Lignosulfonate-polyvinyl alcohol blended coated soil conditioner and preparation method thereof
A technology of lignosulfonate and soil improver, which is applied in the direction of soil conditioning materials, chemical instruments and methods, urea compound fertilizer, etc. It can solve the problems of reducing soil acidity, not meeting sustainable development, and harming human safety. , to achieve the effects of improving effectiveness, isolating lime from contact with water, and facilitating transportation and use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] A lignosulfonate-polyvinyl alcohol blended coating soil improver, comprising lime nitrogen meeting agricultural standards and a coating coated on the outside of the lime nitrogen, the mass ratio of the lime nitrogen to the coating is 100:13, the coating includes the following raw materials in parts by weight: 2 parts of sodium lignosulfonate, 9 parts of polyvinyl alcohol, 2 parts of urea, and 1 part of 37wt% formaldehyde.
[0046] A method for preparing lignosulfonate-polyvinyl alcohol blended coating soil conditioner, comprising the following steps:
[0047] S1: Spread 100 parts by weight of lime nitrogen with a particle size greater than 2mm on an iron pan, then pour the heated and cooled tung oil (anhydrous) on the surface of the lime, roll the lime improving agent and make the tung oil evenly wrapped in the lime After the surface of the improver is dried naturally (rolling occasionally to prevent the oil from sticking to the iron plate), the core agent is obtained f...
Embodiment 2
[0055] A lignosulfonate-polyvinyl alcohol blend coated soil conditioner, comprising a compound preparation containing quicklime and a coating coated on the outside of the compound preparation containing quicklime, the compound preparation containing quicklime and the compound preparation containing quicklime The mass ratio of the coating is 100:13, and the coating includes the following raw materials in parts by weight: 5 parts of sodium lignosulfonate, 10 parts of polyvinyl alcohol, 5 parts of urea, and 5 parts of 40wt% formaldehyde.
[0056] A method for preparing lignosulfonate-polyvinyl alcohol blended coating soil conditioner, comprising the following steps:
[0057] S1: Mix the powder compound preparation containing quicklime and the binder at a weight ratio of 100:0.9, and then prepare calcareous modifier particles with a compressive strength of 8N and a particle diameter of 3.5 mm. Granules, spread on the iron plate, and then pour the heated and cooled tung oil (anhydr...
Embodiment 3
[0065] A lignosulfonate-polyvinyl alcohol blended coating soil conditioner, comprising slaked lime meeting agricultural standards and a coating coated on the outside of the slaked lime, the mass ratio of the slaked lime to the coating being 120:14 , the coating includes the following raw materials in parts by weight: 11 parts of sodium lignosulfonate, 11 parts of polyvinyl alcohol, 11 parts of urea, and 8 parts of 40wt% formaldehyde.
[0066] A method for preparing lignosulfonate-polyvinyl alcohol blended coating soil conditioner, comprising the following steps:
[0067] S1: Mix the slaked lime of the powder with the binder according to the weight ratio of 120:1.7, and then prepare the calcareous modifier particles with a compressive strength of 8.5N and a particle diameter of 4mm, spread the calcareous modifier particles flat Put the heated and cooled tung oil (anhydrous) on the lime surface, roll the calcareous improver and wrap the tung oil evenly on the surface of the calc...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com