Oil baffle plate for high-speed gear case vent cap

A technology of oil baffle and gear box, which is applied in metal material coating process, fusion spraying, coating, etc., can solve environmental pollution and other problems, and achieve the effect of improving matrix performance, improving stability, and uniform structure

Active Publication Date: 2017-03-15
南京创贝高速传动机械有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional high-speed gearbox vent cap directly discharges high-temperature oil and gas into the atmosphere through the vent pipe. Due to the high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The oil baffle plate for the vent cap of the high-speed gear box of the present embodiment, the mass percentages of its components are: tungsten carbide: 0.55%, montmorillonite: 1.36%, kaolin: 1.68%, bone char: 3.48%, alumina: 2.23% %, magnesium oxide: 1.47%, copper oxide: 1.19%, iron oxide: 0.57%, AlN: 0.44%, wollastonite: 1.25%, diopside: 0.58%, talcum powder: 0.67%, antioxidant RD: 0.39 %, Fe: 0.69%, Iron hydroxide: 0.26%, Al: 1.36%, Zn: 0.77%, Mn: 0.46%, Cr: 0.04%, Ni: 1.27%, Cu: 0.68%, Mo: 0.03%, Ti : 1.27%, Pd: 0.15%, Pt: 0.04%, W: 0.59%, Ce: 0.03%, Eu: 0.08%, Lu: 0.06%, Au: 0.35%, Ag: 0.67%, Sn: 0.49%, Zr : 0.02%, Re: 0.03%, the balance is clay;

[0051] The processing technology of the oil baffle for the breather cap of the high-speed gear box includes the following steps:

[0052] (1) The metal materials in the raw materials of the oil baffle are mixed according to the mass percentage and then smelted. The specific steps are as follows:

[0053] a. Add metal...

Embodiment 2

[0083] The oil baffle plate for the vent cap of the high-speed gearbox of the present embodiment is basically the same as that of Embodiment 1, the difference is that the mass percentages of the components of the oil baffle plate for the vent cap of the high-speed gearbox are: tungsten carbide: 0.73%, montmorillonite : 1.45%, kaolin: 1.78%, bone char: 3.62%, alumina: 2.33%, magnesium oxide: 1.66%, copper oxide: 1.21%, iron oxide: 0.63%, AlN: 0.56%, wollastonite: 1.32%, Diopside: 0.68%, talc powder: 0.82%, antioxidant RD: 0.51%, Fe: 0.87%, iron hydroxide: 0.32%, Al: 1.43%, Zn: 1.12%, Mn: 0.48%, Cr: 0.04 %, Ni: 1.33%, Cu: 0.72%, Mo: 0.03%, Ti: 1.38%, Pd: 0.16%, Pt: 0.07%, W: 0.64%, Ce: 0.07%, Eu: 0.11%, Lu: 0.06 %, Au: 0.41%, Ag: 0.82%, Sn: 0.62%, Zr: 0.03%, Re: 0.03%, and the balance is clay.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an oil baffle plate for a high-speed gear case vent cap. The oil baffle plate comprises tungsten carbide, montmorillonite, kaolin, bone black, aluminum oxide, magnesium oxide, copper oxide, ferric oxide, AlN, wollastonite, diopside, talcum powder, an anti-aging agent RD, Fe, ferric hydroxide, Al, Zn, Mn, Cr, Ni, Cu, Mo, Ti, Pd, Pt, W, Ce, Eu, Lu, Au, Ag, Sn, Zr, Re and clay. According to the oil baffle plate for the high-speed gear case vent cap, both the bone black and metal raw materials are added into the raw materials, so that the structural strength of the oil baffle plate is improved, heat dispersion of the oil baffle plate is also greatly strengthened compared with that of a pure ceramic material, the condensation efficiency is improved, and thus the oil baffle efficiency of the oil baffle plate is also improved.

Description

technical field [0001] The invention relates to an oil deflector for a vent cap of a high-speed gear box, belonging to the technical field of auto parts. Background technique [0002] Under the condition of high-speed operation, the internal temperature of the gearbox will gradually rise, the gas will continue to expand, and the pressure will continue to increase. In order to allow the thermally expanded air to be discharged freely, to maintain the pressure balance inside and outside the box, so as not to cause the lubricating oil to separate along the box To prevent leakage from other gaps such as surface or shaft seals, and to enhance the sealing effect of the box, it is necessary to install a breather cap on the gearbox. The function of the breather cap is to connect the air in the gear box with the atmosphere outside the box, so as to ensure that the pressure in the box is balanced with the atmospheric pressure. [0003] The traditional high-speed gearbox vent cap direc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C29/12C22C1/05C23C4/131C23C4/08
CPCC22C1/051C22C29/12C23C4/08
Inventor 陆树根
Owner 南京创贝高速传动机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products