Shedding-prevention and acid-base resistance metal flicker paint for photo frame

A metal flash coating, anti-shedding technology, applied in anti-corrosion coatings, coatings and other directions, can solve the problems of metal flash coating anti-shedding and acid and alkali resistance can not be satisfied.

Inactive Publication Date: 2016-09-21
蚌埠市禹会区贵宾装饰材料商行
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Then the anti-shedding and acid and alkali resistance of the metal flash coating in the prior art cannot meet the needs of actual use, so it is urgent to design a kind of anti-shedding and acid and alkali resistant metal flash coating to meet the actual use requirements. need

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of picture frame that the present invention proposes is used anti-shedding acid and alkali resistant metal glitter paint, and its raw material comprises by weight: 45 parts of fluorocarbon resins, 10 parts of polyacrylate emulsions, 3 parts of silicone resins, 4.5 parts of epoxy resins, 3.5 parts of modified aluminum powder, 2.5 parts of nano-silica, 4 parts of nano-titanium dioxide, 2.5 parts of ceramic powder, 4 parts of jade powder, 3.5 parts of stainless steel powder, 3.5 parts of chrysotile, 4 parts of nitrocellulose solution, butyl glycol ether 2 parts, 4 parts of hexamethoxymethylmelamine, 2.5 parts of dimethylethanolamine, 3 parts of isopropanol, 4 parts of sodium hexametaphosphate, 2.5 parts of butyl acetate, 3.5 parts of silane coupling agent KH-570, dispersant 4.5 parts of TG-755, 3 parts of leveling agent TG-700, 2.5 parts of wetting agent AP-560, 4.5 parts of defoamer TG-810, 2.5 parts of xylene, 15 parts of deionized water.

[0017] The modified alu...

Embodiment 2

[0019]A kind of picture frame that the present invention proposes is used anti-shedding acid and alkali resistant metal glitter paint, and its raw material comprises by weight: 40 parts of fluorocarbon resins, 15 parts of polyacrylate emulsions, 1 part of silicone resins, 6 parts of epoxy resins, 2 parts of modified aluminum powder, 4 parts of nano-silica, 2 parts of nano-titanium dioxide, 4 parts of ceramic powder, 2 parts of jade powder, 6 parts of stainless steel powder, 2 parts of chrysotile, 6 parts of nitrocellulose solution, butyl glycol ether 1 part, 6 parts of hexamethoxymethylmelamine, 1 part of dimethylethanolamine, 4 parts of isopropanol, 3 parts of sodium hexametaphosphate, 4 parts of butyl acetate, 2 parts of silane coupling agent KH-570, dispersant 6 parts of TG-755, 2 parts of leveling agent TG-700, 4 parts of wetting agent AP-560, 3 parts of defoamer TG-810, 4 parts of xylene, 12 parts of deionized water.

[0020] The modified aluminum powder is prepared accor...

Embodiment 3

[0022] A kind of picture frame that the present invention proposes is used anti-shedding acid and alkali resistant metallic glitter paint, and its raw material comprises by weight: 50 parts of fluorocarbon resins, 5 parts of polyacrylate emulsions, 5 parts of organosilicon resins, 3 parts of epoxy resins, 5 parts of modified aluminum powder, 1 part of nano-silica, 6 parts of nano-titanium dioxide, 1 part of ceramic powder, 6 parts of jade powder, 1 part of stainless steel powder, 5 parts of chrysotile, 2 parts of nitrocellulose solution, butyl glycol ether 3 parts, 2 parts of hexamethoxymethylmelamine, 4 parts of dimethylethanolamine, 2 parts of isopropanol, 5 parts of sodium hexametaphosphate, 1 part of butyl acetate, 5 parts of silane coupling agent KH-570, dispersant 3 parts of TG-755, 4 parts of leveling agent TG-700, 1 part of wetting agent AP-560, 6 parts of defoamer TG-810, 1 part of xylene, 18 parts of deionized water.

[0023] The modified aluminum powder is prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a shedding-prevention and acid-base resistance metal flicker paint for a photo frame. The shedding-prevention and acid-base resistance metal flicker paint is prepared from fluorocarbon resin, polyacrylate emulsion, organic silicon resin, epoxy resin, modified aluminum powder, nano-silica, nanometer titania, ceramic powder, jade powder, stainless steel powder, chrysotile, nitrocellulose liquid, ethylene glycol butyl ether, hexakis methoxymethyl melamine, dimethylethanolamine, isopropanol, sodium hexametaphosphate, butyl acetate, a silane coupling agent KH-570, a dispersing agent TG-755, a flatting agent TG-700, a wetting agent AP-560, a defoaming agent TG-810, xylene and deionized water. The metal flicker paint has excellent acid-base resistance and shedding-prevention performance.

Description

technical field [0001] The invention relates to the field of flash paints, in particular to an anti-shedding acid and alkali resistant metallic flash paint for photo frames. Background technique [0002] At present, the scaly aluminum powder in the metallic flash paint forms a multi-layer parallel arrangement in the coating film, which can effectively reflect ultraviolet rays, infrared rays and visible light, delay its aging damage to the coating film, and can also effectively prevent water, air, etc. And the penetration of ions, because of its unique decorative and anti-corrosion effects, it is more and more used in the surface coating of photo frames. [0003] Then the anti-shedding and acid and alkali resistance of the metal flash coating in the prior art can not meet the needs of actual use, so it is urgent to design a kind of anti-shedding and acid and alkali resistant metal flash coating to meet the needs of actual use. need. Contents of the invention [0004] In o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D127/12C09D133/04C09D5/10C09D7/12
CPCC09D127/12C08K2201/011C08L2205/035C09D5/10C09D7/61C09D7/63C09D7/65C08L33/04C08L83/04C08L63/00C08K13/06C08K9/10C08K2003/0806C08K5/05C08K3/36
Inventor 刘贵斌刘阳
Owner 蚌埠市禹会区贵宾装饰材料商行
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com