Capacitor aluminum shell high-temperature-resistant paint

A technology for high temperature resistant coatings and capacitors, used in fire-resistant coatings, polyamide coatings, coatings, etc., can solve the problems of unstable power supply, low service life, and easy cracking of electronic components, and improve scratch resistance. , Improve service life, good effect

Inactive Publication Date: 2017-03-22
ANHUI FEIDA ELECTRICAL TECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the coatings sprayed on the aluminum shell of capacitors generally have a low service life. After long-term use, the coating film is easy to crack and shatter, and the capacitor product will generate heat energy during use. If the heat energy cannot be effectively resolved or diffused, the capacitor will advance with temperature. Aging life, long-term work due to temperature changes, will also cause instability in the power supply of electronic components, causing certain harm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-temperature-resistant coating for capacitor aluminum shells, made of the following components in parts by weight: polyamide resin 55, polyvinyl alcohol 15, polymethyl methacrylate 25, diatomite 8, phenolic resin 15, silicone oil 3, silicon Aluminum Acid 1, Olive Oil 3, Sodium Phosphate 1, Wheat Husk Ash 1, Corn Stalk Extract 0.1.

Embodiment 2

[0020] A high-temperature-resistant coating for capacitor aluminum shells, made of the following components in parts by weight: polyamide resin 60, polyvinyl alcohol 20, polymethyl methacrylate 35, diatomite 10, phenolic resin 18, silicone oil 5, silicon Aluminate 3, Olive Oil 6, Sodium Phosphate 4, Wheat Husk Ash 4, Corn Stalk Extract 0.3.

Embodiment 3

[0022] A high-temperature-resistant coating for capacitor aluminum shells, made of the following components in parts by weight: polyamide resin 58, polyvinyl alcohol 17, polymethyl methacrylate 30, diatomite 9, phenolic resin 16, silicone oil 4, silicon Aluminate 2, Olive Oil 4, Sodium Phosphate 3, Wheat Husk Ash 2, Corn Stalk Extract 0.2.

[0023] The application method of capacitor aluminum shell coating is as follows:

[0024] ① Clean the surface of the aluminum shell of the capacitor with 2.5% sodium bicarbonate solution for 15 minutes, then put it into acetone and use ultrasonic cleaning for 10 seconds;

[0025] ②Heat the aluminum shell of the capacitor at a temperature of 85-90°C for 5 minutes, and then slowly cool it to 36-38°C;

[0026] ③Put the capacitor aluminum case treated in ② into the soaking solution for 20 minutes, the soaking temperature is 58-60°C, and then dry it; the soaking solution is made of the following ingredients in parts by weight: sodium molybdate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a capacitor aluminum shell high-temperature-resistant paint which is prepared from a polyamide resin, polyvinyl alcohol, polymethyl methacrylate, diatomite, a phenolic resin, silicone oil, aluminum silicate, olive oil, sodium phosphate, wheat hull ash and a corn straw extract. After being sprayed on the capacitor aluminum shell surface, the capacitor aluminum shell paint has favorable curing effect, can effectively protect the capacitor, has favorable heat resistance and wear resistance, and can effectively achieve the heat radiation effect under the synergistic actions of the corn straw extract and wheat hull ash.

Description

technical field [0001] The invention relates to the technical field of coatings for aluminum shells of capacitors, in particular to a high-temperature-resistant coating for aluminum shells of capacitors. Background technique [0002] At present, the coatings sprayed on the aluminum shell of capacitors generally have a low service life. After long-term use, the coating film is easy to crack and shatter, and the capacitor product will generate heat energy during use. If the heat energy cannot be effectively resolved or diffused, the capacitor will advance with temperature. Aging life, long-term work due to temperature changes will also cause instability in the power supply of electronic components, causing certain hazards. Contents of the invention [0003] The purpose of the present invention is to provide a high temperature resistant coating for capacitor aluminum case. [0004] The present invention is realized through the following technical solutions: [0005] A high-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D177/00C09D129/04C09D133/12C09D161/06C09D7/12
CPCC09D177/00C08K2201/014C08L2201/08C08L2203/20C08L2205/035C09D5/18C09D7/61C09D7/63C09D7/65
Inventor 胡忠胜华玲萍吴良军
Owner ANHUI FEIDA ELECTRICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com