Lead acid storage battery positive electrode lead paste and preparation method thereof

A technology of lead-acid battery and positive electrode paste, applied in lead-acid battery electrodes, battery electrodes, circuits, etc., can solve problems such as fuel economy fluctuations, improve deep cycle life, improve corrosion resistance, and increase cycle life Effect

Inactive Publication Date: 2017-02-08
陈申申
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to different working conditions, the fuel economy of idling start and stop fluctuates, but it can basically achieve 5%-10% fuel saving ability, which has a significant effect on reducing emissions and protecting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A preparation method of lead-acid storage battery positive electrode paste, the preparation method is as follows:

[0029] S1: Add glue-free carbon fiber, basalt fiber, 4BS seed crystal, polyester fiber, core-shell acrylic elastic emulsion, and carboxymethyl cellulose to the paste equipment and mix and stir evenly to obtain additive mixture A;

[0030] S2: Add trilead tetroxide, antimony trioxide, niobium trialuminum and bisulfate into the paste equipment, mix and stir evenly to obtain additive mixture B;

[0031] S3: Mix the additive mixture A of step S1 with the additive mixture B of step S2, then add lead powder and nano-silicon dioxide to fully stir and mix, mixing and stirring for 5-8 minutes, then add an appropriate amount of pure water, and fully stir and mix, The mixing and stirring time is 2-3min to obtain the mixture.

[0032] S4: adding sulfuric acid into the mixture in step S3 in the form of spraying while stirring, mixing and stirring evenly to obtain the ...

Embodiment 1

[0034] A kind of anode lead paste of lead-acid storage battery, is made of the following ingredients in parts by weight:

[0035] 70 parts of lead powder, 0.01 parts of non-glue carbon fiber, 0.01 part of basalt fiber, 5 parts of trilead tetroxide, 2 parts of antimony trioxide, 1 part of polyester fiber, 2 parts of niobium trialuminum, 2 parts of sulfuric acid, 6 parts of bisulfate Parts, 3 parts of nano-silica, 15 parts of core-shell acrylic elastic emulsion, 0.5 parts of carboxymethyl cellulose, 0.35 parts of chemical resistance modifier, 9 parts of pure water.

Embodiment 2

[0037] A kind of anode lead paste of lead-acid storage battery, is made of the following ingredients in parts by weight:

[0038] 90 parts of lead powder, 0.1 part of non-glue carbon fiber, 0.1 part of basalt fiber, 0.8 part of 4BS seed crystal, 12 parts of trilead tetroxide, 8 parts of antimony trioxide, 5 parts of polyester fiber, 6 parts of niobium trialuminum, and 7 parts of sulfuric acid 8 parts, bisulfate 8 parts, nano-silica 6 parts, core-shell acrylic elastic emulsion 20 parts, carboxymethyl cellulose 1.5 parts, chemical resistance modifier 1.05 parts, pure water 13 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses lead acid storage battery positive electrode lead paste and a preparation method thereof. The lead acid storage battery positive electrode lead paste is prepared from the following ingredients in parts by weight: 70 to 90 parts of lead powder, 0.01 to 0.1 part of adhesive-free carbon fiber, 0.01 to 0.1 part of basalt fiber, 0 to 0.8 part of 4BS seed crystals, 5 to 12 parts of lead tetraoxide, 2 to 8 parts of antimonous oxide, 1 to 5 parts of polyester fiber, 2 to 6 parts of triniobium aluminum, 2 to 7 parts of sulfuric acid, 6 to 8 parts of hydrosulfate,3 to 6 parts of nanometer silicon dioxide, 15 to 20 parts of nucleocapsid acrylic acid elastic emulsion, 0.5 to 1.5 parts of carboxymethyl cellulose, 0.35 to 1.05 parts of chemical-resistant modifying agents and 9 to 13 parts of pure water. The adhesive-free carbon fiber addition technology is used, and the adhesive-free carbon fiber can enhance the adhesion effect of the lead paste; in addition, the lead paste low-acid content technology is used, so that the battery deep circulation service life is greatly prolonged; through the addition of the nucleocapsid acrylic acid elastic emulsion and the nanometer silicon dioxide, the weathering performance of the lead paste is improved; the perfluoroalkyl acrylic acid series additives are introduced to be used as chemical-resistant modifying agents, so that the anti-corrosion performance of the lead paste is greatly improved.

Description

technical field [0001] The invention relates to the field of storage batteries, in particular to a lead-acid storage battery cathode lead paste and a preparation method thereof. Background technique [0002] With the attention of various countries on climate change and the gradual improvement of people's awareness of environmental protection, the voice of reducing vehicle exhaust emissions is also getting higher and higher. Pollutants emitted by motor vehicles mainly include hydrocarbons (HC), nitrogen oxides (NOx), carbon monoxide (CO), particulates (PM) and other harmful substances, which will have a direct impact on global climate change, environmental pollution, and human health. Reducing vehicle exhaust emissions has basically become the common understanding of the world's major economies. [0003] The micro-hybrid idling start-stop car has obvious practical significance in terms of saving fuel, reducing greenhouse gas, and toxic and harmful gas emissions. According t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/56H01M4/16
CPCH01M4/16H01M4/56Y02E60/10
Inventor 陈申申
Owner 陈申申
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog