeleton material: 8-16 mesh waste ceramic particles 58

[0054] 16-30 mesh waste ceramic particles 42

[0055] Colorless transparent glaze 25 (plus)

[0056] CMC 3.5 (plus)

[0057] water 6 (plus)

[0058] Surface skeleton material: 8-14 mesh waste ceramic particles 10

[0059] 14-30 mesh waste ceramic particles 90 ...

Embodiment 2

[0081] An ecological sintered ceramic color permeable brick, the inner layer skeleton material and the surface layer skeleton material respectively use coarser and finer grained waste ceramic particles as the main raw materials, and add lithium porcelain stone, potassium feldspar, kaolin, Colorless and colored transparent glaze composed of raw materials such as calcite powder, dolomite, talc, glass powder and ceramic coloring material for billets. Both the inner layer skeleton material and the surface layer skeleton material need to be added with organic binder CMC and water, as follows Formula ingredients (percentage by weight on a dry basis):

[0082] Inner skeleton material: 8-16 mesh waste ceramic particles 65

[0083] 16-30 mesh waste ceramic particles 35

[0084] Colorless transparent glaze 23 (additional)

[0085] CMC 3 (plus)

[0086] water 5 (plus)

[0087] Surface skeleton material, colorless transparent glaze and secondary cloth proportioning are all identical w...

Embodiment 3

[0090] An ecological sintered ceramic color permeable brick, the inner layer skeleton material and the surface layer skeleton material respectively use coarser and finer grained waste ceramic particles as the main raw materials, and add lithium porcelain stone, potassium feldspar, kaolin, Colorless and colored transparent glaze composed of raw materials such as calcite powder, dolomite, talc, glass powder and ceramic coloring material for billets. Both the inner layer skeleton material and the surface layer skeleton material need to be added with organic binder CMC and water, as follows Formula ingredients (percentage by weight on a dry basis):

[0091] The inner skeleton material is the same as Example 2.

[0092] Surface skeleton material: 8-14 mesh waste ceramic particles 15

[0093] 14-30 mesh waste ceramic particles 85

[0094] Colored transparent glaze 27 (additional)

[0095] CMC 4 (plus)

[0096] water 6 (plus)

[0097] Colorless transparent glaze: lithium china s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of inorganic nonmetallic material, and relates to an ecotypic sintering ceramic colored permeable brick and a production method thereof. The method is characterized by including using the waste ceramic particles as a basic skeleton material, using the coarse particle size gradation as an internal layer skeleton material, using the fine particle size gradation as a surface layer skeleton material, adding proper amount of colorless and colored clear glaze fine powder, organic binder CMC, and water, and preparing the qualified ecotypic sintering ceramic colored permeable brick by performing the technologies such as preparation of materials, mixing, aging, secondary material distribution and pressing, drying, sintering and testing. The production method disclosed by the invention is suitable for industrial production of the permeable brick, and the prepared permeable brick has high water permeability, high compressive strength, rich colors, and good practical durability, and is widely used for ground laying of the outdoor public places such as large parking lot, square and city road, and artistic landscape.

Description

technical field [0001] The invention belongs to the technical field of inorganic non-metallic materials, and specifically relates to an ecological sintered ceramic color permeable brick and a production method thereof. The permeable brick produced by the method not only has strong water permeability and high compressive strength, but also has rich colors and practical durability Well, it is widely used in the ground laying of large parking lots, squares and urban roads, art landscapes and other outdoor public places. Background technique [0002] In the rapid construction of urbanization and urbanization, products such as stone, cement and ceramic tiles have been widely used as ground laying building materials. The common feature of these materials is poor water permeability or even impermeability. The area where such building materials are "hardened" on the urban ground is increasing year by year, which intensifies the formation of the "urban heat island effect". In some a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/24C03C8/00
CPCC03C8/00C04B33/1324C04B33/24Y02P40/60
Inventor 翟建君李小庚
Owner 宜兴友邦陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com