Sterilizing disinfecting slice-shaped honeycomb ceramics and preparation method thereof

A technology of honeycomb ceramics, sterilization and disinfection, applied in the field of ceramic materials, can solve the problems of increased use cost, insufficient heat resistance of ceramic carriers, waste of resources, etc., to achieve cost savings, broad application prospects and market value, and prolong service life Effect

Inactive Publication Date: 2016-12-07
BENGBU NANZI INSTR
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Zhu Jie used cordierite honeycomb ceramics as the carrier in his master's thesis "Study on the Catalytic Performance of Cordierite Honeycomb Ceramics Loaded La-Sr-Co-O on Automobile Exhaust Gas", La-Sr-Co-O perovskite composite oxidation As the active component of the catalyst, a monolithic automobile exhaust catalyst has been prepared, but the heat resistance of the prepared ceramic carrier is not high enough, and once the monolithic catalyst is damaged, it needs to be replaced as a whole, which wastes resources and increases the cost of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0020] A sterilized sheet-shaped honeycomb ceramic, characterized in that it is made of the following raw materials in parts by weight:

[0021] Silver fiber 5, cordierite 40, clay 3, ZrO 2 Flour 10, Soy Protein Fiber 5, CrO 2 Powder 5, talc powder 10, magnesium carbonate 5, glycerol 8, sodium carbonate 8, stearic acid 3, 1 mol / L HNO 3 Appropriate amount of solution, nano-alumina sol 60, 1 mol / L La(NO 3 ) 3 3, 1 mol / L Sr(NO 3 ) 2 2,1 mol / L Co(NO 3 ) 2 1. 1 mol / L citric acid 6, deionized water 200;

[0022] The solid content of the nano-alumina sol is 20%-25%.

[0023] The sterilized sheet-shaped honeycomb ceramic and its preparation method are characterized in that, comprising the following steps:

[0024] a. Preparation of flake honeycomb ceramics:

[0025] Take silver fiber, cordierite, clay, ZrO 2 Flour, soybean protein fiber, CrO 2 Powder, talcum powder, magnesium carbonate and sodium carbonate are ball milled, mixed, and pulverized to 200-500 meshes, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses sterilizing disinfecting slice-shaped honeycomb ceramics and a preparation method thereof. The sterilizing disinfecting slice-shaped honeycomb ceramics are made from the following raw materials in parts by weight: 3-5 parts of silver fibers, 40-50 parts of cordierite, 1-3 parts of clay, 5-10 parts of ZrO2 powder, 3-5 parts of soybean protein fibers, 5-10 parts of CrO2 powder, 10-15 parts of talcum powder, 3-5 parts of magnesium carbonate, 4-8 parts of glycerin, 4-8 parts of sodium carbonate, 1-3 parts of stearic acid, an appropriate amount of 1 mol / L HNO3 solution, 50-60 parts of nanometer aluminum oxide sol, 1-3 parts of 1 mol / L La(NO3)3, 1-2 parts of 1 mol / L Sr(NO3)2, 0.5-1 part of 1 mol / L Co(NO3)2, 2-6 parts of 1 mol / L citric acid, and 100-200 parts of deionized water. The honeycomb ceramics disclosed by the invention have the advantages of being high in compressive strength, good in high temperature resistance, good in chemical stability, high in corrosion resistance and the like.

Description

technical field [0001] The invention relates to ceramic materials, in particular to a sterilized sheet-shaped honeycomb ceramic and a preparation method thereof. technical background [0002] Motor vehicle pollution has become an important source of air pollution in my country and an important cause of haze and photochemical smog pollution. Vehicle exhaust is mainly nitrogen oxides (NO x ), hydrocarbons (HC), carbon monoxide (C0), particulate matter, etc., have become the main air pollutants. Therefore, the most important thing to solve the air pollution problem is to solve the problem of automobile exhaust pollution. [0003] The automobile exhaust purifier is mainly composed of three parts: the shell, the carrier and the catalyst, among which the selection of the catalyst is very important. Three-way catalyst refers to the ability to remove NO at the same time x , HC, CO these three main pollutants catalysts, a large number of experimental studies have shown that the ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/06C04B35/195C04B35/76B01J23/83C04B41/85
CPCB01J23/002B01J23/83B01J2523/00C04B35/195C04B35/76C04B38/0006C04B38/06C04B41/009C04B41/5045C04B41/85C04B2235/3206C04B2235/3244C04B2235/3445C04B2235/349C04B2235/442C04B2235/5212C04B41/5031C04B41/5027C04B41/4535C04B41/0072B01J2523/24B01J2523/3706B01J2523/845
Inventor 闫秦峻
Owner BENGBU NANZI INSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products