Electric brush for treadmill motor

A technology of brushes and mixtures, applied to circuits, current collectors, electrical components, etc., can solve the problems of poor stability, inability to meet the high efficiency and energy saving of treadmill motors, and low operating efficiency, and achieve high stability, high practical efficiency, and load-carrying Good current capability

Inactive Publication Date: 2017-05-10
SUZHOU DONSUN CARBONWARE CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, at present, the general domestic brushes have low operating efficiency and poor stability, and domestic carbon brush factories cannot meet the high efficiency and energy saving requirements of treadmill motors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric brush for treadmill motor
  • Electric brush for treadmill motor
  • Electric brush for treadmill motor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] 1. Prepare materials (parts) according to the following proportions by weight:

[0068]

[0069] Wherein, the metal powder is a mixture of copper powder and silver powder, the weight ratio is 3:1, and the particle size is 200-400 mesh; the additives include molybdenum disulfide and aluminum phosphate, wherein the weight ratio of molybdenum disulfide and aluminum phosphate is 2:1; the binder is selected from bisphenol A epoxy resin, and its epoxy value is 0.25-0.45; the curing agent is selected from epoxy resin latent curing agent T-31 curing agent (Changzhou Shanfeng Chemical Co., Ltd.).

[0070] 2. Prepare the raw material mixture by electric brush

[0071] Put natural graphite, flexible graphite, polyphenylene resin (PHB), polytetrafluoroethylene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder Material; dissolving bisphenol A type epoxy resi...

Embodiment 2

[0081] 1. Prepare materials (parts) according to the following proportions by weight:

[0082]

[0083]

[0084] Wherein, the metal powder is a mixture of copper powder and tungsten powder, the weight ratio is 3:1, and the particle size is 200-400 mesh; the additives include molybdenum disulfide and aluminum phosphate, wherein the weight ratio of molybdenum disulfide and aluminum phosphate It is 2:1; binder selects bisphenol A type epoxy resin for use, and its epoxy value is 0.25-0.45; described curing agent selects epoxy resin latent curing agent T-31 curing agent for use (Changzhou Shanfeng Chemical Co., Ltd.) .

[0085] 2. Prepare the raw material mixture by electric brush

[0086] Put natural graphite, flexible graphite, polyphenylene resin (PHB), polytetrafluoroethylene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder Material; dissolving bis...

Embodiment 3

[0096] 1. Prepare materials (parts) according to the following proportions by weight:

[0097]

[0098] Wherein, the metal powder is a mixture of copper powder and tin powder, the weight ratio is 3:1, and the particle size is 200-400 mesh; the additives include molybdenum disulfide and aluminum phosphate, wherein the weight ratio of molybdenum disulfide and aluminum phosphate It is 2:1; binder selects bisphenol A type epoxy resin for use, and its epoxy value is 0.25-0.45; described curing agent selects epoxy resin latent curing agent T-31 curing agent for use (Changzhou Shanfeng Chemical Co., Ltd.) .

[0099] 2. Prepare the raw material mixture by electric brush

[0100] Put natural graphite, flexible graphite, polyphenylene resin (PHB), polytetrafluoroethylene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder Material; dissolving bisphenol A type epo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an electric brush for a treadmill motor. An electric brush preparation method comprises steps that matrix powder materials and a binder solution are mixed uniformly to prepare an electric brush raw material mixture; the electric brush raw material mixture is dried and crushed to acquire electric brush raw material powder; the electric brush raw material powder is added to a pressing die to carry out pressing processing to acquire an electric brush blank; thermal curing processing on the electric brush blank is carried out to acquire a half-finished electric brush product; finished product processing on the half-finished electric brush product is carried out to acquire a finished electric brush; the matrix powder materials comprise graphite, polyphenyl ester resin, polytetrafluoroethylene and metal powder. The electric brush has advantages of proper electrical resistivity, good wear-resisting performance, good commutation performance and low spark grade and further has more important advantages of high efficiency, low noise and good product stability.

Description

technical field [0001] The invention relates to an electric brush for a treadmill motor, in particular to an energy-saving electric brush for a treadmill motor, which belongs to the field of motors. Background technique [0002] The brush is a conductive part used in the motor to contact the commutator or slip ring to form an electrical connection, and is an important component of the motor. As a sliding contact body that imports and exports current, it has good electrical, thermal and lubricating properties, and has a certain mechanical strength and the instinct to suppress commutation sparks. It is widely used in various AC and DC generators, synchronous motors, battery DC motors, crane motor collector rings, various types of welding machines, etc. Almost all DC motors and commutation motors use brushes. [0003] With the development of science and technology, the types of motors and the working conditions of use are becoming more and more diverse, so various types of bru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01R39/22H01R39/24H01R43/12
CPCH01R39/22H01R39/24H01R43/12
Inventor 殷玲吴爱民
Owner SUZHOU DONSUN CARBONWARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka