Long-acting antimicrobial glass fiber air filtering paper and preparation method thereof

A technology of air filter paper and glass fiber, which is applied in the direction of filter paper, synthetic cellulose/non-cellulose material pulp/paper, filtration and separation, etc., which can solve the problem that nano silver and glass fiber cannot be tightly combined, the ventilation rate is large, and agglomeration is easy to occur and other problems, to achieve the effect of increasing the interaction area and interfacial bonding force, improving strength and stiffness, and excellent antibacterial properties

Active Publication Date: 2016-12-14
泰安三英新材料股份有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the air filter material of power plants requires a large amount of ventilation, which requires high strength and burst resistance for the filter material, and requires water and oil repellency to cope with harsh environments, thereby prolonging the service life of the filter. The existing The filter material needs to be further enhanced
Moreover, it has been reported that by adding nano-silver on the surface of glass fiber to endow glass fiber with antibacterial properties, it can be applied to filter paper and resin to make it have antibacterial properties; The specific parts of the surface cannot be evenly distributed on the surface, thereby affecting the antibacterial effect; on the other hand, nano-silver and glass fibers cannot be tightly combined (especially when the content of nano-silver particles increases, agglomeration is prone to occur), and it is easy to use during use. Falling off, thus affecting the service life and antibacterial effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-acting antimicrobial glass fiber air filtering paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method for antibacterial glass fiber air filter paper, comprising the steps of:

[0024] (1) Preparation of antibacterial glass fiber, comprising the following steps:

[0025] (1) Preparation of glass fiber: After crushing and mixing 54.4% SiO2, 15% B2O3, 0.6% Na2O, 12% Al2O3 and 18% CaO, put it in a 400mL corundum crucible, melt it with a silicon-molybdenum rod resistance furnace, and feed The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers of a specific diameter;

[0026] (2) Glass fiber pretreatment: After taking 45 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 1mol / L. Dissolve the Na2O-B2O3 phase in acid, add 5ml of NH4Cl solution wi...

Embodiment 2

[0037] A preparation method for antibacterial glass fiber air filter paper, comprising the steps of:

[0038] (1) Preparation of antibacterial glass fiber, comprising the following steps:

[0039] (1) Preparation of glass fiber: After crushing and mixing 54.4% SiO2, 15% B2O3, 0.6% Na2O, 12% Al2O3 and 18% CaO, put it in a 400mL corundum crucible, melt it with a silicon-molybdenum rod resistance furnace, and feed The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers with a specific diameter;

[0040] (2) Glass fiber pretreatment: After taking 45 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 1mol / L. Dissolve the Na2O-B2O3 phase in acid, add 5ml of NH4Cl solution wi...

Embodiment 3

[0051] A preparation method for antibacterial glass fiber air filter paper, comprising the steps of:

[0052] (1) Preparation of antibacterial glass fiber, comprising the following steps:

[0053] (1) Preparation of glass fiber: After crushing and mixing 54.4% SiO2, 15% B2O3, 0.6% Na2O, 12% Al2O3 and 18% CaO, put it in a 400mL corundum crucible, melt it with a silicon-molybdenum rod resistance furnace, and feed The temperature is 1370°C, the melting and clarification temperature is 1450±10°C, it is released at 1200°C, poured into a mold, sent into a muffle furnace, and annealed at 500°C to obtain glass; the prepared glass is heated to a drawing viscosity temperature of 1050 ℃, drawn into glass fibers with a specific diameter;

[0054] (2) Glass fiber pretreatment: After taking 45 parts of glass fiber for phase separation, carry out acid leaching treatment in 100ml of HCl solution with a concentration of 1mol / L. Dissolve the Na2O-B2O3 phase in acid, add 5ml of NH4Cl solution ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses long-acting antimicrobial glass fiber air filtering paper and a preparation method thereof. The preparation method comprises the following steps: (1) preparing glass fibers; (2) pretreating the glass fibers; (3) preparing silver-loaded glass fibers; (4) coating porous graphene; (5) preparing silver / titanium dioxide-loaded antimicrobial glass fibers; (6) preparing the glass fiber filtering paper. By the method provided by the invention, the glass fibers are more effectively coated with graphene, silver and titanium dioxide in a uniform and dispersive manner, and the interaction area and the interface bonding strength of the glass fibers are further increased, so that the mechanical property of the glass fiber filtering paper is more excellent and the strength and the stiffness of the material are greatly improved; the composite material has an excellent antimicrobial property due to the antimicrobial characteristics of silver and titanium dioxide.

Description

technical field [0001] The invention relates to a durable antibacterial glass fiber air filter paper and a preparation method thereof. Background technique [0002] my country is a big electricity consumer, with a total annual electricity consumption of 4,868.4 billion kwh, and an annual growth rate of 4-10%. However, the annual average output of my country's largest Three Gorges Hydropower Station is only 107.3 billion kwh, and the annual There are 289 large-scale power stations with an output of more than 5 million kilowatt-hours, and countless medium-sized and small-sized power stations. All power plants need to install multiple sets of air filters in the air intake and exhaust systems to provide clean air. . This type of air filter is divided into three grades of high, medium and primary efficiency according to the efficiency level. Except for the primary filter which uses metal wire or glass fiber felt, the filter material of the rest of the filters is basically glass fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/08D21H13/40D21H21/14D21H21/16
CPCD21H13/40D21H21/14D21H21/16D21H27/08
Inventor 黎淑娟
Owner 泰安三英新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap