High-yield glass and production technology thereof

A high-yield and production technology technology, applied in the field of high-yield glass and its production process, can solve the problems that the raw material formula and process cannot be adjusted and controlled, lack of pulverization and drying processing links, and high yield, and achieve low cost. , The effect of high yield and convenient maintenance

Inactive Publication Date: 2017-06-27
合肥协耀玻璃制品有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems of lack of crushing and drying process in the existing glass and its production process, the inability to adjust and control the raw material formula and process, low yield and high cost, the purpose of the present invention is to provide a glass with high yield And its production process has the advantages of setting efficient crushing and drying treatment links, adjusting and controlling the raw material formula and process, high yield and low cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-yield glass and production technology thereof
  • High-yield glass and production technology thereof
  • High-yield glass and production technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A high-yield glass, which is made of the following raw materials in parts by weight:

[0037]

[0038] It has the advantages of precise adjustment and control of raw material formula, low cost and good quality of glass produced.

[0039] The halide clarifying agent is sodium chloride, and the gasification and volatilization of sodium chloride at high temperature can promote the clarification of glass liquid.

[0040] A production process for high-yield glass, comprising the following steps:

[0041] (1) Raw material pre-processing: crush the bulk raw material with an impact crusher, and dry the wet raw material with a drum dryer;

[0042] (2) Batch material preparation: put the raw material into the mixing machine according to the raw material ratio of glass parts by weight to make batch material;

[0043] (3) Melting material: put the batch material into the crucible kiln for melting, the melting temperature is controlled at 1585°C, and the melting effect of the m...

Embodiment 2

[0051] A high-yield glass, which is made of the following raw materials in parts by weight:

[0052]

[0053] It has the advantages of precise adjustment and control of raw material formula, low cost and good quality of glass produced.

[0054] The halide clarifying agent is sodium chloride, and the gasification and volatilization of sodium chloride at high temperature can promote the clarification of glass liquid.

[0055] A production process for high-yield glass, comprising the following steps:

[0056] (1) Raw material pre-processing: crush the bulk raw material with an impact crusher, and dry the wet raw material with a drum dryer;

[0057] (2) Batch material preparation: put the raw material into the mixing machine according to the raw material ratio of glass parts by weight to make batch material;

[0058] (3) Melting material: put the batch material into the crucible kiln for melting, the melting temperature is controlled at 1580°C, and the melting effect of the m...

Embodiment 3

[0066] A high-yield glass, which is made of the following raw materials in parts by weight:

[0067]

[0068] It has the advantages of precise adjustment and control of raw material formula, low cost and good quality of glass produced.

[0069] The halide clarifying agent is sodium chloride, and the gasification and volatilization of sodium chloride at high temperature can promote the clarification of glass liquid.

[0070] A production process for high-yield glass, comprising the following steps:

[0071] (1) Raw material pre-processing: crush the bulk raw material with an impact crusher, and dry the wet raw material with a drum dryer;

[0072] (2) Batch material preparation: put the raw material into the mixing machine according to the raw material ratio of glass parts by weight to make batch material;

[0073] (3) Melting material: Put the batch material into the crucible kiln for melting, the melting temperature is controlled at 1550 ° C, and the melting effect of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides high-yield glass and a production technology of the high-yield glass, and relates to the technical field of glass production. The glass is prepared from the following raw materials in parts by weight: 55-70 parts of quartz sand, 12-18 parts of sodium carbonate, 5-10 parts of mirabilite, 5-8 parts of limestone, 0.5-2 parts of sodium nitrate, 4-8 parts of pagodastone, 2-8 parts of dolomite, 5-9 parts of fluorite and 0.4-0.8 part of a halide clarifying agent. The production technology of the glass comprises the following steps: (1) raw material preprocessing, (2) mixture preparation, (3) material melting, (4) forming, (5) annealing, (6) processing, (7) inspection, and (8) analysis and summary. The production technology has the advantages that high-efficiency crushing and drying treatment links are adopted; formulae and technologies of the raw materials can be adjusted and controlled; the yield is high; the cost is low.

Description

technical field [0001] The invention belongs to the technical field of glass production, and in particular relates to a high-yield glass and a production process thereof. Background technique [0002] Glass has good transparency, no pollution, strong fashion, rich shapes, wide application and low cost. Glass molds are formed with precise dimensions, which can produce light and thin products with rich and varied colors and exquisite workmanship. [0003] A Chinese patent document announced on January 20, 2016, a porcelain white glass and its production process (authorized announcement number CN103482870B), the production process includes the following steps: (1) batch material preparation; (2) melting: mixing the batch material and The cullet is put into the furnace for melting; (3) Forming: use glass forming equipment for forming processing; (4) Annealing: use an annealing kiln for annealing. The porcelain white glass formula is composed of the following raw materials by w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/06C03B9/193C03B25/00
CPCC03C1/004C03B9/193C03B25/00C03C1/00
Inventor 魏芳芳
Owner 合肥协耀玻璃制品有限公司