Preparation method and application of molybdenum oxide nanoparticles used for targeted photo-thermal and photodynamic therapy
A technology of photodynamic therapy and nanoparticles, which is applied in the field of photodynamic therapy materials and photothermal, and can solve the problems of molybdenum oxide nanoparticles without targeted modification, blindness of photothermal therapy, and failure of molybdenum oxide nanoparticles to accurately reach cancer cells. Cell location and other issues, to achieve good photodynamic effect, good near-infrared absorption, good photothermal conversion efficiency and photothermal stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] 1) Weigh 0.4g of hyaluronic acid, 0.48g of ammonium heptamolybdate, and 0.9g of glucose, add 15mL of water, and stir to dissolve completely into a transparent liquid;
[0028] 2) Add 4 drops of concentrated hydrochloric acid with a 3mL disposable dropper, heat the oil bath to 90°C, and react for 6 hours to obtain a dark blue solution;
[0029] 3) Add dehydrated ethanol, then centrifuge with a centrifuge at a centrifugal speed of 10000r / min, and centrifuge for 10min; the amount of dehydrated ethanol added is: the volume ratio of dehydrated ethanol to the blue solution is 2:1;
[0030] 4) Wash the solid obtained in step 3) several times with water, add absolute ethanol, and centrifuge to obtain a dark blue solid;
[0031] 5) Vacuum drying is used to obtain the hyaluronic acid-modified molybdenum oxide nanoparticles of the present invention.
Embodiment 2
[0033] 1) Weigh 0.4g of hyaluronic acid, 0.48g of ammonium heptamolybdate, and 0.9g of glucose, add 10mL of water, and stir to dissolve completely into a transparent liquid;
[0034] 2) Add 3 drops of concentrated hydrochloric acid with a 3 mL disposable dropper, heat the oil bath to 90°C, and react for 6 hours to obtain a dark blue solution;
[0035] 3) Add dehydrated ethanol, then centrifuge with a centrifuge at a centrifugal speed of 10000r / min, and centrifuge for 10min; the amount of dehydrated ethanol added is: the volume ratio of dehydrated ethanol to the blue solution is 2:1;
[0036] 4) Wash the solid obtained in 3) several times with water, add absolute ethanol, and centrifuge to obtain a dark blue solid;
[0037] 5) Vacuum drying is used to obtain the hyaluronic acid-modified molybdenum oxide nanoparticles of the present invention.
Embodiment 3
[0039] 1) Weigh 0.8g of hyaluronic acid, 0.96g of ammonium heptamolybdate, and 1.8g of glucose, add 15mL of water, and stir to dissolve completely into a transparent liquid;
[0040] 2) Add 4 drops of concentrated hydrochloric acid with a 3mL disposable dropper, heat the oil bath to 90°C, and react for 6 hours to obtain a dark blue solution;
[0041] 3) Add dehydrated ethanol, then centrifuge with a centrifuge at a centrifugal speed of 10000r / min, and centrifuge for 10min; the amount of dehydrated ethanol added is: the volume ratio of dehydrated ethanol to the blue solution is 2:1;
[0042] 4) Wash the solid obtained in 3) several times with water, add absolute ethanol, and centrifuge to obtain a dark blue solid;
[0043] 5) Vacuum drying is used to obtain the hyaluronic acid-modified molybdenum oxide nanoparticles of the present invention;
[0044] The products prepared in Examples 1, 2, and 3 can all be well dispersed in aqueous solution and can exist stably.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com