Diaphragm material for purifying sewage and preparation method thereof

A diaphragm and sewage technology, applied in chemical instruments and methods, biological water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problem of poor working environment of aeration pans, affecting the quality of sewage treatment, affecting economic benefits, etc. Problems, to achieve good low volatility, low expansion, increase the effect of mechanical properties

Inactive Publication Date: 2017-01-18
ANHUI ZHONGDING SEALING PARTS
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the harsh working environment of the aeration disc, the diaphragm will harden and shrink after being soaked in sewage for a long time, resulting in high maintenance costs, affecting the quality of sewage treatment, and also affecting economic benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A diaphragm material for purifying sewage, its raw materials include by weight: Mooney value ML (1+4), 175 parts of 125 ℃ 65MU oil-filled ethylene propylene rubber raw rubber, 20 parts of super wear-resistant carbon black, fast pressing 80 parts of carbon black, 45 parts of thermal carbon black, 50 parts of naphthenic oil, 3 parts of indirect method zinc oxide, 0.5 parts of stearic acid, 2.5 parts of polyethylene glycol, 2.5 parts of lubricant, 1 part of sulfur, promote 3 doses.

[0019] The preparation method of the above membrane material for purifying sewage comprises the following steps:

[0020] S1, preparation of synthetic rubber: put each raw material in a banbury mixer, and carry out banbury mixing to obtain a synthetic rubber, wherein the hardness of the synthetic rubber is 42°, the strength is 14.3MPa, and the elongation is 523%;

[0021] S2. Molding and vulcanization: Put the synthetic rubber obtained in S1 into the open mill, raise the temperature to 60°C, ...

Embodiment 2

[0024] A membrane material for purifying sewage, the raw materials of which include by weight: Mooney value ML (1+4), 175 parts of oil-filled ethylene propylene rubber raw rubber at 125°C 75MU, 25 parts of Zhongchao wear-resistant carbon black, fast pressing 85 parts of carbon black, 50 parts of thermal carbon black, 55 parts of naphthenic oil, 5 parts of zinc oxide by indirect method, 1 part of stearic acid, 3 parts of polyethylene glycol, 3 parts of lubricant, 1.2 parts of sulfur, promote 4 doses.

[0025] The preparation method of the above membrane material for purifying sewage comprises the following steps:

[0026] S1, preparation of synthetic rubber: put each raw material in the banbury mixer, carry out banbury mixing to obtain synthetic rubber, wherein, the hardness of the synthetic rubber is 55°, the strength is 14.5MPa, and the elongation is 516%;

[0027] S2. Molding and vulcanization: put the synthetic rubber obtained in S1 into the open mill, raise the temperatur...

Embodiment 3

[0030] A diaphragm material for purifying sewage, its raw materials include by weight: Mooney value ML (1+4), 175 parts of 125 ℃ 69MU oil-filled ethylene propylene rubber raw rubber, 30 parts of Zhongchao wear-resistant carbon black, fast pressing 90 parts of carbon black, 55 parts of thermal carbon black, 60 parts of naphthenic oil, 8 parts of indirect zinc oxide, 1.5 parts of stearic acid, 4.5 parts of polyethylene glycol, 4.5 parts of lubricant, 1.5 parts of sulfur, promote 5 doses.

[0031] The preparation method of the above membrane material for purifying sewage comprises the following steps:

[0032] S1. Preparation of synthetic rubber: adding various raw materials into a banbury mixer, and banburying to obtain a synthetic rubber, wherein the hardness of the synthetic rubber is 57°, the strength is 15.1MPa, and the elongation is 512%;

[0033] S2. Molding and vulcanization: put the synthetic rubber obtained in S1 into the open mill, raise the temperature to 60°C, start...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a diaphragm material for purifying sewage. Raw materials of the diaphragm material comprise, by weight, 175 parts of ethylene propylene rubber, 20-30 parts of intermediate super abrasion carbon black, 80-90 parts of fast extruding carbon black, 45-55 parts of thermal decomposition process carbon black, 50-60 parts of naphthenic oil, 3-8 parts of indirect zinc oxide, 0.5-1.5 parts of stearic acid, 2.5-4.5 parts of polyethylene glycol, 2.5-4.5 parts of a lubricant, 1-1.5 parts of sulphur and 3-5 parts of a promoter. The invention also discloses a preparation method of the above diaphragm material for purifying sewage. The diaphragm material of the invention has high mechanical property and low expandability.

Description

technical field [0001] The invention relates to the technical field of membranes for purifying sewage, in particular to a membrane material for purifying sewage and a preparation method thereof. Background technique [0002] Since entering the 21st century, the global industry, especially China, has developed faster and faster, and at the same time, the pollution caused by it has become more and more serious. Among them, sewage pollution is one of the important ways, whether it is harmful to human health or have had adverse effects on the environment. Therefore, in today's advocacy of environmental protection, the control of industrial pollution is becoming more and more important, and corresponding sewage treatment plants and sewage treatment systems have emerged as the times require and are more and more widely used. The core part of the sewage treatment system is the aeration pan, and the membrane is used to filter and purify the sewage in the aeration pan. The quality o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L71/02C08L91/00C08K13/02C08K3/04C08K3/22C08K5/09C08K3/06B29C35/02B01D71/24C02F7/00C02F3/20
CPCB01D71/24B29C35/02C02F3/201C02F7/00C08K2201/014C08L23/16C08L2205/03C08L71/02C08L91/00C08K13/02C08K3/04C08K2003/2296C08K5/09C08K3/06Y02W10/10
Inventor 魏巍俞晨曦章朋飞彭世明杨登兵陈志翔
Owner ANHUI ZHONGDING SEALING PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap