Modified argillaceous lake mud construction material and preparation method

A clay-based and modified technology, applied in the field of building materials, can solve problems such as high price, secondary pollution of dust, pollutants, etc., achieve excellent light stability and weather resistance, reduce ecological damage, and alleviate the effects of lake mud deposition

Active Publication Date: 2017-03-15
施仙增
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the use of the above-mentioned many ore powders without proper use of binders, after drying and weathering, the coatings that are easy to dehydrate and become hardened tend to lose their bonding effect with the wall, and problems such as cracking, falling off, and powder falling of the coating are prone to occur. Dust and other secondary pollution
However, the above-mentioned patent only uses diatomite and sepiolite with adsorption function, but does not use materials with catalytic and decomposition functions, so after its adsorption is saturated, its coating becomes a potential pollutant
Moreover, its high price has discouraged many consumers, which has ultimately led to its failure to popularize and promote.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified argillaceous lake mud construction material and preparation method
  • Modified argillaceous lake mud construction material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A modified clay lake mud building material, comprising the following components in parts by weight: 30 parts of distilled water, 45 parts of modified clay lake mud powder, 5 parts of modified mineral water-retaining thickener, and 15 parts of hydrophilic nano-titanium dioxide 1 part, 1 part of photocatalyst, 5 parts of talcum powder, 1 part of modified acrylate emulsion, 3 parts of medical stone powder, 0.5 part of hydroxyethyl methylcellulose, 3 parts of pigment, nano-TiO2 modified chitosan antibacterial and antifungal agent 1 serving.

[0027] A preparation method of a modified clay lake mud building material, comprising the following steps: putting clay lake mud into a mixer, adding 4 parts by weight of PAS inorganic flocculant, stirring at 120r / min for 50s, standing for 45min, and discharging the supernatant Then put it into a rotary kiln, calcined at 540°C for 7 hours, crushed after sintering and passed through a 700-mesh screen to obtain dry clay lake mud powder; ...

Embodiment 2

[0029] A modified clay lake mud building material, comprising the following components in parts by weight: 50 parts of distilled water, 10 parts of modified clay lake mud powder, 12 parts of modified mineral water-retaining thickener, and 4 parts of hydrophilic nano-titanium dioxide 12 parts of photocatalyst, 0.5 parts of talcum powder, 5 parts of modified acrylate emulsion, 0.5 parts of medical stone powder, 3 parts of hydroxyethyl methylcellulose, 0.1 part of pigment, nano-TiO2 modified chitosan antibacterial and antifungal agent 3 copies.

[0030] A preparation method of a modified clay lake mud building material, comprising the following steps: putting clay lake mud into a mixer, adding 4 parts by weight of PAS inorganic flocculant, stirring at 180r / min for 40s, standing for 50min, and discharging the supernatant Then put it into the rotary kiln, calcined at 510°C for 7 hours, crushed after sintering and passed through a 150-mesh screen to obtain dry clay lake mud powder; ...

Embodiment 3

[0032] A modified clay lake mud building material, comprising the following components in parts by weight: 45 parts of distilled water, 24 parts of modified clay lake mud powder, 10 parts of modified mineral water-retaining thickener, and 5 parts of hydrophilic nano-titanium dioxide 8 parts, 8 parts of photocatalyst, 1 part of talcum powder, 3 parts of modified acrylate emulsion, 1 part of medical stone powder, 1.5 parts of hydroxyethyl methylcellulose, 0.3 parts of pigment, nano-TiO2 modified chitosan antibacterial and antifungal agent 2 servings.

[0033] A method for preparing a modified clay lake mud building material, comprising the following steps: putting clay lake mud into a mixer, adding 4 parts by weight of PAS inorganic flocculant, stirring at 130r / min for 48s, standing for 46min, and discharging the supernatant Then put it into a rotary kiln, calcined at 530°C for 7 hours, crushed after sintering and passed through a 500-mesh screen to obtain dry clay lake mud powd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified argillaceous lake mud construction material and a preparation method, and belongs to the technical field of construction materials. The construction material comprises distilled water, modified argillaceous lake mud powder, a modified mineral water retention thickener, hydrophilic nanometer titanium dioxide, a photocatalyst, talcum powder, a modified polyacylate emulsion, medical stone powder, hydroxyethyl methyl cellulose, pigment and a nanometer TiO2 modified chitosan antibacterial and antifungal agent. The construction material is prepared by scientific compatibility of environmental-friendly materials, and the construction material is safe, stable, and free of toxicity and volatile harmful gas. Moreover, the construction material not only can adsorb and purify formaldehyde, benzene and other harmful gas, but also can adjust indoor humidity, enhance finishing metope texture, achieve sound insulation and heat preservation, eliminate peculiar smells, and achieve fire prevention and fire resistance. The construction material also has the advantages of being low in cost, free of cracking and dusting, antibacterial, antifungal, and easy to repair and the like.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to a modified clay lake mud building material and a preparation method thereof. Background technique [0002] With the continuous improvement of living standards, people have higher and higher requirements for the personalization of decoration and the environmental protection of materials. In the past, the combination of putty powder and latex paint used to decorate interior walls can no longer meet people's needs. Diatom mud paint has become popular, but its high price has discouraged many consumers. The release of formaldehyde and other harmful gases after house decoration lasts for weeks or even decades, seriously affecting people's lives and health. At present, building materials such as deodorizing latex paint, aldehyde-removing latex paint, and diatom mud are common in the market. The deodorization and aldehyde removal mainly rely on methods such as reducing or not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/06C04B111/20C04B111/28C04B111/52
CPCC04B26/06C04B2111/00017C04B2111/00025C04B2111/00827C04B2111/20C04B2111/28C04B2111/52C04B18/0436C04B14/106C04B22/06C04B14/042C04B14/14C04B24/383C04B2103/54C04B2103/69
Inventor 梁剑斌郑荣莹
Owner 施仙增
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap