Anti-cracking PE (polyethylene) primer and production method thereof

An anti-cracking and primer technology, applied in fire-retardant coatings, coatings, polyester coatings, etc., to achieve the effects of low viscosity, improved solubility, and accelerated reaction speed

Inactive Publication Date: 2017-06-13
江苏赛鑫树脂有限公司 +2
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In response to this situation, we have developed an anti-cracking PE primer resin for PE wood furniture coatings, which can cha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-cracking PE (polyethylene) primer and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment one: with 8kg diethylene glycol; 30kg maleic acid; 33kg dicyclopentadiene; 6kg methylpropanediol; 0.025kg hydroquinone; Start stirring at ℃, the stirring speed is 1000 rpm, after 3 hours of heat preservation and stirring, reduce the stirring speed to 600 revolutions per minute and raise the temperature to 220 degrees Celsius at a speed of 40 °C / h, continue the heat preservation and stirring for 3 hours, stop stirring and cool down to room temperature to make PE resin;

[0018] With 40kg resin; 2kg styrene; 0.3kg dispersant; 7kg titanium dioxide; 0.6kg anti-settling agent; 27kg1250 mesh talcum powder; 18kg1250 mesh heavy calcium; Put 0.2k leveling agent into the stirring tank in turn, and stir for 1 hour at a speed of 1000 rpm at room temperature to make a PE primer;

[0019] Mix 10kg of PE primer; 0.1kg of cobalt isooctanoate; 0.1kg of methyl ethyl ketone peroxide; 4kg of thinner to form a coating, and paint it on the board to cure at room temperature and dr...

Embodiment 2

[0020] Embodiment two: with 8kg diethylene glycol; 30kg maleic acid; 33kg dicyclopentadiene; 6kg methylpropanediol; 0.025kg hydroquinone; Start stirring at ℃, the stirring speed is 1000 rpm, after 4 hours of heat preservation and stirring, reduce the stirring speed to 600 rpm and raise the temperature to 230 degrees Celsius at a rate of 25 °C / h, continue the heat preservation and stirring for 4.5 hours, stop stirring and cool down to room temperature. PE resin;

[0021] With 40kg resin; 2kg styrene; 0.3kg dispersant; 7kg titanium dioxide; 0.6kg anti-settling agent; 27kg1250 mesh talcum powder; 18kg1250 mesh heavy calcium; Put 0.2k leveling agent into the stirring tank in turn, and stir at 1000 rpm for 2 hours at room temperature to make PE primer;

[0022] Mix 10kg of PE primer; 0.1kg of cobalt isooctanoate; 0.1kg of methyl ethyl ketone peroxide; 4kg of thinner to form a coating, and paint it on the board to cure at room temperature and dry.

Embodiment 3

[0023] Embodiment three: with 8kg diethylene glycol; 30kg maleic acid; 33kg dicyclopentadiene; 6kg methylpropanediol; 0.025kg hydroquinone; Start stirring at ℃, the stirring speed is 1000 rpm, after 5 hours of heat preservation and stirring, reduce the stirring speed to 600 rpm and raise the temperature to 230 degrees Celsius at a rate of 10°C / h, continue the heat preservation and stirring for 5 hours, stop stirring and cool down to room temperature to make PE resin;

[0024] With 40kg resin; 2kg styrene; 0.3kg dispersant; 7kg titanium dioxide; 0.6kg anti-settling agent; 27kg1250 mesh talcum powder; 18kg1250 mesh heavy calcium; Put 0.2k leveling agent into the stirring tank in turn, and stir for 2.5h at a speed of 1000 rpm at room temperature to make a PE primer;

[0025] Mix 10kg of PE primer; 0.1kg of cobalt isooctanoate; 0.1kg of methyl ethyl ketone peroxide; 4kg of thinner to form a coating, and paint it on the board to cure at room temperature and dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of paint, and provides an anti-cracking PE (polyethylene) primer and a preparation method thereof. The PE anti-cracking primer provided by the invention comprises the following components in parts by weight: 40-45 parts of resin, 2 parts of styrene, 0.3 part of dispersing agent, 7-8 parts of titanium white, 0.6 part of anti-settling agent, 27-30 parts of 1250-mesh talcum powder, 18-20 parts of 1250-mesh heavy calcium carbonate, 3 parts of zinc stearate, 1.8 parts of xylene, 0.1 part of defoaming agent and 0.2 part of leveling agent. Compared with the prior art, the PE primer provided by the invention has a favorable film coating effect and excellent anti-cracking performance and can be widely used for furniture painting.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a primer with anti-cracking performance for wooden furniture and a manufacturing and using method thereof. Background technique [0002] Since the advent of PE wood lacquer, because of its excellent high fullness, filling and hardness, etc., it has improved the efficiency of furniture coating and improved the comprehensive performance of the paint film, so it has been widely promoted in the furniture industry. In recent years, with the changes in the furniture market and the transformation of the furniture coating process, the requirements for furniture paint are also getting higher and higher. The application of PE white primer is very extensive. The problem of cracking in the heterogeneous structure of furniture, especially in grooves or carvings, has always troubled many people in the paint industry. As we all know, the grooves and carvings are relatively deep, and it is n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/06C09D7/12C08G63/676
CPCC09D167/06C08G63/676C08K2201/014C08L2205/03C09D5/18C09D7/61C09D7/63C09D7/65C08L71/00C08K13/02C08K2003/2241C08K3/34C08K2003/265C08K5/098C08K5/14
Inventor 路旭东张小平
Owner 江苏赛鑫树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap