Environment-friendly hot melt adhesive

A hot-melt adhesive, environmentally friendly technology, applied in the direction of epoxy resin adhesive, adhesive, adhesive type, etc., can solve the problems of high preparation cost, poor environmental protection performance, environmental pollution, etc., and achieves less preparation raw materials and low preparation cost. , the effect of good environmental performance

Inactive Publication Date: 2017-01-18
安徽永大胶业科技发展有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with thermosetting, solvent-based and water-based adhesives, it has many advantages. Therefore, since the 1950s, hot-melt adhesives have developed rapidly in many fields and have been used in construction, aircraft, ships and automobiles. In interior decoration and other fields, especially in printing, packaging and other industries, hot melt adhesives have been used to replace nail binding and wire binding, but the most widely used one is hot melt adhesives for bookbinding. Most of the existing hot melt adhesives have many raw materials and cost High, and some components that pollute the environment are added, and the environmental protection performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] An environment-friendly hot melt adhesive, the hot melt adhesive is composed of the following components by weight: 80 parts of resin, 13 parts of dioctyl phthalate, 18 parts of attapulgite, 12 parts of pentaerythritol ester, 3 parts of ferrocene 1 part, antioxidant TBM-63 parts, mica powder 1 part, benzoin 1 part, microcrystalline wax 6 parts, paraffin oil 1 part, magnesium oxide powder 2 parts, angelica oil 3 parts, pottery clay 15 parts, glass powder 4 parts, 6 parts of diatomaceous earth and 10 parts of precipitated barium sulfate.

[0012] The resin is any two of EVA resin, silicone resin, epoxy resin and phenolic resin.

Embodiment 2

[0014] An environment-friendly hot-melt adhesive, the hot-melt adhesive is composed of the following components by weight: 87 parts of resin, 157 parts of dioctyl phthalate, 19 parts of attapulgite, 14 parts of pentaerythritol ester, 3 parts of ferrocene 4 parts, antioxidant TBM-65 parts, 3 parts of mica powder, 2 parts of benzoin, 8 parts of microcrystalline wax, 2 parts of paraffin oil, 4 parts of magnesium oxide powder, 5 parts of angelica oil, 17 parts of pottery clay, 4 parts of glass powder, 7 parts of diatomaceous earth and 12 parts of precipitated barium sulfate.

[0015] The resin is any two of EVA resin, silicone resin, epoxy resin and phenolic resin.

Embodiment 3

[0017] An environment-friendly hot-melt adhesive, the hot-melt adhesive is composed of the following components by weight: 95 parts of resin, 17 parts of dioctyl phthalate, 21 parts of attapulgite, 16 parts of pentaerythritol ester, 4 parts of ferrocene , antioxidant TBM-67 parts, mica powder 4 parts, benzoin 3 parts, microcrystalline wax 9 parts, paraffin oil 3 parts, magnesium oxide powder 6 parts, angelica oil 6 parts, pottery clay 18 parts, glass powder 5 parts, 8 parts of diatomaceous earth and 15 parts of precipitated barium sulfate.

[0018] The resin is any two of EVA resin, silicone resin, epoxy resin and phenolic resin.

[0019] The hot-melt adhesive prepared by implementing the components of implementation 1, implementation 2 and implementation 3, compared with the ordinary hot-melt adhesive in the prior art, has less raw materials for preparation, low preparation cost, does not contain any components that pollute the environment, and falls off after use. It will n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to an environment-friendly hot melt adhesive, the hot melt adhesive comprises the following components in part by weight: 80-95 parts of resin, 13-17 parts of dioctyl phthalate, 18-21 parts of attapulgite, 12-16 parts of pentaerythritol ester, 3-4 parts of ferrocene, 3-7 parts of antioxidant TBM-6, 1-4 parts of mica powder, 1-3 parts of benzoin, 6-9 parts of microcrystalline wax, 1-3 parts of paraffin oil, 2-6 parts of magnesium oxide powder, 3-6 parts of angelica oil, 15-18 parts of clay, 4-5 parts of glass powder, 6-8 parts of diatomite and 10-15 parts of precipitated barium sulfate. The hot melt adhesive has the advantages of less preparation materials, low preparation cost, no any environmental pollution components, no environmental pollution after peeling when in use, and good environmental protection performance.

Description

technical field [0001] The invention relates to a hot melt adhesive, in particular to an environment-friendly hot melt adhesive. Background technique [0002] Hot melt adhesive is a solid adhesive made of thermoplastic resin or elastomer as the base material, adding tackifier, plasticizer, antioxidant, flame retardant and filler, and melting and mixing. Compared with thermosetting, solvent-based and water-based adhesives, it has many advantages. Therefore, since the 1950s, hot-melt adhesives have developed rapidly in many fields and have been used in construction, aircraft, ships and automobiles. In interior decoration and other fields, especially in printing, packaging and other industries, hot melt adhesives have been used to replace nail binding and wire binding, but the most widely used one is hot melt adhesives for bookbinding. Most of the existing hot melt adhesives have many raw materials and cost High, and some components that pollute the environment have been added...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J183/04C09J163/00C09J161/06C09J11/04C09J11/06C09J11/08
CPCC09J123/0853C08L2205/02C08L2205/035C09J11/04C09J11/06C09J11/08C09J161/06C09J163/00C09J183/04C08L83/04C08L63/00C08L61/06C08L91/06C08L91/00C08K13/02C08K5/12C08K3/346C08K5/053C08K3/34C08K3/40C08K2003/3045C08L23/0853
Inventor 姚寒周铸成方文革
Owner 安徽永大胶业科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products