Non-sparking wear-resisting concrete and method for carrying out floor construction through concrete

A technology for concrete and floor, applied in the field of building concrete, can solve the problems of complex floor concrete construction method, unable to meet various production needs, single function of floor concrete, etc., achieve high strength, low friction, prevent electrostatic sparks Effect

Inactive Publication Date: 2017-04-26
CHINA CONSTR FIRST BUREAU GRP INTERIOR FITOUT ENG +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide non-fire wear-resistant concrete and a floor construction method using the concrete, to solve the technical problem that the existing floor concrete function is t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-sparking wear-resisting concrete and method for carrying out floor construction through concrete

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] Conductive powder 3.42 parts, ordinary sand 0.5 parts, coarse aggregate 3.2 parts, SBS polymer modified emulsified asphalt 2 parts, cement 0.5 parts, water 1 part, admixture 0.4 parts. The admixture is a combination of flame retardant, anti-wear agent, foaming agent, carbon forming agent, carbon catalyst, water reducing agent and pumping agent. The conductive powder is spherical silicon-based conductive powder, the ordinary sand is quartz sand, the flame retardant is aramid fiber, the coarse aggregate is limestone, and the wear-resistant agent is α-crystalline SiO 2 Powder and cement are ordinary Portland cement with a grade strength of 42.5.

Example Embodiment

[0030] Example 2

[0031] 4.45 parts of conductive powder, 2.5 parts of ordinary sand, 4.88 parts of coarse aggregate, 2.2 parts of SBS polymer modified emulsified asphalt, 1.2 parts of cement, 1 part of water, and 0.8 parts of admixture. The admixture is a combination of flame retardant, anti-wear agent and blowing agent. The conductive powder is a combination of spherical silicon-based conductive powder, electric mica powder, conductive titanium dioxide and conductive barium sulfate. Spherical silicon-based conductive powder is made of powdered quartz mineral, polymer dispersant, crystalline SnCl 4 and SbCl 3 Made of superfine spherical composite conductive powder. Ordinary sand is quartz sand with a fineness modulus of 2.2 to 2.8. The flame retardant is a combination of aramid fibers, carbon fibers, chlorinated paraffin particles, chlorinated rubber particles, aluminum hydroxide particles and magnesium hydroxide particles. The coarse aggregate is marble, and the diamet...

Example Embodiment

[0032] Example 3

[0033] 3.42 parts of conductive powder, 0.78 parts of ordinary sand, 4.2 parts of coarse aggregate, 2.1 parts of SBS polymer modified emulsified asphalt, 1.11 parts of cement, 1 part of water, and 0.66 parts of admixture. The admixture is a combination of flame retardant, anti-wear agent and foaming agent. Conductive powder is a combination of spherical silicon-based conductive powder and electric mica powder. Spherical silicon-based conductive powder is made of powdered quartz mineral, polymer dispersant, crystalline SnCl 4 and SbCl 3 Made of superfine spherical composite conductive powder. Ordinary sand is corundum with a fineness modulus of 2.2 to 2.8. The flame retardant is a combination of aramid fibers, carbon fibers, chlorinated paraffin particles, chlorinated rubber particles, phosphorus-containing resin particles, polyethylene particles, aluminum hydroxide particles and magnesium hydroxide particles. The coarse aggregate is dolomite. The wear ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses non-sparking wear-resisting concrete and a method for carrying out floor construction through the concrete. The non-sparking wear-resisting concrete is prepared from, by weight, 3.42-4.45 parts of conductive powder, 0.5-2.5 parts of common sand, 3.2-4.88 parts of coarse aggregate, 2-2.2 parts of SBS high polymer modified emulsified asphalt, 0.5-1.2 parts of cement, 1 part of water and 0.4-0.8 part of an additive. The additive is a combination of one or more of a fire retardant, a wear resisting agent, a foaming agent, a carbon forming agent, a carbon catalyst, a water reducing agent and a pumping agent. The conductive powder is a combination of one or more of spherical silicon-based conductive powder, electric mica powder, conductive titanium dioxide and conductive barium sulfate. The non-sparking wear-resisting concrete can be widely applied to ground construction of combustible product warehouses, production areas with sparks prone to being generated or explosive plants, hangars and other areas with high requirements for the fireproof degree and wear resisting degree.

Description

technical field [0001] The invention belongs to the technical field of building concrete, and in particular relates to non-fire wear-resistant concrete and a floor construction method using the concrete. Background technique [0002] With the development of technology, the function of concrete is gradually refined. In industrial buildings, such as military manufacturing, liquefied petroleum gas stations, gas production plants, oil storage, oil station docks and other flammable and explosive projects, warehouses and other areas, There are special requirements for fire and explosion protection on the ground or walls. In addition, with the acceleration of my country's industrialization process, large-scale industrial plants have sprung up, and the high-tech trend of industrial plants is becoming more and more obvious. The requirements for the use of the ground are also getting higher and higher, and sometimes it is necessary to meet two or more functions. need. Due to the flam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B38/02E04F15/12C04B111/60C04B111/28
CPCC04B28/04C04B2111/28C04B2111/60C04B2111/905C04B2201/50E04F15/12C04B14/06C04B14/28C04B24/36C04B16/0691C04B2103/0068C04B2103/10C04B38/02C04B14/285C04B22/12C04B14/20C04B14/305C04B14/368C04B14/386C04B24/08C04B18/22C04B22/06C04B22/066C04B2103/408C04B20/0076C04B14/26C04B24/243C04B16/04
Inventor 单宝龙施林铁孔德重刘峰杨建华黄雷徐龙宝李新衣秀才王晓光付伟
Owner CHINA CONSTR FIRST BUREAU GRP INTERIOR FITOUT ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap