8k plate

A substrate and polishing fluid technology, applied in grinding machines, other chemical processes, grinding/polishing equipment, etc., can solve the problems of poor scratch resistance and stain resistance, fast replacement speed, and short service life of 8k boards, and achieve polishing Good effect, high grinding force, long service life

Inactive Publication Date: 2017-06-13
ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current 8K board production process is time-consuming, labor-intensive, and costly, and the prepared 8K board has poor scratch resistance and stain resistance, and has a short service life, resulting in fast replacement and great waste of board materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of 8k board, the manufacturing method comprises the following steps:

[0016] (1) Select stainless steel as the substrate, clean it with a hydrochloric acid solution with a molar concentration of 0.1 mol / liter, then scrub it with a care solution, and dry it in a drying oven;

[0017] (2) Put the dried substrate into the vibrating grinder, pour the grinding liquid along the four sides, so that the grinding liquid is evenly distributed in the machine, and grind. The grinding time is 80 minutes. The grinding liquid is measured in parts by weight Composed of the following ingredients: 25 parts of aluminum oxide, 14 parts of titanium dioxide, 13 parts of silicon dioxide, 6 parts of melamine, 6 parts of sodium polystyrene sulfonate, 2 parts of zirconium oxide, 3.5 parts of zinc oxide, and 2.0 parts of methacrylic acid , 2.5 parts of sodium silicate, 4.0 parts of ethyl formate, 4 parts of dimethylformamide, 1.5 parts of dodecyltrimethylammonium chloride, 2.2 parts of st...

Embodiment 2

[0023] A kind of 8k board, the manufacturing method comprises the following steps:

[0024] (1) Select stainless steel as the substrate, clean it with a hydrochloric acid solution with a molar concentration of 0.15 mol / L, then scrub it with a care solution, and dry it in a drying oven;

[0025] (2) Put the dried substrate into the vibrating grinder, and pour the grinding liquid along the periphery, so that the grinding liquid is evenly distributed in the machine, and then grind. The grinding time is 90 minutes, and the grinding liquid is measured in parts by weight. Composed of the following ingredients: 28 parts of aluminum oxide, 14.5 parts of titanium dioxide, 13.5 parts of silicon dioxide, 7 parts of melamine, 6.5 parts of sodium polyphenylene propylene sulfonate, 3 parts of zirconia, 4.5 parts of zinc oxide, 2.5 parts of methacrylic acid , 3.0 parts of sodium silicate, 5.0 parts of ethyl formate, 5 parts of dimethylformamide, 1.6 parts of dodecyltrimethylammonium chloride...

Embodiment 3

[0031] A kind of 8k board, the manufacturing method comprises the following steps:

[0032] (1) Select stainless steel as the substrate, clean it with a hydrochloric acid solution with a molar concentration of 0.2 mol / L, then scrub it with a care solution, and dry it in a drying oven;

[0033] (2) Put the dried substrate into a vibrating grinder, and pour the grinding liquid along the periphery, so that the grinding liquid is evenly distributed in the machine, and then grind. The grinding time is 100 minutes, and the grinding liquid is measured in parts by weight. Composed of the following ingredients: 30 parts of aluminum oxide, 15 parts of titanium dioxide, 14 parts of silicon dioxide, 8 parts of melamine, 7 parts of sodium polyphenylene propylene sulfonate, 4 parts of zirconia, 5.5 parts of zinc oxide, 3.0 parts of methacrylic acid 3.5 parts of sodium silicate, 5.5 parts of ethyl formate, 6 parts of dimethylformamide, 1.8 parts of dodecyltrimethylammonium chloride, 2.7 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Glossaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of metal product sheet materials and discloses an 8k plate and a production method of the 8k plate. The 8k plate takes stainless steel as a base plate; before grinding, the base plate treated by a washing agent and a nursing agent has high permeability and can absorb a grinding solution very well; the production efficiency is greatly improved and the production cost is reduced; the grinding solution for grinding can keep a high grinding force and scratches are not easy to generate, so that a plane is smooth and bright; meanwhile, a good condition is provided for subsequent precision polishing and machining; a polishing agent used by the invention has good polishing effect and the surface glossiness of the metal sheet material reaches 90 degrees; the 8k plate has rust-proof and anti-pollution effects and the service life is 5 to 8 years longer than that of a common 8k plate.

Description

technical field [0001] The invention relates to the field of sheet metal products, in particular to an 8k sheet. Background technique [0002] The 8k plate is a stainless steel plate with a smooth surface and a mirror luster after the stainless steel raw material is ground and polished, also called a mirror panel. The surface of the stainless steel plate is polished with an abrasive liquid through a polishing equipment to make the surface of the plate as clear as a mirror. At present, 8K board is mainly used in building decoration, elevator decoration, industrial decoration, facility decoration and other stainless steel products. The current 8K board manufacturing process is time-consuming and labor-intensive, and the cost is high, and the prepared 8K board has poor scratch resistance and stain resistance, and has a short service life, resulting in a fast replacement speed and a great waste of board materials. Contents of the invention [0003] In view of the problems of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K3/14C23F3/06B24B31/06
CPCC09K3/1472B24B31/06C23F3/06
Inventor 洪功正潘永刚蔡永波
Owner ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com