Antibacterial and thermal insulation foam brick and preparation method thereof

A technology of foam bricks and raw materials, applied in ceramic products, other household utensils, applications, etc., can solve the problems of wasting natural resources and destroying the environment, and achieve the effects of saving resources, protecting the environment, and reducing costs

Inactive Publication Date: 2017-05-31
QINGDAO HAIZHIXING BIOLOGICAL SCI & TECH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Pile up and landfill the Enteromorpha that has been salvaged through painstaking efforts, which not only wastes natural resources, but also damages the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An antibacterial thermal insulation foam brick. The raw materials for making the antibacterial thermal insulation foam brick include the following components in parts by weight: 60 parts of Portland cement, 10 parts of enteromorpha, 6 parts of shells, 8 parts of loofah vine, and 6 parts of tea meal , 8 parts of glass fiber cloth, 10 parts of expanded perlite, 10 parts of coal ash, 3 parts of lanolin, 2 parts of gelatin, 0.6 parts of coconut oil fatty acid monoethanolamide, 0.3 parts of disodium edetate, lithium silicate 9 parts, 0.3 parts of sodium lignosulfonate, 0.6 parts of alkylphenol polyoxyethylene ether, 1 part of early strength agent, 1 part of sodium dehydroacetate, and 1 part of fluorine-containing silicon acrylate.

[0035] The preparation method of described antibacterial thermal insulation foam brick comprises the following steps:

[0036] (1) Weigh the glass fiber cloth ear material, clean it until there is no mud, dirt, etc., and dry it to no moisture, se...

Embodiment 2

[0047] An antibacterial thermal insulation foam brick. The raw materials for making the antibacterial thermal insulation foam brick include the following components in parts by weight: 80 parts of Portland cement, 16 parts of enteromorpha, 10 parts of shells, 12 parts of loofah vine, and 8 parts of tea meal , 16 parts of glass fiber cloth, 14 parts of expanded perlite, 20 parts of coal ash, 5 parts of lanolin, 3 parts of gelatin, 0.8 parts of coconut oil fatty acid monoethanolamide, 0.5 parts of disodium edetate, lithium silicate 15 parts, 0.5 parts of sodium lignosulfonate, 0.8 parts of alkylphenol polyoxyethylene ether, 2 parts of early strength agent, 2 parts of sodium dehydroacetate, and 2 parts of fluorine-containing silicon acrylate.

[0048] The preparation method of described antibacterial thermal insulation foam brick comprises the following steps:

[0049] (1) Weigh the glass fiber cloth ear material, clean it until there is no mud, dirt, etc., and dry it to no moist...

Embodiment 3

[0060] An antibacterial thermal insulation foam brick. The raw materials for making the antibacterial thermal insulation foam brick include the following components in parts by weight: 70 parts of portland cement, 13 parts of enteromorpha, 8 parts of shells, 10 parts of luffa vine, and 7 parts of tea meal , 12 parts of glass fiber cloth, 12 parts of expanded perlite, 15 parts of coal ash, 4 parts of lanolin, 2.5 parts of gelatin, 0.7 parts of coconut oil fatty acid monoethanolamide, 0.4 parts of disodium edetate, lithium silicate 12 parts, 0.4 parts of sodium lignosulfonate, 0.7 parts of alkylphenol polyoxyethylene ether, 1.5 parts of early strength agent, 1.5 parts of sodium dehydroacetate, and 1.5 parts of fluorine-containing silicon acrylate.

[0061] The preparation method of described antibacterial thermal insulation foam brick comprises the following steps:

[0062] (1) Weigh the glass fiber cloth ear material, clean it until there is no mud, dirt, etc., and dry it to no...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of building materials and discloses an antibacterial and thermal insulation foam brick and a preparation method thereof. The antibacterial and thermal insulation foam brick comprises, by weight, 60 to 80 parts of portland cement, 10 to 16 parts of enteromorpha prolifera, 6 to 10 parts of shells, 8 to 12 parts of luffa vine, 6 to 8 parts of tea meal, 8 to 16 parts of a glass fiber cloth, 10 to 14 parts of expanded perlite, 10 to 20 parts of coal ash, 3 to 5 parts of lanolin, 2 to 3 parts of gelatin, 0.6 to 0.8 parts of coconut fatty acid monoethanolamide, 0.3 to 0.5 parts of disodium ethylenediaminetetraacetate, 9 to 15 parts of lithium silicate, 0.3 to 0.5 parts of sodium lignosulfonate, 0.6 to 0.8 parts of alkylphenol ethoxylates, 1 to 2 parts of an early strength agent, 1 to 2 parts of sodium dehydroacetate and 1 to 2 parts of silicon-containing fluorinated acrylate. The antibacterial and thermal insulation foam brick has the advantages of energy saving, environmental friendliness, good compressive strength, thermal insulation and antibacterial properties.

Description

technical field [0001] The invention belongs to the field of building materials, and relates to an antibacterial thermal insulation foam brick, and also relates to a preparation method of the antibacterial thermal insulation foam brick. Background technique [0002] At present, the wall masonry materials widely used in construction projects are mainly bricks, such as: clay-fired bricks, hollow bricks, autoclaved lime-sand bricks, fly bricks, autoclaved aerated concrete blocks and ceramsite bricks. In recent years, some new lightweight vitrified ceramic hollow blocks, fly ash bricks, foam concrete core insulation blocks, sulfur-fixed ash concrete hollow blocks, sandwich-type injection hole insulation coal gangue sintered blocks have appeared. And other wall masonry materials, in addition, there are also some lightweight partition wall slats, such as: there are three main types: cement series, magnesium oxychloride and gypsum series. With the improvement of people's quality o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/10C04B41/68C04B111/40C04B111/20
CPCC04B28/04C04B38/10C04B41/009C04B41/5024C04B41/68C04B2111/20C04B2111/40C04B14/42C04B18/24C04B14/18C04B14/28C04B18/10C04B24/12C04B41/46C04B41/4896
Inventor 袁国防张聪聪王建军张建谷刘萌
Owner QINGDAO HAIZHIXING BIOLOGICAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com