Basalt fiber reinforced tape and its preparation method

A technology of basalt fiber and reinforcing tape, applied in braid, polyether coating, coating, etc., can solve the problems of restricting mass production and high price, and achieve high elastic modulus, less waste, and easy continuous use. Effect

Active Publication Date: 2019-05-24
JIANGSU HENGTONG PHOTOELECTRIC
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aramid fiber is currently the strongest non-metallic reinforcement. There is no domestic supplier that can produce high-performance aramid yarn. Optical cable manufacturers must rely on imports. The high price restricts the large-scale production of aramid fiber used in optical cables.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Basalt fiber reinforced tape and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~4

[0033] Embodiments 1 to 4: A basalt fiber reinforced belt, the basalt fiber reinforced belt is obtained by weaving basalt fibers coated with coating slurry and then coating the coating slurry, and the coating slurry consists of the following parts by weight Component composition:

[0034] Table 1

[0035] Component

Example 1

Example 2

Example 3

Example 4

85~90 parts of water

88 copies

90 copies

86 copies

88 copies

E-type epoxy resin 2~3 parts

2.8 servings

2 copies

2.5 servings

2.6 servings

Polyethylene adipate glycol-based polyurethane 1~2 parts

1.8 servings

1 copy

1.5 servings

1.2 parts

0.5~1.5 parts of polyvinyl acetate

0.8 parts

1 copy

1.4 parts

1.2 parts

nano-SiO 2 2~4 servings

2.8 servings

3 copies

2.2 parts

3.6 servings

Nano calcium silicate 1~3 parts

2 copies

1.2 parts

3 copies

1.8 servings

Fatty acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A basalt fiber enhanced belt is prepared by painting coating slurry on woven basalt fibers, which have been painted by the coating slurry. The coating slurry consists of the following components in parts by weight: 85 to 90 parts of water, 2 to 3 parts of E type epoxy resin, 1 to 2 parts of poly(glycol adipate) based polyurethane, 0.5 to 1.5 parts of polyvinyl acetate, 2 to 4 parts of nano SiO2, 1 to 3 parts of nano calcium silicate, 0.2 to 0.5 part of fatty acid amine acetate, 0.1 to 0.3 part of polyoxyethylene stearate, 0.2 to 0.3 part of ethoxyamine, 0.1 to 0.2 part of quaternary ammonium salt, and 0.2 to 0.7 part of silane coupling agent KH550. The basalt fiber enhanced belt has the advantages of high tensile strength, high elasticity modulus, good flexibility, wear resistance, bending resistance, high temperature resistance, and user friendliness.

Description

technical field [0001] The invention relates to a basalt fiber reinforced belt and a preparation method thereof, and relates to the technical field of optical fiber and cable. Background technique [0002] With the development of power transmission systems, the optical fiber and cable industry has grown rapidly, and the non-metallic reinforcement materials for optical cables are mainly glass fibers and aramid fibers. Glass fiber can meet the requirements of conventional optical cable applications, but it has great limitations in terms of strength, moisture absorption, creep resistance, and chemical stability. Aramid is currently the strongest non-metallic reinforcement. There is no domestic supplier that can produce high-performance aramid yarn. Optical cable manufacturers must rely on imports. The high price restricts the large-scale production of aramid for optical cables. Therefore, the current situation makes the market urgently need a high-quality and low-cost reinforc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D175/06C09D131/04C09D171/02C09D7/61C09D7/63D04C1/02
CPCC08L2205/035C09D7/61C09D7/63C09D163/00D04C1/02D10B2101/02
Inventor 王伟薛梦驰顾利国罗斌董王娟
Owner JIANGSU HENGTONG PHOTOELECTRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com