A kind of anti-aging, glass glue technology, applied in the direction of ink, household utensils, applications, etc., can solve the problems of loss of bonding performance, slow drying speed, weak adhesive force, etc. strong effect

Inactive Publication Date: 2016-12-14
青岛燕园海洋生物科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Glass glue is usually soluble in water and can be used as an adhesive. However, the current glass glue often has defects such as slow drying speed, weak adhesion, and flammability. Cause it to fall off, lose its bonding performance, and bring inconvenience to people's use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A novel aging-resistant glass glue, comprising the following components in parts by weight:

[0015] 35 parts of polyacrylate emulsion, 5 parts of organic methyl silicone, 5 parts of calcium carbonate, 0.1 part of antibacterial agent, 15 parts of polyoxyethylene sorbitan monolaurate, 1 part of sodium monofluorophosphate, 2 parts of hydrogen peroxide, ethylene glycol 2 parts of alcohol, 6 parts of phenolic resin, 10 parts of water glass, 20 parts of deionized water.

Embodiment 2

[0017] A novel aging-resistant glass glue, comprising the following components in parts by weight:

[0018] 45 parts of polyacrylate emulsion, 7.5 parts of organic methyl silicone, 10 parts of calcium carbonate, 0.3 parts of antibacterial agent, 18 parts of polyoxyethylene sorbitol monolaurate, 1.5 parts of sodium monofluorophosphate, 4.5 parts of hydrogen peroxide, ethylene glycol 5 parts of alcohol, 7 parts of phenolic resin, 15 parts of water glass, and 35 parts of deionized water.

Embodiment 3

[0020] A novel aging-resistant glass glue, comprising the following components in parts by weight:

[0021] 55 parts of polyacrylate emulsion, 10 parts of organic methyl silicone, 15 parts of calcium carbonate, 0.5 parts of antibacterial agent, 20 parts of polyoxyethylene sorbitol monolaurate, 3 parts of sodium monofluorophosphate, 6 parts of hydrogen peroxide, ethylene glycol 6 parts of alcohol, 9 parts of phenolic resin, 20 parts of water glass, and 50 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical materials, in particular to novel anti-aging glass cement. The novel anti-aging glass cement is prepared from, by weight, 35-55 parts of polyacrylate emulsion, 5-10 parts of organic methyl silicone, 5-15 parts of calcium carbonate, 0.1-0.5 part of antibacterial agent, 15-20 parts of polyoxyethylenesorbitol monolaurate, 1-3 parts of sodium monofluorophosphate, 2-6 parts of hydrogen peroxide, 2-6 parts of ethanediol, 6-9 parts of phenolic resin, 10-20 parts of sodium silicate and 20-50 parts of deionized water. The novel anti-aging glass cement has the advantages of being high in ageing resistance, short in drying time, high in drying speed, large in adhesive force, not prone to falling and environmentally friendly; production raw materials of the glass cement are cheap, and the production process is simple, suitable for batch production and capable of being applied and popularized.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to a novel aging-resistant glass glue. Background technique [0002] Glass glue is a material for bonding and sealing various glasses with other substrates. Mainly divided into two categories: silicone glue and polyurethane glue (PU). Silicone glue is divided into acid glue and neutral glue. Neutral glue includes structural glue, sealant and weather-resistant glue. Glass glue is usually soluble in water and can be used as an adhesive. However, the current glass glue often has defects such as slow drying speed, weak adhesion, and flammability. Cause it to come off, lose bonding performance, bring inconvenience to people's use. Therefore, need a kind of glass cement of new formula to satisfy people's market demand. Contents of the invention [0003] Aiming at the problems in the prior art, the invention provides a novel aging-resistant glass glue, which solves the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D11/04C09D11/06
CPCC09D133/04C08L2205/035C09D11/04C09D11/06
Inventor 陆明军
Owner 青岛燕园海洋生物科技有限公司