Wear-resistant corrosion-resistant sizing machine and preparation method thereof

A wear-resistant and anti-corrosion layer, sizing technology, applied in anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve problems such as damage and large scrap, and achieve the advantages of reducing glass transition temperature, low cost, and reducing film forming temperature. Effect

Inactive Publication Date: 2017-04-26
SUZHOU CHENHENG WEAVING
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The sizing machine is a machine with great demand in the weaving industry. With the continuous development of the economy, people have higher and higher requirements for the sizing machine. The sizing machine in the prior art is easy to cause damage after continuous use. , the amount of scrap is extremely large, in order to improve work efficiency, reduce scrap rate and cost, the present invention proposes a wear-resistant and anti-corrosion sizing machine and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] This embodiment provides a wear-resistant and anti-corrosion sizing machine. The outer surface of the sizing machine is coated with a wear-resistant and anti-corrosion layer. The wear-resistant and anti-corrosion layer is composed of two components A and B in a ratio of A:B=3:2. A and B comprise the following components in parts by mass:

[0024] Component A includes the following components in parts by mass: black silicon carbide: 18 parts, fine-grained alumina: 4 parts, dispersant: 3 parts, zinc oxide: 17 parts, color masterbatch: 10 parts, filler: 16 parts, antimony trioxide: 9 parts, plasticizer: 11 parts, film-forming aid: 12 parts, defoamer: 8 parts, auxiliary material: 14 parts;

[0025] Component B includes the following components in parts by mass: binder: 11 parts, suspending agent: 9 parts, heat stabilizer: 14 parts, methyl methacrylate: 33 parts, butyl acrylate: 15 parts, Aluminum isopropoxide: 10 parts, vinyltriethoxysilane: 2 parts, curing agent: 7 parts,...

Embodiment 2

[0033] This embodiment provides a wear-resistant and anti-corrosion sizing machine. The outer surface of the sizing machine is coated with a wear-resistant and anti-corrosion layer. The wear-resistant and anti-corrosion layer is composed of two components A and B in a ratio of A:B=3:2. A and B comprise the following components in parts by mass:

[0034] Component A includes the following components in parts by mass: black silicon carbide: 22 parts, fine-grained alumina: 12 parts, dispersant: 9 parts, zinc oxide: 20 parts, color masterbatch: 14 parts, filler: 19 parts, antimony trioxide: 13 parts, plasticizer: 16 parts, film-forming aid: 18 parts, defoamer: 13 parts, auxiliary materials: 19 parts;

[0035] Component B includes the following components in parts by mass: binder: 16 parts, suspending agent: 12 parts, heat stabilizer: 18 parts, methyl methacrylate: 36 parts, butyl acrylate: 19 parts, Aluminum isopropoxide: 14 parts, vinyltriethoxysilane: 6 parts, curing agent: 14 ...

Embodiment 3

[0043] This embodiment provides a wear-resistant and anti-corrosion sizing machine. The outer surface of the sizing machine is coated with a wear-resistant and anti-corrosion layer. The wear-resistant and anti-corrosion layer is composed of two components A and B in a ratio of A:B=3:2. A and B comprise the following components in parts by mass:

[0044] Component A includes the following components in parts by mass: black silicon carbide: 20 parts, fine-grained alumina: 9 parts, dispersant: 5 parts, zinc oxide: 18 parts, color masterbatch: 12 parts, filler: 17 parts, antimony trioxide: 10 parts, plasticizer: 13 parts, film-forming aid: 15 parts, defoamer: 11 parts, auxiliary materials: 16 parts;

[0045] Component B includes the following components in parts by mass: binder: 13 parts, suspending agent: 11 parts, heat stabilizer: 15 parts, methyl methacrylate: 35 parts, butyl acrylate: 18 parts, Aluminum isopropoxide: 12 parts, vinyltriethoxysilane: 4 parts, curing agent: 12 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant corrosion-resistant sizing machine. A component A comprises, by mass, 18-22 parts of black silicon carbide, 4-12 parts of fine-grain alumina, 3-9 parts of dispersant, 17-20 parts of zinc oxide, 10-14 parts of color masterbatch, 16-19 parts of filler, 9-13 parts of antimonous oxide, 11-16 parts of plasticizer, 12-18 parts of film forming aid, 8-13 parts of defoamer and 14-19 parts of auxiliary material, and a component B comprises, by mass, 11-16 parts of binder, 9-12 parts of suspension agent, 14-18 parts of heat stabilizer, 33-36 parts of methyl methacrylate, 15-19 parts of butyl acrylate, 10-14 parts of aluminum isopropoxide, 2-6 parts of vinyl triethoxysilane, 7-14 parts of curing agent, 5-10 parts of coupling agent and 3-8 parts of flame retardant. By the wear-resistant corrosion-resistant sizing machine, working efficiency is improved, scrappage rate is lowered, and product practicability is improved.

Description

technical field [0001] The invention relates to the technical field of weaving, in particular to a wear-resistant and anti-corrosion sizing machine and a preparation method thereof. Background technique [0002] The sizing machine is a machine with great demand in the weaving industry. With the continuous development of the economy, people have higher and higher requirements for the sizing machine. The sizing machine in the prior art is easy to cause damage after continuous use. , the amount of scrap is extremely large, in order to improve work efficiency, reduce scrap rate and cost, the present invention proposes a wear-resistant and anti-corrosion sizing machine and a preparation method thereof. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a wear-resistant and anti-corrosion sizing machine in view of the above shortcomings of the prior art. The outer surface of the sizing machine is coated with a wear-resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/06C09D5/08C09D5/18C09D7/12
CPCC09D4/06C09D5/08C09D5/18C09D7/48C09D7/61C09D7/63C09D7/65C09D7/70
Inventor 陈菊媛
Owner SUZHOU CHENHENG WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com