Thermal insulation coating and preparation method thereof

A technology of thermal insulation and coating, applied in the field of thermal insulation coating and its preparation, can solve the problems of thermal insulation, poor thermal insulation performance, short service life of the thermal insulation system, and no thermal insulation function, etc., to achieve the best Anti-ultraviolet performance and surface strength, improve the overall performance of the product, improve the effect of easy flow and self-resistance strength

Inactive Publication Date: 2017-03-15
杭州正博新型建筑材料有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the traditional external thermal insulation system, the finishing coating only has the function of decoration and general waterproofing, and does not have the function of thermal insulation, which has certain limitations for the protection of the entire system.
However, some existing thermal insulation coatings generally have problems such as thermal insulation and thermal insulation performance are not good, and the service life of the thermal insulation system is short.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Thermal insulation coating, which includes the following raw materials by weight: 53 parts of deionized water, 11 parts of perlite, 4 parts of sepiolite, 6 parts of porous powder quartz, 4 parts of hollow glass beads, 6 parts of aluminum silicate, acrylic acid 6 parts of emulsion, 6 parts of light calcium carbonate, 2 parts of wood fiber, 1 part of adhesive, 1 part of defoamer.

[0023] Among them, the bulk density of the hollow glass beads is 100kg / m3, the fineness particle size is 30-40 mesh, and the binder uses hydroxypropyl methylcellulose with a viscosity of 200,000 MPa·s.

Embodiment 2

[0025] Same as Example 1, the difference is that the thermal insulation coating includes the following raw materials by weight: 50 parts of deionized water, 10 parts of perlite, 4 parts of sepiolite, 7 parts of porous powdered quartz, 3 parts of hollow glass beads, 5 parts of aluminum silicate, 6 parts of acrylic emulsion, 8 parts of light calcium carbonate, 3 parts of wood fiber, 2 parts of adhesive, 2 parts of defoamer.

Embodiment 3

[0027] Same as Example 1, the difference is that the thermal insulation coating includes the following raw materials by weight: 60 parts of deionized water, 10 parts of perlite, 3 parts of sepiolite, 5 parts of porous powdered quartz, 3 parts of hollow glass beads, 5 parts of aluminum silicate, 5 parts of acrylic emulsion, 5 parts of light calcium carbonate, 2 parts of wood fiber, 1 part of adhesive, 1 part of defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field, and discloses a thermal insulation coating and a preparation method thereof. The thermal insulation coating is mainly composed of the following raw materials in parts by weight: 50-60 parts of deionized water, 10-15 parts of perlite, 3-5 parts of sepiolite, 5-10 parts of porous konilite, 3-5 parts of hollow glass beads, 5-8 parts of aluminum silicate, 5-8 parts of acrylic emulsion, 5-10 parts of light calcium carbonate, 2-3 parts of wood fibers, 1-2 parts of an adhesive and 1-2 parts of an antifoaming agent. The thermal insulation coating is small in heat conductivity coefficient and has excellent thermal insulation effects, and compared with general thermal insulation coatings, the thermal insulation coating disclosed by the invention has high tensile strength and overall adhesion and cohesiveness.

Description

Technical field [0001] The invention relates to the technical field, in particular to a thermal insulation coating and a preparation method thereof. Background technique [0002] As my country's urbanization process is advancing step by step, a large number of new buildings are being constructed every year. In the current environment of energy saving and emission reduction, building energy saving has become the focus of social attention. The main method of building energy saving is to reduce the transmission of indoor and outdoor temperature, that is, to heat the inner and outer protective structure of the building. A large number of experiments are also the same. Insulation technology can obviously protect the wall and save energy. [0003] In the traditional external thermal insulation system, the finish coating only has decorative and general waterproof functions, and does not have thermal insulation functions, which has certain limitations for the protection of the entire syst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28
CPCC04B26/285C04B2111/00482C04B22/002C04B14/18C04B14/042C04B14/06C04B14/22C04B14/041C04B24/04C04B14/28C04B16/02C04B2103/50
Inventor 张正良
Owner 杭州正博新型建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products