Environment-friendly wall decoration fireproof coating and preparation method thereof

A technology for wall decoration and fireproof coatings, applied in fireproof coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as black smoke, unenvironmentally friendly raw materials, poor physical and chemical performance indicators and fire resistance, etc. Achieve the effects of easy operation, simple preparation method and good fire resistance

Active Publication Date: 2017-04-26
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a result, the physical and chemical performance indicators and fire resistance of the fireproof finish coatings on the market are not good, and the raw materials used in some coatings are not environmentally friendly, and high concentrations of organic volatile compounds (VOCs) will be produced when they are burned in a fire, and even black out. smoke, which is very harmful to fire victims and rescuers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of environment-friendly type wall decoration fireproof coating of the present invention comprises the raw material of following weight portion: ceramic fiber is 15 parts, and vermiculite is 25 parts, and perlite is 5 parts, and fine asbestos is 25 parts, and borax 10 parts, 18 parts of mica powder, 10 parts of aliphatic water-based polyurethane, 5 parts of film-forming agent, 20 parts of foaming agent and 45 parts of deionized water; the film-forming agent is pure acrylic acid emulsion, The aliphatic water-based polyurethane is polyether polyol.

[0023] Described blowing agent is made up of the raw material of following percentage by weight: 16% thermoplastic acrylic resin polymer, 18% sodium dodecylbenzene sulfonate, 28% ammonium borate, 7% ammonium polyphosphate, balance for deionized water.

Embodiment 2

[0024] Embodiment 2: a kind of environment-friendly type wall decoration fireproof coating of the present invention comprises the raw material of following weight portion: ceramic fiber is 20 parts, and vermiculite is 30 parts, and perlite is 10 parts, and fine asbestos is 20 parts, and borax 8 parts, 15 parts of mica powder, 15 parts of aliphatic water-based polyurethane, 8 parts of film-forming agent, 18 parts of foaming agent and 40 parts of deionized water; the film-forming agent is pure acrylic acid emulsion, The aliphatic water-based polyurethane is polyether polyether.

[0025] Described blowing agent is made up of the raw material of following percentage by weight: 18% thermoplastic acrylic resin polymer, 16% sodium dodecylbenzenesulfonate, 24% ammonium borate, 5% ammonium polyphosphate, balance for deionized water.

Embodiment 3

[0026] Embodiment 3: a kind of environment-friendly type wall decoration fireproof coating of the present invention comprises the raw material of following weight portion: ceramic fiber is 25 parts, and vermiculite is 20 parts, and perlite is 8 parts, and fine asbestos is 30 parts, and borax 5 parts, 20 parts of mica powder, 20 parts of aliphatic water-based polyurethane, 10 parts of film-forming agent, 15 parts of blowing agent and 50 parts of deionized water; the film-forming agent is pure polyvinyl acetate In the emulsion, the aliphatic water-based polyurethane is polyether polyol.

[0027] Described blowing agent is made up of the raw material of following percentage by weight: 20% thermoplastic acrylic resin polymer, 22% sodium dodecylbenzene sulfonate, 30% ammonium borate, 3% ammonium polyphosphate, balance for deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly wall decoration fireproof coating, comprising ceramic fiber, vermiculite, perlite, fine asbestos, borax, mica powder, aliphatic waterborne polyurethane, a film-forming agent, a foaming agent and deionized water, wherein the foaming agent consists of a thermoplastic acrylic resin type polymer, sodium dodecyl benzene sulfonate, ammonium borate, ammonium polyphosphate and deionized water. The raw materials for preparing the coating disclosed by the invention are environment-friendly, have good fireproof performance, cannot deform easily, are high in strength, and cannot fall off and bulk; and preferably, the foaming agent is environment-friendly and nontoxic and has a reasonable formula, so that in the case of fire, the foaming agent expands to generate foams quickly to form a compact sponge-shaped expansion foam layer with a good heat-insulating property, combustible base materials can be protected more effectively, black smoke cannot be generated, and the concentration of organic volatiles is extremely low, which is beneficial for the health of sufferers and rescuers in the fire disaster. The preparation method disclosed by the invention is simple and is easy to operate, and the environment-friendly wall decoration fireproof coating is convenient in construction and firm in adhesion, and cannot crack to ensure that a wall body has a long service life.

Description

technical field [0001] The invention belongs to the technical field of architectural paint and its preparation, and in particular relates to an environment-friendly fireproof paint suitable for wall decoration. Background technique [0002] Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. According to different purposes and objects of use, it can be divided into: decorative fireproof coatings, cable fireproof coatings, steel structure fireproof coatings, prestressed concrete floor fireproof coatings, etc. Among them, decorative fire retardant coatings are getting more and more attention in the architectural coatings industry. But at present, the fireproof coatings for decorative walls pay more attention to the decorative effect, and the fireproof effect is not ideal. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D175/06C09D5/18
CPCC08K2201/003C09D5/185C09D175/06C09D175/08C08L33/00C08K13/04C08K7/02C08K7/12C08K2003/387C08K3/34C08K3/346C08L31/04
Inventor 刘西平
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com