UV glue and preparation method thereof

A methyl and monomer technology, applied in the field of UV-curable coatings, can solve problems such as insufficient bonding strength and limited use of UV-curable adhesives, and achieve good thixotropy, easy processing and use, and good aging resistance.

Active Publication Date: 2017-06-13
东莞市亚聚光固新材料有限公司
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are a large number of silver-plated materials in the field of electronic and electrical communication products. At present, most

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV glue and preparation method thereof
  • UV glue and preparation method thereof
  • UV glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033]Accurately weigh each raw material by the following weight percentages, the 624-100 epoxy acrylate of Changxing Chemical: 20%, the 6141H-80 aliphatic polyurethane acrylate of Changxing Chemical: 35%, IBOA isobornyl acrylate: 25%, EM214 ( Tetrahydrofuran acrylate): 15%, photoinitiator 184 (1-hydroxycyclohexyl benzophenone): 2%, photoinitiator TPO (2,4,6-trimethylbenzoyl diphenylphosphine oxide): 2%, KH560 (γ-glycidyl etheroxypropyl trimethoxysilane): 0.5%, antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] Pentaerythritol ester): 0.5%; Add the above-mentioned components in the double planetary power mixing mixer in turn, vacuumize until the vacuum degree is -0.08MPa, stir at 700 rpm for 1-2 hours, stir evenly, and let it air to room temperature , to obtain a UV-curable adhesive with good adhesion to the silver-plated layer, and seal the package.

Embodiment 2

[0035] Accurately weigh each raw material by the following weight percentages, 624-100 epoxy acrylate of Changxing Chemical: 20%, 6141H-80 aliphatic polyurethane acrylate of Changxing Chemical: 35%, IBOMA isobornyl methacrylate: 25%, EM214 (tetrahydrofuran acrylate): 15%, photoinitiator 184 (1-hydroxycyclohexyl benzophenone): 2%, photoinitiator TPO (2,4,6-trimethylbenzoyl diphenylphosphine oxide ): 2%, KH560 (γ-glycidyl etheroxypropyl trimethoxysilane): 0.5%, antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propyl Acid] pentaerythritol ester): 0.5%; Add the above-mentioned components in the double planetary power mixing mixer in turn, vacuumize until the vacuum degree is -0.08MPa, stir for 1-2 hours at 700 rpm, stir evenly, and let it air in the air to room temperature to obtain a UV-curable adhesive with good adhesion to the silver-plated layer, which can be sealed and packaged.

Embodiment 3

[0037] Accurately weigh each raw material by the following weight percentages, Changxing Chemical's 624-100 epoxy acrylate: 18%, Changxing Chemical's 6141H-80 aliphatic polyurethane acrylate: 35%, IBOA (isobornyl acrylate): 25%, EM214 (tetrahydrofuran acrylate): 17%, photoinitiator 184 (1-hydroxycyclohexyl benzophenone): 2%, photoinitiator TPO (2,4,6-trimethylbenzoyl diphenylphosphine oxide) : 2%, KH560 (γ-glycidyl etheroxypropyl trimethoxysilane): 0.5%, antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid ] pentaerythritol ester): 0.5%; the above-mentioned components are added in the double planetary power mixing mixer successively, vacuumized to a vacuum degree of -0.08MPa, stirred for 1-2 hours at 700 rpm, stirred evenly, and left to air until At room temperature, obtain a UV-curable adhesive with good adhesion to the silver-plated layer, and seal the package.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides UV glue and a preparation method thereof. The UV glue is prepared from the following ingredients of 35 to 60 weight parts of prepolymer, 35 to 50 weight parts of monomer and 1 to 6 weight parts of photoinitiator, wherein the prepolymer is epoxy acrylate and/or modified polyurethane acrylate, and the monomer is chosen from one or several of (methyl) isobornyl acrylate, tetrahydrofuran acrylate and hydroxyethyl methylacrylate. The UV glue can be applied to the surface of a silver-coated material, has the characteristics of high bonding strength, small viscosity, high fluidity, good wear resistance and the like and overcomes the defects of existing photochemical solidification adhesive.

Description

technical field [0001] The invention relates to the technical field of ultraviolet curing coatings, and more specifically, relates to a UV glue and a preparation method thereof. Background technique [0002] Ultraviolet light curing (i.e. UV curing) refers to the chemical reaction of photosensitive substances in the system under the action of ultraviolet light to produce active fragments, which trigger the polymerization and crosslinking of active monomers or oligomers in the system, so that the system can be coated from a liquid state. The layer instantly becomes a solid coating. Ultraviolet light curing glue (UV glue) has been widely studied due to its many outstanding advantages such as fast curing speed, environmental friendliness, low energy consumption, and no solvent volatilization. It is mainly used in: electronics industry, optical product industry, medical equipment, decoration materials industry. As people pay more and more attention to environmental protection,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/14C09J163/10C09J11/06
CPCC08L2201/10C09J11/06C09J163/10C09J175/14C08L63/10C08K5/5435C08L75/14
Inventor 龚鑫
Owner 东莞市亚聚光固新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap