Preparation method of wear-resisting formaldehyde adsorption material

A formaldehyde adsorption and raw material technology, applied in chemical instruments and methods, gas treatment, membrane technology and other directions, can solve the problems of low formaldehyde removal rate, slow adsorption speed, short service life, etc. Long service life effect

Inactive Publication Date: 2017-04-26
SUZHOU LVDIAN INFORMATION TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] This application aims at the technical problems of low formaldehyde removal rate, poor wear resistance, short service life and slow adsorption speed of existing coatings, and provides a new method for preparing wear-resistant formaldehyde adsorption materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Weigh 100 parts of diatomite, 12 parts of hydroxypropyl ammonium bicarbonate, 20 parts of ethylene glycol, 5 parts of rock wool, 1 part of magnesium oxide, 30 parts of Portland cement, and 1 part of leucine according to the ratio of parts by weight. 6 parts of bentonite, 4 parts of quartz powder, 3 parts of alumina, 2 parts of ammonium bicarbonate, 13 parts of menthol, 15 parts of tetrahydrofuran, and 20 parts of deionized water.

[0024] Put hydroxypropylammonium bicarbonate, ethylene glycol, leucine, bentonite, quartz powder, aluminum oxide, ammonium bicarbonate, menthol and tetrahydrofuran into a reaction kettle equipped with a stirrer and a thermometer, raise the temperature to 40°C, and stir 30min, the stirring speed is 400 rpm, then add deionized water, and continue stirring for 30min.

[0025] Dry diatomite, rock wool, magnesia and Portland cement at a constant temperature of 90°C, then combine with the homogeneously stirred product in the previous step, mix for ...

Embodiment 2

[0028] Weigh 100 parts of diatomite, 18 parts of hydroxypropyl ammonium bicarbonate, 60 parts of ethylene glycol, 25 parts of rock wool, 5 parts of magnesium oxide, 50 parts of Portland cement, and 20 parts of leucine according to the ratio of parts by weight. 10 parts of bentonite, 8 parts of quartz powder, 7 parts of alumina, 6 parts of ammonium bicarbonate, 17 parts of menthol, 35 parts of tetrahydrofuran, and 40 parts of deionized water.

[0029] Put hydroxypropylammonium bicarbonate, ethylene glycol, leucine, bentonite, quartz powder, aluminum oxide, ammonium bicarbonate, menthol and tetrahydrofuran into a reaction kettle equipped with a stirrer and a thermometer, raise the temperature to 60°C, and stir 50min, the stirring speed is 800 rpm, then add deionized water, and continue stirring for 50min.

[0030] Dry diatomite, rock wool, magnesia and Portland cement at a constant temperature of 110°C, then combine with the homogeneously stirred product in the previous step, mi...

Embodiment 3

[0033] Weigh 100 parts of diatomite, 13 parts of hydroxypropyl ammonium bicarbonate, 30 parts of ethylene glycol, 10 parts of rock wool, 2 parts of magnesium oxide, 35 parts of Portland cement, and 5 parts of leucine according to the ratio of parts by weight. 7 parts of bentonite, 5 parts of quartz powder, 4 parts of alumina, 3 parts of ammonium bicarbonate, 14 parts of menthol, 20 parts of tetrahydrofuran, and 25 parts of deionized water.

[0034] Put hydroxypropylammonium bicarbonate, ethylene glycol, leucine, bentonite, quartz powder, aluminum oxide, ammonium bicarbonate, menthol and tetrahydrofuran into a reaction kettle equipped with a stirrer and a thermometer, raise the temperature to 40°C, and stir 30min, the stirring speed is 400 rpm, then add deionized water, and continue stirring for 30min.

[0035] Dry diatomite, rock wool, magnesia and Portland cement at a constant temperature of 90°C, then combine with the homogeneously stirred product in the previous step, mix f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a wear-resisting formaldehyde adsorption material. The preparation method comprises the following steps: (1) weighing hydroxypropyl ammonium hydrogen carbonate, ethylene glycol, leucine, bentonite, ground quartz, aluminum oxide, ammonium hydrogen carbonate, menthol and tetrahydrofuran and adding into a reaction kettle provided with a stirrer and a thermograph; raising the temperature to 40 DEG C-60 DEG C and stirring for 30min-50min; adding de-ionized water and continually stirring for 30min-50min; (2) weighing diatomite, rock wool, magnesium oxide and Portland cement and drying at a constant temperature of 90 DEG C-110 DEG C, and mixing a mixture with a product which is uniformly stirred in the step (2); and (3) putting the product mixed in the step (2) into a vacuum drying box and drying at 30 DEG C-40 DEG C for one night to obtain the wear-resisting formaldehyde absorption material. The formaldehyde removing rate of the product is up to 97.8%-99.5%; the product has the advantages of high wearing resistance, long service life, capability of being repeatedly utilized, and environmental protection, wide adsorption speed and wide adsorption range; after the product is put into a sealed space with the formaldehyde content of 400microg / m<3>-500microg / m<3> for 24h-48h, the concentration of formaldehyde is 2 microg / m<3>-8 microg / m<3>; and the preparation method is simple, the cost is low, the operability is high and the wear-resisting formaldehyde adsorption material can be widely produced and continuously replace an existing material.

Description

technical field [0001] The invention relates to the field of adsorption materials, in particular to a wear-resistant formaldehyde adsorption material and a preparation method thereof. Background technique [0002] Formaldehyde purification adsorbent refers to the adsorption material mainly used to absorb formaldehyde in household life, mainly including: activated silicon, activated carbon, activated alumina. [0003] When the concentration of formaldehyde is relatively high (for example, the new house has just been renovated), the method of ventilation can be used to discharge the formaldehyde outside, but physical methods such as ventilation can only reduce the concentration of formaldehyde, and cannot completely remove formaldehyde. [0004] The formaldehyde in the adhesive is released slowly, and the time to eliminate formaldehyde is longer, and the release period is as long as 3-15 years. The daily manifestation is that after a long time in the new house, when the door o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/30B01D53/02
CPCB01J20/22B01D53/02B01D2257/708B01J20/046B01J20/10B01J20/14
Inventor 顾黎明张宇
Owner SUZHOU LVDIAN INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap