Corrosion resistant ethylene propylene diene monomer rubber

A kind of EPDM rubber, corrosion-resistant technology, applied in the field of EPDM rubber, can solve the problems of restricting development and application, affecting service life, poor economic benefits, etc., to increase economic benefits, long service life, reduce The effect of business costs

Inactive Publication Date: 2017-05-31
佛山市高明区生产力促进中心
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, EPDM rubber still has the problem of poor corrosion resistance. When it is used in a highly corrosive place, it will quickly corrode and fade, seriously affecting the service life and poor economic benefits, which greatly restricts its further development. development and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion resistant ethylene propylene diene monomer rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A corrosion-resistant EPDM rubber, the raw materials include: 90 parts of EPDM rubber, 21 parts of polytetrafluoroethylene, 19 parts of butyl rubber, 13 parts of fluororubber, 10 parts of neoprene rubber, CR232 type chlorine 22 parts of butyl rubber, 7 parts of glass, 10 parts of candle, 16 parts of titanium silicon alloy, 9 parts of Monel 400 alloy, 15 parts of 316 stainless steel, 18 parts of fluorinated graphite, 7 parts of fungicide, 12 parts of filler, flame retardant 14 servings.

[0031] Further, a preparation method of corrosion-resistant EPDM, comprising the following steps:

[0032] (1) After weighing each constituent raw material according to the formula ratio, place it separately;

[0033] (2) Preheat the EPDM rubber to 95°C and set aside;

[0034] (3) Put polytetrafluoroethylene, butyl rubber, fluororubber, neoprene, CR232 neoprene, glass, candle, titanium-silicon alloy, Monel 400 alloy, 316 stainless steel, and fluorinated graphite into the mixer , at a...

Embodiment 2

[0038] A corrosion-resistant EPDM rubber, the raw materials include: 80 parts of EPDM rubber, 18 parts of polytetrafluoroethylene, 15 parts of butyl rubber, 11 parts of fluororubber, 7 parts of neoprene rubber, CR232 type chlorine 20 parts of butyl rubber, 5 parts of glass, 8 parts of candle, 14 parts of titanium silicon alloy, 7 parts of Monel 400 alloy, 12 parts of 316 stainless steel, 15 parts of fluorinated graphite, 5 parts of fungicide, 10 parts of filler, flame retardant 12 copies;

[0039] Further, a preparation method of corrosion-resistant EPDM, comprising the following steps:

[0040] (1) After weighing each constituent raw material according to the formula ratio, place it separately;

[0041] (2) Preheat the EPDM rubber to 93°C and set aside;

[0042] (3) Put polytetrafluoroethylene, butyl rubber, fluororubber, neoprene, CR232 neoprene, glass, candle, titanium-silicon alloy, Monel 400 alloy, 316 stainless steel, and fluorinated graphite into the mixer , at a tem...

Embodiment 3

[0046] A corrosion-resistant EPDM rubber, the raw materials include: 100 parts of EPDM rubber, 25 parts of polytetrafluoroethylene, 23 parts of butyl rubber, 16 parts of fluorine rubber, 13 parts of neoprene rubber, CR232 type chlorine 25 parts of butyl rubber, 11 parts of glass, 13 parts of candle, 19 parts of titanium silicon alloy, 11 parts of Monel 400 alloy, 18 parts of 316 stainless steel, 22 parts of fluorinated graphite, 9 parts of fungicide, 14 parts of filler, flame retardant 16 servings.

[0047] Further, a preparation method of corrosion-resistant EPDM, comprising the following steps:

[0048] (1) After weighing each constituent raw material according to the formula ratio, place it separately;

[0049] (2) Preheat the EPDM rubber to 98°C and set aside;

[0050](3) Put polytetrafluoroethylene, butyl rubber, fluororubber, neoprene, CR232 neoprene, glass, candle, titanium-silicon alloy, Monel 400 alloy, 316 stainless steel, and fluorinated graphite into the mixer ,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a corrosion resistant ethylene propylene diene monomer rubber and relates to the technical field of high polymer materials. The corrosion resistant ethylene propylene diene monomer rubber contains the raw materials of 80-100 parts of ethylene propylene diene monomer rubber, 18-25 parts of polytetrafluoroethylene, 15-23 parts of butyl rubber, 11-16 parts of fluororubber, 7-13 parts of chloroprene rubber, 20-25 parts of CR232 type chloroprene rubber, 5-11 parts of glass, 8-13 parts of wax candles, 14-19 parts of titanium silicon, 7-11 parts of monel 400 alloys, 12-18 parts of 316 stainless steel, 15-22 parts of carbon monofluoride, 5-9 parts of a bactericide, 10-14 parts of a filler, and 12-16 parts of a fire retardant. The corrosion resistant ethylene propylene diene monomer rubber provided by the invention has the advantages of low raw material price, simple making process, good corrosion resistant effect of the prepared ethylene propylene diene monomer rubber and long service life.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a corrosion-resistant EPDM rubber. Background technique [0002] EPDM (Ethylene Propylene Diene Monomer) is a copolymer of ethylene, propylene and a small amount of non-conjugated diene. It is a kind of ethylene propylene rubber. Composition, only contains unsaturated double bonds in the side chain, so it has excellent aging resistance such as ozone resistance, heat resistance, and weather resistance, and can be widely used in automotive parts, waterproof materials for construction, wire and cable sheaths, heat-resistant hoses, tapes , Automotive seals and other fields. However, at present, EPDM rubber still has the problem of poor corrosion resistance. When it is used in a highly corrosive place, it will quickly corrode and fade, seriously affecting the service life and poor economic benefits, which greatly restricts its further development. development and applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L27/18C08L23/22C08L27/12C08L11/00C08L91/06C08K13/04C08K3/40C08K3/08C08K3/04C08K5/19C08K3/16C08K5/3432C08K3/22C08K7/12C08K3/34C08K3/36C08K7/06C08K5/5313
CPCC08L23/16C08L2205/02C08L2205/025C08L2205/035C08L27/18C08L23/22C08L27/12C08L11/00C08L91/06C08K13/04C08K3/40C08K3/08C08K3/04C08K5/19C08K3/16C08K5/3432C08K2003/2227C08K7/12C08K3/34C08K3/36C08K7/06C08K5/5313
Inventor 贺海兰
Owner 佛山市高明区生产力促进中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com